NASA NTRS1975

Creep behavior of uranium carbide-based alloys

The present work gives the results of experiments on the influence of zirconium carbide and tungsten on the creep properties of uranium carbide. The creep behavior of high-density UC samples follows the classical time-dependence pattern of (1) an instantaneous deformation, (2) a primary creep region, and (3) a period of steady-state creep. Creep rates for unalloyed UC-1.01 and UC-1.05 are several orders of magnitude greater than those measured for carbide alloys containing a Zr-C and/or W dispersoid. The difference in creep strength between alloyed and unalloyed materials varies with temperature and applied stress.

Seltzer, M. S.↗
NASA NTRS1974

Improved toughness of refractory compounds

The concept of grain-boundary-engineering through elimination of the grain-boundary silicate phase in silicon nitride was developed. The process involved removal of the silica from the nitride powder via a thermal treatment coupled with the use of nitride additives to compensate the remaining oxygen. Magnesium and aluminum nitrides are found to be the most effective additive for use as oxygen compensators. Strength decreases at elevated temperatures are not observed in the alumina containing material. The creep rate of a dual additive sialon composition was two orders of magnitude lower at 1400 C than commercial silicon nitride. A cursory analysis of the creep mechanism indicate that grain-boundary sliding is avoided through elimination of the grain-boundary silicate phase.

Wright, T. R.↗
NASA NTRS1974

Out-of-pile creep behavior of uranium carbide

Compression creep tests were investigated on various UC-based fuel materials having a variation in both density and composition. Specimens were prepared by casting and by hot pressing. Steady-state creep rates were measured under vacuum at 1400 to 1800 C in the stress range 500-4000 psi.

Wright, T. R.↗
NASA NTRS1973

Preparation of refractory cermet structures for lithium compatibility testing

High-purity nitride and carbide cermets were synthesized for compatability testing in liquid lithium. A process was developed for the preparation of high-purity hafnium nitride powder, which was subsequently blended with tungsten powder or tantalum nitride and tungsten powders and fabricated into 3 in diameter billets by uniaxial hot pressing. Specimens were then cut from the billets for compatability testing. Similar processing techniques were applied to produce hafnium carbide and zirconium carbide cermets for use in the testing program. All billets produced were characterized with respect to chemistry, structure, density, and strength properties.

Heestand, R. L.↗