A method of growing an oxide coating on Inconel 718 samples was investigated to increase the emissivity of the redesigned Inconel Mu2e production target. Microscopy and emissivity measurements of a range of samples indicate excellent performance.
Mu2e, the Muon-to-Electron Conversion Experiment, aims to identify physics beyond the Standard Model, namely, the conversion of muons to electrons without the emission of neutrinos. The muons are produced from pions generated in a production target when it is hit by an 8 GeV proton beam from the Fermilab Booster/Main Injector. The proton target design space is strongly constrained by a one-year operating lifetime and the need for radiative cooling in a vacuum environment. Uncertainties in the lifetime of the existing baseline design – a monolithic, segmented tungsten target – are large, particularly due to unknown impacts of radiation damage at the very high proton fluences expected in the experiment. We have begun evaluation of a new design utilizing Inconel 718 over the WL10 used in the existing target design. As a result, the structural design of the target has evolved significantly. This evolution focuses on lowering the target temperature, minimizing obstruction to muons, increasing structural stability, maximizing fatigue lifetime, simplifying the fabrication process, and more. The thermal management, structural stability and fatigue lifetime are emphasized here. These optimizations have led to a promising new target design for the Mu2e experiment.
There are 96 combined function magnets, 48 focusing and 48 defocusing, that have been in operation in the Fermi NAL Booster without a critical failure requiring replacement for over 50 years. The Proton Improvement Plan-II (PIP-II) poses risk to these magnets and Fermilab does not currently have the tooling or knowledge of process to fabricate spares. Two new variants of these magnets are needed to reduce beam loss by having a larger aperture (Booster Gradient Defocusing Wide, or BGDS) and create space for a new injection system (Booster Gradient Defocusing Short, or BGDS). Risk of failure and need for spares will increase substantially with the implementation of PIP-II in consequence of a frequency increase from 15 Hz to 20 Hz and a 30 percent increase in peak to ground voltage. The BGDS and BGDW magnets will be fabricated in the same way as the current booster magnets so that future combined function magnet spares can be produced using learned processes.