NDT and SHM of Carbon Fiber Composites using Linear Drive MWM-Arrays
No abstract available
Washabaugh, Andrew↗
Engineering topics
Wincheski, Russell
Publications and source records attributed to Wincheski, Russell.
Development of In-situ Nondestructive Evaluation Techniques and Physical Standards for Inspection of Welded Tubing Used in Spacecraft
Objective Develop and validate an eddy current inspection technique for orbital tubing welds that cannot be inspected using the normally applied methods due to access restrictions.
Koshiti, Ajay↗
NDT and SHM of Carbon Fiber Composites using Linear Drive MWM-Arrays
Carbon fiber composites are used in a wide range of structural applications due to their excellent specific strength and stiffness. However, the anisotropic mechanical and electrical properties associated with the fibers within each composite layer present challenges, and opportunities, for Nondestructive Testing (NDT) methods used to characterize and assess the structure condition. This includes composite condition after manufacture (such as fiber orientation and density, porosity, delamination, and bond strength) and during usage (such as damage from impact, fiber breakage, thermal exposure or applied stress). Ultrasonic and thermographic methods can address some of these challenges, but eddy current methods provide an alternative method for composite structures that contain a conducting material, such as carbon fibers or a metallic liner. This presentation reviews recent advances in the development of eddy current sensors and arrays for carbon fiber composite NDT and Structural Health Monitoring (SHM) applications. The focus is on eddy current sensor constructs with linear drive windings, such as MWM -Arrays, that induce currents primarily within the linear fibers of the composite. By combining this type of sensor construct with micromechanical models that relate composite constituent properties to measurable sensor responses, insight is obtained into the volumetric distribution of electrical properties within the composite and the associated manufacturing, damage, or strain conditions. With knowledge of the fiber layup, this MWM-Array technology is able to detect damage and strain/stress as a function of depth and fiber orientation. This work has been funded by NASA, NA V AIR and the Army for applications ranging from composite overwrapped pressure vessels (COPVs) to aircraft structures and rotorcraft blades. This presentation will specifically present background on the MWM-Array technology, results from the micromechanical modeling effort, and results from ongoing efforts for high resolution imaging and volumetric strain sensing.
Washabaugh, Andrew↗
Carbon Nanotube-Based Structural Health Monitoring Sensors
Carbon nanotube (CNT)-based sensors for structural health monitoring (SHM) can be embedded in structures of all geometries to monitor conditions both inside and at the surface of the structure to continuously sense changes. These CNTs can be manipulated into specific orientations to create small, powerful, and flexible sensors. One of the sensors is a highly flexible sensor for crack growth detection and strain field mapping that features a very dense and highly ordered array of single-walled CNTs. CNT structural health sensors can be mass-produced, are inexpensive, can be packaged in small sizes (0.5 micron(sup 2)), require less power than electronic or piezoelectric transducers, and produce less waste heat per square centimeter than electronic or piezoelectric transducers. Chemically functionalized lithographic patterns are used to deposit and align the CNTs onto metallic electrodes. This method consistently produces aligned CNTs in the defined locations. Using photo- and electron-beam lithography, simple Cr/Au thin-film circuits are patterned onto oxidized silicon substrates. The samples are then re-patterned with a CNT-attracting, self-assembled monolayer of 3-aminopropyltriethoxysilane (APTES) to delineate the desired CNT locations between electrodes. During the deposition of the solution-suspended single- wall CNTs, the application of an electric field to the metallic contacts causes alignment of the CNTs along the field direction. This innovation is a prime candidate for smart skin technologies with applications ranging from military, to aerospace, to private industry.
Wincheski, Russell↗
Continued Development of Meandering Winding Magnetometer (MWM (Register Trademark)) Eddy Current Sensors for the Health Monitoring, Modeling and Damage Detection of Composite Overwrapped Pressure Vessels
Composite Overwrapped Pressure Vessels (COPVs) are used in essentially all NASA spacecraft, launch. vehicles and payloads to contain high-pressure fluids for propulsion, life support systems and science experiments. Failure of any COPV either in flight or during ground processing would result in catastrophic damage to the spacecraft or payload, and could lead to loss of life. Therefore, NASA continues to investigate new methods to non-destructively inspect (NDE) COPVs for structural anomalies and to provide a means for in-situ structural health monitoring (SHM) during operational service. Partnering with JENTEK Sensors, engineers at NASA, Kennedy Space Center have successfully conducted a proof-of-concept study to develop Meandering Winding Magnetometer (MWM) eddy current sensors designed to make direct measurements of the stresses of the internal layers of a carbon fiber composite wrapped COPV. During this study three different MWM sensors were tested at three orientations to demonstrate the ability of the technology to measure stresses at various fiber orientations and depths. These results showed good correlation with actual surface strain gage measurements. MWM-Array technology for scanning COPVs can reliably be used to image and detect mechanical damage. To validate this conclusion, several COPVs were scanned to obtain a baseline, and then each COPV was impacted at varying energy levels and then rescanned. The baseline subtracted images were used to demonstrate damage detection. These scans were performed with two different MWM-Arrays. with different geometries for near-surface and deeper penetration imaging at multiple frequencies and in multiple orientations of the linear MWM drive. This presentation will include a review of micromechanical models that relate measured sensor responses to composite material constituent properties, validated by the proof of concept study, as the basis for SHM and NDE data analysis as well as potential improvements including design changes to miniaturize and make the sensors durable in the vacuum of space
Russell, Richard↗
Nondestructive Crack Detection in a Fuel System Component
The paper discusses development of various NDE techniques to detect cracks in A40 steel poppets used in a valve of the fuel system of the Space Shuttle Orbiter. The valve assembly experiences a severe high cycle fatigue environment during its operation. Cracks were discovered at the radius of the poppet flange. Experience shows that very small cracks or material anomalies do not cause failure in a single operation event. While the design is being modified to eliminate the issue, NDE has been used to screen the poppets for cracks before every use. Several surface flaw detection techniques were considered and a few NDE techniques were developed to provide NDE screening for the flaw detection. The primary method used was the eddy current testing. In the eddy current technique, the X-Y channel test data from the eddy current instrument was recorded as computer files. A Matlab data review and plotting application was developed to analyze the data files. The Matlab application provides much higher resolution than the eddy current instrument that was used to acquire the data. Other techniques that were used included ultrasonic surface wave and magnetic particle testing. A probability of detection (POD) study was undertaken to determine the 90/95 size for the eddy current technique. This study used specimens with same geometry and material as the poppet. Fatigue cracks were grown in these specimens. Information on results of the NDE techniques and results of the POD study are provided.
Koshti, Ajay↗
Nondestructive Crack Detection in a Fuel System Component
The presentation examines the background and objective of nondestructive crack detection, flow control valve assembly and poppet post flight evaluation, poppet properties. magnetic property characterization of lab data, NDE, eddy current inspection, simulation, eddy current criteria, poppet cycle testing and NDE criteria, and the use of ultrasonic surface wave for crack detection.
Koshti, Ajay↗