DOE OSTI2024

Measuring the density, viscosity, and surface tension of molten titanates using electrostatic levitation in microgravity

Rare earth and barium titanates are useful as ferroelectric, dielectric, and optical materials. Measurements of their thermophysical properties in the liquid state can help guide melt processing technologies for their manufacture and advance understanding of fragile liquids' behavior and glass formation. Here, we report the density, thermal expansion, viscosity, and surface tension of molten BaTi 2 O 5 , BaTi 4 O 9 , and 83TiO 2 -17RE 2 O 3 (RE = La or Nd). Measurements were made using electrostatic levitation and droplet oscillation techniques in microgravity, which provide access to quiescent liquid droplets and deep supercooling of 510–815 K below the equilibrium melting points. Densities were measured over 900–2400 K. Viscosities were similar for all four compositions, increasing from ~10 mPa s near 2100 K to ~30 mPa s near 1750 K. Surface tensions were 450–490 dyn cm -1 for the rare earth titanates and 383–395 dyn cm -1 for the barium titanates; surface tensions of all compositions had small or negligible temperature dependence over 1700–2200 K. In conclusion, for solids recovered after melt quenching, x-ray microtomography revealed the fracture mechanics in crystalline products and minimal internal porosity in glass products, likely arising from entrapped gas bubbles. Internal microstructures were generally similar for products processed either in microgravity or in a terrestrial aerodynamic levitator.

42 ENGINEERING↗

DOE OSTI2024

The structure of CaO–MgO–Al 2 O 3 –SiO 2 melts and glasses doped with FeO X –NiO

Neutron and x-ray diffraction measurements have been performed on CaO–MgO–Al 2 O 3 –SiO 2 (CMAS) glasses doped with NiO–Fe X O at room temperature, along with x-ray measurements on aerodynamically levitated liquids at ≥2000 K. The disordered structures have been modeled using empirical potential structure refinement to investigate the relation between the aluminosilicate network and the modifying cations. The SiO 4 and AlO 4 tetrahedra are found to have wider Si–O and Al–O bond distance distributions in the glass, and the first Ca–O n coordination shell is highly distorted, redistributing different populations of long and short bonds between the liquid and the glass. The addition of Fe and Ni at low aluminosilicate content increases the number of free oxygens not bonded to AlO 4 or SiO 4 . Mg–O and Fe–O are both found to be predominantly fourfold and fivefold in the liquid and glassy states. Despite these low coordination numbers, their bond angle distributions indicate that they are predominantly in nontetrahedral-type geometries, with ferrous and ferric iron possessing similar coordination environments. The Ca–O and Mg–O average coordination numbers and enthalpies of solution are consistent with their higher reactivity within relatively acidic aluminosilicate melts.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Site‐selective fluorescence and spectroscopic properties of Yb‐doped lanthanum titanate glasses

Abstract Ytterbium‐doped lanthanum titanate glasses were prepared by levitation melting for the detailed characterization of the spectroscopic properties in the rare‐earth titanate glass host. Low‐temperature fluorescence spectroscopy reveals distinct site‐selectivity in both static and lifetime fluorescence measurements suggesting an absence of clustering as well as significant variation of local ytterbium environments. Typical site‐selectivity behavior of a shrinking Stark manifold with lower excitation energy is observed. At 77 K, both the mean emission frequency and the fluorescence lifetime initially increase as the excitation energy decreases from about 11100 to 10750 and then slightly decrease at lower excitation energy. Temperature‐dependent lifetime measurements between 77 and 420 K show a decreasing lifetime with increasing temperature and are well described by a two‐level thermal activation model. The temperature‐dependent fluorescence spectroscopy coupled with a room temperature white light absorption measurement allow the determination of the Stark energy levels of in lanthanum titanate glass as well as the calculation of the laser cross‐sections.

Materials Science↗

DOE OSTI2024

Microgravity effects on nonequilibrium melt processing of neodymium titanate: thermophysical properties, atomic structure, glass formation and crystallization

The relationships between materials processing and structure can vary between terrestrial and reduced gravity environments. As one case study, we compare the nonequilibrium melt processing of a rare-earth titanate, nominally 83TiO 2 -17Nd 2 O 3 , and the structure of its glassy and crystalline products. Density and thermal expansion for the liquid, supercooled liquid, and glass are measured over 300–1850 °C using the Electrostatic Levitation Furnace (ELF) in microgravity, and two replicate density measurements were reproducible to within 0.4%. Cooling rates in ELF are 40–110 °C s -1 lower than those in a terrestrial aerodynamic levitator due to the absence of forced convection. X-ray/neutron total scattering and Raman spectroscopy indicate that glasses processed on Earth and in microgravity exhibit similar atomic structures, with only subtle differences that are consistent with compositional variations of ~2 mol. % Nd 2 O 3 . The glass atomic network contains a mixture of corner- and edge-sharing Ti-O polyhedra, and the fraction of edge-sharing arrangements decreases with increasing Nd 2 O 3 content. X-ray tomography and electron microscopy of crystalline products reveal substantial differences in microstructure, grain size, and crystalline phases, which arise from differences in the melt processes.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Nonlinear optical properties of lanthanum titanate glasses prepared by levitation melting

Lanthanum titanate glasses (17 La 2 O 3 -83 TiO 2 ) are fabricated via aerodynamic levitation melting. Here, nonlinear refraction and absorption were measured with the Z scan technique using ps optical pulses at 532 nm wavelength with peak intensities in the range of 0.25–2.5 GW/cm 2 . The two-photon absorption coefficient (β) and the effective nonlinear refraction coefficient (⁠$n^{eff}_{2}$) are found to be, respectively, 2.19 cm/GW and 152 × 10 -16 cm 2 /W (85 × 10 -13 esu). The Raman gain is measured to be 106 × 10 -11 cm/W. The nonlinearity strength is found to be nearly 60 times larger in lanthanum titanate glasses relative to silica.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Revisiting metastable immiscibility in SiO 2 –Al 2 O 3 : Structure and phase separation of supercooled liquids and glasses

Understanding and controlling liquid–liquid phase separation in aluminosilicates is crucial for optimizing glass properties. However, the metastable nature of aluminosilicates’ phase separation has made it difficult to study experimentally, and uncertainty persists regarding the compositional and temperature extents of the miscibility gap. Here, we present new experimental evidence that suggests a consolute temperature between 1440 and 1590°C and endmember compositions of 7 and 62 mol.% Al 2 O 3 for the phase-separated glasses. Using containerless melt processing, deeply supercooled liquids over the 0–60 mol.% Al 2 O 3 range are probed with in situ small- and wide-angle X-ray scattering, which simultaneously reveals changes in nanoscale density heterogeneity and atomic structure. Correlations between phase separation and atomic coordination environments are compared for liquids and glasses. Pair distribution function analysis shows mean O–(Si + Al) coordination increases with Al 2 O 3 content and decreases with temperature.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Phase separation in mullite-composition glass

Aluminosilicates (AS) are ubiquitous in ceramics, geology, and planetary science, and their glassy forms underpin vital technologies used in displays, waveguides, and lasers. In spite of this, the nonequilibrium behavior of the prototypical AS compound, mullite (40SiO 2 -60Al 2 O 3 , or AS60), is not well understood. By deeply supercooling mullite-composition liquid via aerodynamic levitation, we observe metastable liquid–liquid unmixing that yields a transparent two-phase glass, comprising a nanoscale mixture of AS7 and AS62. Extrapolations from X-ray scattering measurements show the AS7 phase is similar to vitreous SiO 2 with a few Al species substituted for Si. The AS62 phase is built from a highly polymerized network of 4-, 5-, and 6-coordinated AlO x polyhedra. Polymerization of the AS62 network and the composite morphology provide essential mechanisms for toughening the glass.

36 MATERIALS SCIENCE↗

DOE OSTI2022

A Combined Machine Learning and High-Energy X-ray Diffraction Approach to Understanding Liquid and Amorphous Metal Oxides

Determining the structure-property relations of liquid and amorphous metal oxides is challenging, due to their variable short-range order and polyhedral connectivity. To predict chemically realistic structures, we have developed a Machine Learned, Gaussian Approximation Potential (GAP) for HfO 2 , with a focus on enhanced sampling of the training database and accurate density functional theory calculations. By using training datasets for the GAP model at the level of Density Functional Theory-Strongly Constrained and Appropriately Normed (DFT-SCAN) level of theory, our results show that the topology of both the low viscosity liquid and the amorphous form are dominated by edge-shared chains and small corner-shared rings of polyhedra. This topology is shown to be consistent with the structure of other liquid and amorphous transition metal oxides of variable ion size, such as TiO 2 and ZrO 2 . Current limitations of the ML-GAP modeling method for obtaining glass structures and future perspectives are also discussed.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Octahedral oxide glass network in ambient pressure neodymium titanate

Abstract Rare-earth titanates form very fragile liquids that can be made into glasses with useful optical properties. We investigate the atomic structure of 83TiO 2 -17Nd 2 O 3 glass using pair distribution function (PDF) analysis of X-ray and neutron diffraction with double isotope substitutions for both Ti and Nd. Six total structure factors are analyzed (5 neutron + 1 X-ray) to obtain complementary sensitivities to O and Ti/Nd scattering, and an empirical potential structure refinement (EPSR) provides a structural model consistent with the experimental measurements. Glass density is estimated as 4.72(13) g cm −3 , consistent with direct measurements. The EPSR model indicates nearest neighbor interactions for Ti-O at $$\overline{r}_{TiO}$$ r ¯ TiO = 1.984(11) Å with coordination of $$n_{TiO}$$ n TiO = 5.72(6) and for Nd-O at $$\overline{r}_{NdO}$$ r ¯ NdO = 2.598(22) Å with coordination of $$n_{NdO}$$ n NdO = 7.70(26), in reasonable agreement with neutron first order difference functions for Ti and Nd. The titanate glass network comprises a mixture of distorted Ti-O 5 and Ti-O 6 polyhedra connected via 71% corner-sharing and 23% edge-sharing. The O-Ti coordination environments include 15% nonbridging O-Ti 1 , 51% bridging O-Ti 2 , and 32% tricluster O-Ti 3 . This structure is highly unusual for oxide glasses melt-quenched at ambient pressure, as it consists of Ti-O x predominantly in octahedral (with nearly no tetrahedral) coordination.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Containerless Techniques for in-situ X-Ray Measurements on Materials in Extreme Conditions

This article reviews containerless methods in the context of measuring materials in-situ using x-ray techniques. Non-contact processing enables high chemical purity to be achieved even at temperatures above 2000 °C. The absence of extrinsic heterogenous nucleation allows supercooling and supersaturation of liquids and solutions. In many cases new types of glass can be made, particularly from fragile liquids. Current methods for containerless processing are briefly reviewed. The application of scattering, spectroscopic and emerging x-ray techniques is described. Examples including measurements on molten metal oxides, molten metallic alloys and organic molecules are presented. The work is discussed in the broader context of combining structure and property data to predict how to make new applied materials.

36 MATERIALS SCIENCE↗