Engineering topics

Wojtczuk, Steven

Publications and source records attributed to Wojtczuk, Steven.

8 records

NASA NTRS2012

Inverted Three-Junction Tandem Thermophotovoltaic Modules

An InGaAs-based three-junction (3J) tandem thermophotovoltaic (TPV) cell has been investigated to utilize more of the blackbody spectrum (from a 1,100 C general purpose heat source GPHS) efficiently. The tandem consists of three vertically stacked subcells, a 0.74-eV InGaAs cell, a 0.6- eV InGaAs cell, and a 0.55-eV InGaAs cell, as well as two interconnecting tunnel junctions. A greater than 20% TPV system efficiency was achieved by another group with a 1,040 C blackbody using a single-bandgap 0.6- eV InGaAs cell MIM (monolithic interconnected module) (30 lateral junctions) that delivered about 12 V/30 or 0.4 V/junction. It is expected that a three-bandgap tandem MIM will eventually have about 3 this voltage (1.15 V) and about half the current. A 4 A/cm2 would be generated by a single-bandgap 0.6-V InGaAs MIM, as opposed to the 2 A/cm2 available from the same spectrum when split among the three series-connected junctions in the tandem stack. This would then be about a 50% increase (3xVoc, 0.5xIsc) in output power if the proposed tandem replaced the single- bandgap MIM. The advantage of the innovation, if successful, would be a 50% increase in power conversion efficiency from radioisotope heat sources using existing thermophotovoltaics. Up to 50% more power would be generated for radioisotope GPHS deep space missions. This type of InGaAs multijunction stack could be used with terrestrial concentrator solar cells to increase efficiency from 41 to 45% or more.

Wojtczuk, Steven↗

NASA NTRS1996

Diffusion lengths in irradiated N/P InP-on-Si solar cells

Indium phosphide (InP) solar cells were made on silicon (Si) wafers (InP/Si) by to take advantage of both the radiation-hardness properties of the InP solar cell and the light weight and low cost of Si wafers. The InP/Si cell application is for long duration and/or high radiation orbit space missions. Spire has made N/P InP/Si cells of sizes up to 2 cm by 4 cm with beginning-of-life (BOL) AM0 efficiencies over 13% (one-sun, 28C). These InP/Si cells have higher absolute efficiency and power density after a high radiation dose than gallium arsenide (GaAs) or silicon (Si) solar cells after a fluence of about 2e15 1 MeV electrons/sq. cm. In this work, we investigate the minority carrier (electron) base diffusion lengths in the N/P InP/Si cells. A quantum efficiency model was constructed for a 12% BOL AM0 N/P InP/Si cell which agreed well with the absolutely measured quantum efficiency and the sun-simulator measured AM0 photocurrent (30.1 mA/sq. cm). This model was then used to generate a table of AM0 photocurrents for a range of base diffusion lengths. AM0 photocurrents were then measured for irradiations up to 7.7e16 1 MeV electrons/sq. cm (the 12% BOL cell was 8% after the final irradiation). By comparing the measured photocurrents with the predicted photocurrents, base diffusion lengths were assigned at each fluence level. A damage coefficient K of 4e-8 and a starting (unirradiated) base electron diffusion length of 0.8 microns fits the data well. The quantum efficiency was measured again at the end of the experiment to verify that the photocurrent predicted by the model (25.5 mA/sq. cm) agreed with the simulator-measured photocurrent after irradiation (25.7 mA/sq. cm).

Wojtczuk, Steven↗

NASA NTRS1996

Multijunction InGaAs thermophotovoltaic power converter

The experimental performance of a multijunction monolithic lattice-matched 0.74 eV InGaAs thermophotovoltaic (TPV) power converter under 980 C blackbody irradiation is reported. Eight InGaAs PN junctions grown epitaxially on a semi-insulating wafer were monolithically integrated in series to boost the approximately 0.4 V photovoltage per typical InGaAs junction to over 3 volts for the 1 cm(exp 2) chip. This chip was originally designed and characterized for free-space 1.3 micron laser power beaming. The power efficiency of this TPV device is 16% for that part of the blackbody spectrum above the material bandgap. The device is shown to deliver about 1 watt of output power when driven with enough light. This is the first report of such a multijunction TPV device. This is not a traditional tandem cell in which the junctions are stacked vertically. Eight 1 mm long by 1 cm wide junctions are laterally connected across the device area. This multijunction design has the potential for lower I(exp 2)R power loss since the smaller PN junction area limits the current to one eighth that of the equivalent surface area. In essence, the current is traded for voltage to avoid the I(exp 2)R loss, analogous to the way power utilities avoid I(exp 2)R loss in high-tension power lines, by transforming the high current, low voltage generated at a power plant into a high voltage at a low current before transmitting the power over great distances.

Wojtczuk, Steven↗

NASA NTRS1995

Diffusion lengths in irradiated N/P InP-on-Si solar cells

Indium phosphide (InP) solar cells are being made on silicon (Si) wafers (InP/Si) to take advantage of both the radiation-hardness properties of the InP solar cell and the light weight and low cost of Si wafers compared to InP or germanium (Ge) wafers. The InP/Si cell application is for long duration and/or high radiation orbit space missions. InP/Si cells have higher absolute efficiency after a high radiation dose than gallium arsenide (GaAs) or silicon (Si) solar cells. In this work, base electron diffusion lengths in the N/P cell are extracted from measured AM0 short-circuit photocurrent at various irradiation levels out to an equivalent 1 MeV fluence of 1017 1 MeV electrons/sq cm for a 1 sq cm 12% BOL InP/Si cell. These values are then checked for consistency by comparing measured Voc data with a theoretical Voc model that includes a dark current term that depends on the extracted diffusion lengths.

Wojtczuk, Steven↗

NASA NTRS1995

Multijunction InGaAs thermophotovoltaic power converter

The experimental performance of a multijunction monolithic In(0.53)Ga(0. 47)As power converter under blackbody irradiation is reported. Eight InGaAs PN junctions grown epitaxially on a semi-insulating wafer were monolithically integrated in series to boost the approximately 0.4 V photovoltage per typical InGaAs junction to over 3 volts for the 1 sq cm chip. This chip was originally designed and characterized for free-space 1.3 micron laser power beaming. This is the first report of such a multijunction TPV. This is not a traditional tandem cell in which the junctions are stacked vertically. The junctions are each about 1mm long by 1 cm wide and are laterally connected across the 1 sq cm device area. This multijunction design has the potential for lower I(sup 2)R power loss since the smaller PN junction area limits the current to one-eighth that of the equivalent surface area. In essence, the current is traded for voltage to avoid the I(sup 2)R loss, analogous to the way power utilities avoid I(sup 2)P loss in high-tension power lines, by transforming the high current, low voltage generated at a power plant into a high voltage at a low current before transmitting the power over great distances.

Wojtczuk, Steven↗

NASA NTRS1994

P/N InP solar cells on Ge wafers

Indium phosphide (InP) P-on-N one-sun solar cells were epitaxially grown using a metalorganic chemical vapor deposition process on germanium (Ge) wafers. The motivation for this work is to replace expensive InP wafers, which are fragile and must be thick and therefore heavy, with less expensive Ge wafers, which are stronger, allowing use of thinner, lighter weight wafers. An intermediate InxGs1-xP grading layer starting as In(0.49)Ga(0.51) at the GaAs-coated Ge wafer surface and ending as InP at the top of the grading layer (backside of the InP cell) was used to attempt to bend some of the threading dislocations generated by lattice-mismatch between the Ge wafer and InP cell so they would be harmlessly confined in this grading layer. The best InP/Ge cell was independently measured by NASA-Lewis with a one-sun 25 C AMO efficiently measured by NASA-Lewis with a one-circuit photocurrent 22.6 mA/sq cm. We believe this is the first published report of an InP cell grown on a Ge wafer. Why get excited over a 9 percent InP/Ge cell? If we look at the cell weight and efficiency, a 9 percent InP cell on an 8 mil Ge wafer has about the same cell power density, 118 W/kg (BOL), as the best InP cell ever made, a 19 percent InP cell on an 18 mil InP wafer, because of the lighter Ge wafer weight. As cell panel materials become lighter, the cell weight becomes more important, and the advantage of lightweight cells to the panel power density becomes more important. In addition, although InP/Ge cells have a low beginning-of-life (BOL) efficiency due to dislocation defects, the InP/Ge cells are very radiation hard (end-of-life power similar to beginning-of-life). We have irradiated an InP/Ge cell with alpha particles to an equivalent fluence of 1.6 x 10(exp 16) 1 MeV electrons/sq cm and the efficiency is still 83 percent of its BOL value. At this fluence level, the power output of these InP/Ge cells matches the GaAs/Ge cell data tabulated in the JPL handbook. Data are presented indicating InP/Ge has more power output than GaAs/Ge cells at fluences in excess of this value.

Wojtczuk, Steven↗

NASA NTRS1994

P/N In(Al) GaAs multijunction laser power converters

Eight In(AI)GaAs PN junctions grown epitaxially on the semi-insulating wafer were monolithically integrated in series to boost the approximately 0.4V photovoltage per typical In(Al)GaAs junction to over 3 volts for the 1 sq cm laser power converted (LPC) chip. Advantages of multijunction LCP designs include the need for less circuitry for power reconditioning and the potential for lower I(sup 2)R power loss. As an example, these LPC's have a responsivity of approximately 1 amp/watt. With a single junction LPC, 100 watts/sq cm incident power would lead to about 100 A/sq cm short-circuit current at approximately 0.4V open-cicuit voltage. One disadvantage is the large current would lead to a large I(sup 2)R loss which would lower the fill factor so that 40 watts/sq cm output would not be obtained. Another is that few circuits are designed to work at 0.4 volts, so DC-DC power conversion circuitry would be necessary to raise the voltage to a reasonable level. The multijunction LPC being developed in this program is a step toward solving these problems. In the above example, an eight-junction LPC would have eight times the voltage, approximately 3V, so that DC-DC power conversion may not be needed in many instances. In addition, the multijunction LPC would have 1/8 the current of a single-junction LPC, for only 1/64 the I(sup 2)R loss if the series resistance is the same. Working monolithic multijunction laser power converters (LPC's) were made in two different compositions of the In(x)Al(y)Ga(1-x-y)As semiconductor alloy, In(0.53)Ga(0.47)As (0.74 eV) and In(0.5)Al(0.1)Ga(0.4)As (0.87 eV). The final 0.8 sq cm LPC's had output voltages of about 3 volts and output currents up to about one-half amp. Maximum 1.3 micron power conversion efficiencies were approximately 22 percent. One key advantage of multijunction LPC's is that they have higher output voltages, so that less DC-DC power conversion circuitry is needed in applications.

Wojtczuk, Steven↗

NASA NTRS1994

P/N In(Al) GaAs Multijunction Laser Power Converters

Eight In(Al)GaAs P/N junctions grown epitaxially on a semi-insulating wafer were monolithically integrated in series to boost the approx. 0.4 V photovoltage per typical In(Al)GaAs junction to over 3 volts for the 1 sq cm laser power converter (LPC) chip. This is the first report of a multijunction LPC for the 1.3 to 1.5 microns wavelength range. This wavelength range is optimum for laser power transmission over low- loss single-mode silica optical fiber, and is also useful with high efficiency 1.315 microns iodine lasers in free-space power transmission. Advantages of multijunction LPC designs include the need for less circuitry for power reconditioning and the potential for lower I(exp 2)R power loss. As an example, these LPCs have a responsivity of approx.1 amp/watt. With a single junction LPC, 100 watts/sq cm incident power would lead to about 100 A/sq cM short-circuit current at approx. 0.4 V open-circuit voltage. One disadvantage is the large current would lead to a large 1(exp 2)R loss which would lower the fill factor so that 40 wattS/sq cm output would not be obtained. Another is that few circuits are designed to work at 0.4 volts, so DC-DC power conversion circuitry would be necessary to raise the voltage to a reasonable level. The multijunction LPC being developed in this program is a step toward solving these problems. In the above example, an eight-junction LPC would have eight times the voltage, approx. 3 V, so that DC-DC power conversion may not be needed in many instances. In addition, the multijunction LPC would have 1/8 the current of a single-junction LPC, for only 1/64 the 1(exp 2)R loss if the series resistance is the same. Working monolithic multijunction laser power converters (LPCs) were made in two different compositions of the ln(x)Al(y)Ga(l-x-y)As semiconductor alloy, In(0.53)Ga(0.47)As (0.74 eV) and In(0.5)Al(0.1)Ga(0.4)As (0.87 eV). The final 0.8 sq cm LPCs had output voltages of about 3 volts and output currents up to about one-half amp. Maximum 1.3 microns power conversion efficiencies were approx. 22%. One key advantage of multijunction LPCs is that they have higher output voltages, so that less DC-DC power conversion circuitry is needed in applications.

Wojtczuk, Steven↗