Rational design of technologically important exotic perovskites is hampered by the insufficient geometrical descriptors and costly and extremely high-pressure synthesis, while the big-data driven compositional identification and precise prediction entangles full understanding of the possible polymorphs and complicated multidimensional calculations of the chemical and thermodynamic parameter space. Here we present a rapid systematic data-mining-driven approach to design exotic perovskites in a high-throughput and discovery speed of the A 2 BB ’O 6 family as exemplified in A 3 TeO 6 . The magnetoelectric polar magnet Co 3 TeO 6 , which is theoretically recognized and experimentally realized at 5 GPa from the six possible polymorphs, undergoes two magnetic transitions at 24 and 58 K and exhibits helical spin structure accompanied by magnetoelastic and magnetoelectric coupling. We expect the applied approach will accelerate the systematic and rapid discovery of new exotic perovskites in a high-throughput manner and can be extended to arbitrary applications in other families.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Single-Crystal Growth and Room-Temperature Magnetocaloric Effect of X-Type Hexaferrite Sr 2 Co 2 Fe 28 O 46

X-type hexaferrites have been receiving considerable attention due to their promising applications in many magnetic-electronic fields. However, the growth of single-crystal X-type hexaferrite is still a challenge. Herein we reported, for the first time, the preparation of single crystal X-type hexaferrite Sr 2 Co 2 Fe 28 O 46 (Sr 2 Co 2 X) with high-quality and large size using floating-zone method with laser as the heating source. The crystals show rhombohedral symmetry with space group of R-3m (No. 166, a = 5.8935(1) Å and c = 83.7438(17) Å). Co 2+ and Fe 3+ oxidation states were confirmed by the X-ray absorption near-edge spectroscopy. The prepared Sr 2 Co 2 X exhibits a spin reorientation transition from easy-cone to easy-axis at T 2 of 343 K and a ferrimagnetism–paramagnetism transition at Curie temperature (TC) of ~743 K. The spin reorientation transition was accompanied by magnetocaloric effect (MCE). Both conventional and inverse MCEs were observed near T 2 with a magnetic field applied along the c-axis. The maximum value of the magnetic entropy change along the c-axis was evaluated to be 1.1 J/kg·K for a magnetic field change of 5 T.

36 MATERIALS SCIENCE↗

DOE OSTI2019

Spin Liquid State and Topological Structural Defects in Hexagonal TbInO 3

Not Available