NASA NTRS2009

Recent Advances in Thermoplastic Puncture-Healing Polymers

Self-healing materials provide a route for enhanced damage tolerance in materials for aerospace applications. In particular, puncture-healing upon impact has the potential to mitigate significant damage caused by high velocity micrometeoroid impacts. This type of material also has the potential to improve damage tolerance in load bearing structures to enhance vehicle health and aircraft durability. The materials being studied are those capable of instantaneous puncture healing, providing a mechanism for mechanical property retention in lightweight structures. These systems have demonstrated healing capability following penetration of fast moving projectiles -- velocities that range from 9 mm bullets shot from a gun (approx.330 m/sec) to close to micrometeoroid debris velocities of 4800 m/sec. In this presentation, we report on a suite of polymeric materials possessing this characteristic. Figure 1 illustrates the puncture healing concept. Puncture healing in these materials is dependent upon how the combination of a polymer's viscoelastic properties responds to the energy input resulting from the puncture event. Projectile penetration increases the temperature in the vicinity of the impact. Self-healing behavior occurs following puncture, whereby energy must be transferred to the material during impact both elastically and inelastically, thus establishing two requirements for puncture healing to occur: a.) The need for the puncture event to produce a local melt state in the polymer material and b.) The molten material has to have sufficient melt elasticity to snap back and close the hole. 1,2 Previous ballistic testing studies revealed that Surlyn materials warmed up to a temperature approx.98 C during projectile puncture (3 C higher than it s melting temperature). 1,2 The temperature increase produces a localized flow state and the melt elasticity to snap back thus sealing the hole. Table 1 lists the commercially polymers studied here, together with their physical properties. The polymers were selected based on chemical structure, tensile strengths, tensile moduli, glass transition temperature, melting temperatures, and impact strength. The thermal properties of the polymers were characterized by Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA). Mechanical properties were assessed by a Sintech 2W instron according to ASTM D1708 or D638 at crosshead speeds of 5.08 cm/min. 7.6 cm x 7.6 cm panels of the different materials were prepared and ballistic testing was performed at various temperatures. The panels were shot with a .223 caliber semiautomatic rifle from a distance of 23 meters at various temperatures. Chronographs were used to measure initial and final bullet velocity. Temperatures at the site of impact were measured using a FLIR ThermaCAM S60 thermal camera. A Vision Research model Phantom 9 high speed video camera was used to capture high speed video footage of ballistics testing.

Gordon, K. L.↗

NASA NTRS2007

Thermal Conductivity of Ethylene Vinyl Acetate Copolymer/Nanofiller Blends

To reduce weight and increase the mobility, comfort, and performance of future spacesuits, flexible, thermally conductive fabrics and plastic tubes are needed for the Liquid Cooling and Ventilation Garment. Such improvements would allow astronauts to operate more efficiently and safely for extended extravehicular activities. As an approach to raise the thermal conductivity (TC) of an ethylene vinyl acetate copolymer (Elvax 260), it was compounded with three types of carbon based nanofillers: multi-walled carbon nanotubes (MWCNTs), vapor grown carbon nanofibers (CNFs), and expanded graphite (EG). In addition, other nanofillers including metallized CNFs, nickel nanostrands, boron nitride, and powdered aluminum were also compounded with Elvax 260 in the melt at various loading levels. In an attempt to improve compatibility between Elvax 260 and the nanofillers, MWCNTs and EG were modified by surface coating and through noncovalent and covalent attachment of organic molecules containing alkyl groups. Ribbons of the nanocomposites were extruded to form samples in which the nanofillers were aligned in the direction of flow. Samples were also fabricated by compression molding to yield nanocomposites in which the nanofillers were randomly oriented. Mechanical properties of the aligned samples were determined by tensile testing while the degree of dispersion and alignment of nanoparticles were investigated using high-resolution scanning electron microscopy. TC measurements were performed using a laser flash (Nanoflash ) technique. TC of the samples was measured in the direction of, and perpendicular to, the alignment direction. Additionally, tubing was also extruded from select nanocomposite compositions and the TC and mechanical flexibility measured.

Ghose, S.↗

NASA NTRS2007

Thermal Conductivity of Ethylene Vinyl Acetate Copolymer/Carbon Nanofiller Blends

To reduce weight and increase the mobility, comfort, and performance of future spacesuits, flexible, thermally conductive fabrics and plastic tubes are needed for the Liquid Cooling and Ventilation Garment. Such improvements would allow astronauts to operate more efficiently and safely for extended extravehicular activities. As an approach to raise the thermal conductivity (TC) of an ethylene vinyl acetate copolymer (Elvax 260), it was compounded with three types of carbon based nanofillers: multi-walled carbon nanotubes (MWCNTs), vapor grown carbon nanofibers (CNFs), and expanded graphite (EG). In addition, other nanofillers including metallized CNFs, nickel nanostrands, boron nitride, and powdered aluminum were also compounded with Elvax 260 in the melt at various loading levels. In an attempt to improve compatibility between Elvax 260 and the nanofillers, MWCNTs and EG were modified by surface coating and through noncovalent and covalent attachment of organic molecules containing alkyl groups. Ribbons of the nanocomposites were extruded to form samples in which the nanofillers were aligned in the direction of flow. Samples were also fabricated by compression molding to yield nanocomposites in which the nanofillers were randomly oriented. Mechanical properties of the aligned samples were determined by tensile testing while the degree of dispersion and alignment of nanoparticles were investigated using high-resolution scanning electron microscopy. TC measurements were performed using a laser flash (Nanoflash ) technique. TC of the samples was measured in the direction of, and perpendicular to, the alignment direction. Additionally, tubing was also extruded from select nanocomposite compositions and the TC and mechanical flexibility measured.

Ghose, S.↗

NASA NTRS2007

Thermal Conductivity of Copoly(ethylene vinyl acetate)/Nano-Filler Blends

The development of flexible, thermally conductive fabrics and plastic tubes for the Liquid Cooling and Ventilation Garment (LCVG) are needed to reduce weight and improve the mobility, comfort, and performance of future spacesuits. Such improvements would allow astronauts to operate more efficiently and safely for extended extravehicular activities. As a continuation of our work on the improvement of thermal conductivity (TC) of polymeric materials, nanocomposites were prepared from copoly(ethylene vinyl acetate), trade name Elvax 260TradeMark), metallized carbon nanofibers (CNFs), nickel (Ni) nanostrands, boron nitride both alone and as mixtures with aluminum powder. The nanocomposites were prepared by melt mixing at various loading levels and subsequently fabricated into several material forms (i.e., ribbons, tubes, and compression molded plaques) for analysis. Ribbons and tubes were extruded to form samples in which the nanoparticles were aligned in the direction of flow. The degree of dispersion and alignment of the nanoparticles were investigated using high-resolution scanning electron microscopy. Tensile properties of the aligned samples were determined at room temperature. TC measurements were performed using a laser flash (Nanoflash(TradeMark) technique. The TC of the samples was measured in both the direction of alignment as well as transverse. Tubing of comparable dimensions to that used in the LCVG was extruded from select compositions and the thermal conductivities of the tubes measured.

Ghose, S.↗

NASA NTRS2007

Thermal Conductivity of Polymer Copoly(Ethylene Vinyl Acetate)/Nano-Filler Blends

The development of flexible, thermally conductive fabrics and plastic tubes for the Liquid Cooling and Ventilation Garment (LCVG) are needed to reduce weight and improve the mobility, comfort, and performance of future spacesuits. Such improvements would allow astronauts to operate more efficiently and safely for extended extravehicular activities. As a continuation of our work on the improvement of thermal conductivity (TC) of polymeric materials, nanocomposites were prepared from copoly(ethylene vinyl acetate), trade name Elvax 260 , metallized carbon nanofibers (CNFs), nickel (Ni) nanostrands, boron nitride both alone and as mixtures with aluminum powder. The nanocomposites were prepared by melt mixing at various loading levels and subsequently fabricated into several material forms (i.e., ribbons, tubes, and compression molded plaques) for analysis. Ribbons and tubes were extruded to form samples in which the nanoparticles were aligned in the direction of flow. The degree of dispersion and alignment of the nanoparticles were investigated using high-resolution scanning electron microscopy. Tensile properties of the aligned samples were determined at room temperature. TC measurements were performed using a laser flash (Nanoflash ) technique. The TC of the samples was measured in both the direction of alignment as well as transverse. Tubing of comparable dimensions to that used in the LCVG was extruded from select compositions and the thermal conductivities of the tubes measured.

Ghose, S.↗

NASA NTRS2007

Thermal Conductivity of Polyimide/Carbon Nanofiller Blends

In efforts to improve the thermal conductivity (TC) of Ultem(TM) 1000, it was compounded with three carbon based nano-fillers. Multiwalled carbon nanotubes (MWCNT), vapor grown carbon nanofibers (CNF) and expanded graphite (EG) were investigated. Ribbons were extruded to form samples in which the nano-fillers were aligned. Samples were also fabricated by compression molding in which the nano-fillers were randomly oriented. The thermal properties were evaluated by DSC and TGA, and the mechanical properties of the aligned samples were determined by tensile testing. The degree of dispersion and alignment of the nanoparticles were investigated with high-resolution scanning electron microscopy. The thermal conductivity of the samples was measured in both the direction of alignment as well as perpendicular to that direction using the Nanoflash technique. The results of this study will be presented.

Ghose, S.↗

NASA NTRS2006

Thermal Conductivity of Polyimide/Carbon Nanofiller Blends

Ultem(TM) was mixed with three different carbon-based nanofillers in efforts to increase the thermal conductivity of the polymer. After initial mixing, the nanocomposites were extruded or processed via the Laboratory Mixing Molder (LMM) process. High resolution scanning electron microscopy (HRSEM) revealed significant alignment of the nanofillers in the extruded samples. Thermal conductivity measurements were made both in the direction and perpendicular to the direction of alignment of nanofillers as well as for unaligned samples. It was found that the largest improvement in thermal conductivity was achieved in the case of aligned samples when the measurement was performed in the direction of alignment. Unaligned samples also showed a significant improvement in thermal conductivity and may be useful in applications when it is not possible to align the nanofiller. However the improvements in thermal conductivity did not approach those expected based on a rule of mixtures. This is likely due to poor phonon transfer through the matrix.

Delozier, D. M.↗

NASA NTRS2006

Thermal Conductivity of Ultem(TradeMark)/Carbon Nanofiller Blends

In an effort to improve polymer thermal conductivity (TC), Ultem(TradeMark) 1000 was compounded with nano-fillers of carbon allotropes. Ultem(TradeMark) 1000 was selected since it is both solution and melt processable. As-received and modified multiwalled carbon nanotubes (MWCNTs), vapor grown carbon nanofibers (CNF) and expanded graphite (EG) were investigated. MWCNTs were modified by functionalizing the surface through oxidization with concentrated acids, mixing with an alkyl bromide, and addition of alkyl and phosphorus compounds after initial treatment with n-butyl lithium. Functionalization was performed to improve the TC compatibility between the resin and MWCNTs. It was postulated that this may provide an improved interface between the MWCNT and the polymer which would result in enhanced TC. The nano-fillers were mixed with Ultem(TradeMark) 1000 in the melt and in solution at concentrations ranging from 5 to 40 wt%. Ribbons were extruded from the blends to form samples where the nano-fillers were aligned to some degree in the extrusion direction. Samples were also fabricated by compression molding resulting in random orientation of the nano-fillers. Thermal properties of the samples were evaluated by Differential Scanning Calorimetry (DSC) and Thermal Gravimetric Analyzer (TGA). Tensile properties of aligned samples were determined at room temperature. The specimens were cut from the ribbons in the extrusion direction; hence the nano-fillers are somewhat aligned in the direction of stress. Typically it was observed that melt mixed samples exhibited superior mechanical properties compared to solution mixed samples. As expected, increased filler loading led to increased modulus and decreased elongation with respect to the neat polymer. The degree of dispersion and alignment of the nano-fillers was determined by high-resolution scanning electron microscopy (HRSEM). HRSEM of the ribbons revealed that the MWCNTs and CNFs were predominantly aligned in the flow direction. The TC of the samples was measured using a Nanoflash(TradeMark) instrument. Since the MWCNTs and CNF are anisotropic, the TC was expected to be different in the longitudinal (parallel to the nanotube and fiber axis) and transverse (perpendicular to the nanotube and fiber axis) directions. The extruded ribbons provided samples for transverse TC measurements. However, to determine the TC in the longitudinal direction, the ribbons needed to be stacked and molded under 1.7 MPa and 270 C. Samples were then obtained by cutting the molded block with a diamond saw. The largest TC improvement was achieved for aligned samples when the measurement was performed in the direction of MWCNT and CNF alignment (i.e. longitudinal axis). Unaligned samples also showed a significant improvement in TC and may be potentially useful in applications when it is not possible to align the nano-filler. The results of this study will be presented.

Ghose, S.↗