3 records

DOE OSTI2024

Magnetic structure and magnetoelectric effect in the centrosymmetric antiferromagnet Cu 2 ( MoO 4 ) ( SeO 3 )

Magnetic properties of Cu 2 ⁢(MoO 4 )⁢(SeO 3 ), an S = $\frac{1}{2}$ centrosymmetric antiferromagnet (AFM), were investigated using superconducting quantum interference device magnetometry, neutron diffraction, and magnetoelectric (ME) measurements. Here, the magnetic susceptibility measurements indicate a broad peak at ~50 K, followed by a phase transition into AFM order at T N = 23.6⁢(1) K. Above T N , a fit to the Curie-Weiss law gives a Curie-Weiss temperature Θ CW = -68⁢(1) K, suggesting the dominant AFM coupling. Neutron powder diffraction reveals that the C⁢u 2+ spins are aligned AFM along the c axis with weak noncollinearity under the magnetic space group of P2$^{'}_{1}$/c. The ME response indicates that a nondiagonal component of a ME tensor is active, supporting the simultaneous spatial and time reversal symmetry breaking under P2$^{'}_{1}$/c.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗

DOE OSTI2021

Magnetocapacitance effect and magnetoelectric coupling in type-II multiferroic HoFeWO 6

We have investigated the multiferroicity and magnetoelectric (ME) coupling in HoFeWO 6 . With a noncentrosymmetric polar structure (space group Pna2 1 ) at room temperature, this compound shows an onset of electric polarization with an antiferromagnetic ordering at the Néel temperature (T N ) of 17.8 K. The magnetic properties of the polycrystalline samples were studied by DC and AC magnetization and heat capacity measurements. The metamagnetic behavior at low temperatures was found to be directly related to the dielectric properties of the compound. In particular, field-dependent measurements of capacitance show a magnetocapacitance (MC) effect with double-hysteresis loop behavior in direct correspondence with the magnetization. Our x-ray diffraction results show the Pna2 1 structure down to 8 K and suggest the absence of a structural phase transition across T N . Soft x-ray absorption spectroscopy and soft x-ray magnetic circular dichroism (XMCD) measurements at the Fe L 2,3 and Ho M 4,5 edges revealed the oxidation state of Fe and Ho cations to be 3+. Fe L 2,3 XMCD further shows that Fe 3+ cations are antiferromagnetically ordered in a noncollinear fashion with spins arranged 90° with respect to each other. Our findings show that HoFeWO 6 is a type-II multiferroic exhibiting a MC effect. Furthermore, the observed MC effect and the change in polarization by the magnetic field, as well as their direct correspondence with magnetization, further support the strong ME coupling in this compound.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗

DOE OSTI2020

Room-temperature skyrmion phase in bulk Cu 2 OSeO 3 under high pressures

Significance Skyrmion materials hold great promise for information technology due to the extremely low current needed to modify the spin configurations and the small size of magnetic domains. To facilitate their application, one great challenge is to break the magnetic field–temperature phase space restriction for the skyrmion state. We found that the temperature region for the skyrmion phase in bulk Cu 2 OSeO 3 can be greatly enhanced under physical pressure, making applications more practical by the use of strained heterostructures, for example. The observation of additional structures suggests that the skyrmion state may be insensitive to the underlying crystal structure. This work will stimulate research on finding skyrmion materials with different crystal structures and retaining the room-temperature skyrmion state at ambient condition.

Deng, Liangzi↗