Engineering topics
Worth, Robert N.
Publications and source records attributed to Worth, Robert N..
Using porous random fields to predict the elastic modulus of unoxidized and oxidized superfine graphite
Nuclear graphite is a candidate material for Generation IV nuclear power plants. Porous materials such as graphite can contain complex networks of pores that influence the material's mechanical and irradiation response. A methodology known as the random finite element method (RFEM) was adapted to create synthetic microstructures and predict the influence of porosity on the elastic properties of graphite during oxidation. RFEM combines random field theory and the finite element method in a Monte Carlo framework to estimate the mechanical response of a given grade of graphite. In this research, the random fields were verified through experimental characterization to predict the elastic response of three nuclear graphite grades, ETU-10, IG-110, and 2114. Finite element models (FEM) were generated using segmentations of x-ray computed tomography (XCT) data known as image-based models (IBMs) to validate and compare with the RFEM results and better understand the effects of uniform oxidation in these graphite grades. The RFEM predictions appear to correlate well with the experimental values of the measured Young’s modulus of the three graphite grades and display the same trends as IBMs.
Multiscale characterization and comparison of historical and modern nuclear graphite grades
Beginning with Chicago Pile I, graphite has been used as a moderator material in nuclear power stations and is considered a potential material for use in future Generation IV advanced reactors. The microstructure of graphite is responsible for much of its mechanical and thermo-physical properties, and how it responds to irradiation. To understand graphite microstructure, it is necessary to understand its porosity at the macro- and micro-scales; and to understand its porosity, it is necessary to characterize the morphological connectivity of the void content and the two main phases of graphite: filler and binder. Here, using several microscopy and analytical techniques, a detailed examination of the heterogeneity, microstructure and pore structure of different graphite grades and their binder and filler phases is presented. Significant differences were found between coarser and finer nuclear grades. Coarse grades have a more diverse range of filler particles, pores and thermal cracks. Finer grades have a more well-defined pore size distribution, fewer variations of filler particles sizes and do not contain as many large thermal cracks. Fine grades tend to have a well-connected network of pores whereas coarser grades contain a larger content of closed porosity. The framework developed within this work can be applied and used to assess the various graphite grades that would down-select materials for specific use in graphite moderated reactor designs.
The distribution and selective decontamination of carbon-14 from nuclear graphite
This work investigates 14 C release behaviour from UK Magnox reactor sourced irradiated graphite under relatively low temperature oxidation conditions: a 1% oxygen in argon atmosphere at temperatures ranging from 600°C to 700°C, and durations from 4 to 120 hours. A method is used for construction of a detailed 14 C release profile with mass loss. The 14 C release profile is predictable between samples, and an empirical release profile is derived to predict releases to higher mass losses than in this work. An accelerated 14 C release rate at small mass losses is observed, indicative of a 14 C-enriched surface region with a depleting concentration gradient into the material, and the source terms and complexities associated with predicting where the 14 C arose from are discussed. Selective decontamination of a fraction of the 14 C is possible, with the limitation of a reducing efficiency with mass loss and time. This work demonstrates a method for determining the distribution of 14 C between near-surface regions and the bulk material in differing sources of irradiated graphite, and provides data in support of making an informed assessment for the adoption of low temperature thermal treatment and isotopic reduction of irradiated graphite wastes.
Observations of crystal strains in filler and QI particles through TEM examination – Effect of processing and grain size
Not Available