DOE OSTI2022

Atomically dispersed Pt and Fe sites and Pt–Fe nanoparticles for durable proton exchange membrane fuel cells

Proton exchange membrane fuel cells convert hydrogen and oxygen into electricity without emissions. The high cost and low durability of Pt-based electrocatalysts for the oxygen reduction reaction hinder their wide application, and the development of non-precious metal electrocatalysts is limited by their low performance. Here we design a hybrid electrocatalyst that consists of atomically dispersed Pt and Fe single atoms and Pt–Fe alloy nanoparticles. Its Pt mass activity is 3.7 times higher than that of commercial Pt/C in a fuel cell. More importantly, the fuel cell with a low Pt loading in the cathode (0.015 mg Pt cm –2 ) shows an excellent durability, with a 97% activity retention after 100,000 cycles and no noticeable current drop at 0.6 V for over 200 hours. These results highlight the importance of the synergistic effects among active sites in hybrid electrocatalysts and provide an alternative way to design more active and durable low-Pt electrocatalysts for electrochemical devices.

25 ENERGY STORAGE↗

DOE OSTI2021

Solid-State Synthesis of Highly Dispersed Nitrogen-Coordinated Single Iron Atom Electrocatalysts for Proton Exchange Membrane Fuel Cells

Fe–N–C with atomically dispersed Fe single atoms is the most promising candidate to replace platinum for the oxygen reduction reaction (ORR) in fuel cells. However, the conventional synthesis procedures require quantities solvents and metal precursors, sluggish adsorption process, and tedious washing, resulting in limited metal doping and uneconomical for large-scale production. Here, for the first time, Fe 2 O 3 is adopted as the Fe precursor to derive abundant single Fe atoms dispersed on carbon surfaces. The Fe–N–C catalyst synthesized by this simple method shows an excellent ORR activity with half-wave potentials of 0.82 and 0.90 V in acidic and alkaline solutions, respectively. A single fuel cell with an optimized Fe–N–C cathode shows a high peak power density of 0.84 W cm –2 . The solid-state transformation synthesis method developed in this study may shed light on mass production of single-atom-based catalysts.

25 ENERGY STORAGE↗

DOE OSTI2020

Durable hybrid electrocatalysts for proton exchange membrane fuel cells

The low durability of carbon-based non-precious metal electrocatalysts hinders their practical applications in proton exchange membrane fuel cells (PEMFCs). In this study, we rationally design a hybrid Pt-Fe-N-C electrocatalyst with unprecedented durability. It consists of abundant Pt and Fe single atoms homogeneously dispersed on the nitrogen-doped carbon support and a small amount of Pt-Fe alloy nanoparticles. A PEMFC with Pt-Fe-N-C as the cathode shows a larger peak power density (0.75 W cm -2 ) than that with Fe-N-C as the cathode (0.50 W cm -2 ). The remarkable durability of Pt-Fe-N-C is reflected from no noticeable drop in the half-wave potential after 70000 potential cycles between 0.6 and 1.0 V in the liquid cell, and 80% current retention after 85 h of potential hold at 0.4 V in the fuel cell. This work demonstrates the feasibility of improving the durability of Fe-N-C material via ultra-low Pt doping and makes non-precious metal electrocatalysts be close to achieving commercial metrics.

25 ENERGY STORAGE↗