An additively manufactured near-eutectic Al-Ce-Ni-Mn-Zr alloy with high creep resistance

A new additively manufactured (AM) Al-7.5Ce-4.5Ni-0.4Mn-0.7Zr (wt.%) near-eutectic alloy is reported, which shows unprecedented creep resistance up to 400 °C (a homologous temperature of 0.72). The eutectic solidification microstructure comprises ~ 27 vol% of coarsening-resistant second phase network with an ultrafine (<100 nm) inter-phase spacing. Both Mn and Zr contribute to creep resistance of the alloy. Small amount of Mn addition promotes selection of coarsening resistant phases without compromising the alloy processability. Zr not only improves hot-tearing resistance, but further enhances the second phase coarsening resistance resulting in improved creep resistance. Neutron diffraction performed during creep deformation reveals that the underlying mechanism for creep resistance in this alloy is impedance to dislocation motion stemming from the ultrafine eutectic solidification microstructure, whereas load transfer strengthening becomes less effective as the creep temperature increases. The second phase forms a continuous network in the as-fabricated condition, which is maintained during long-term creep at 300 °C. However, this network is fragmented into fine dispersoids at higher temperatures. It is proposed that the rate-limiting deformation mechanism at 300–400 °C is (i) dislocation climb for the alloy with fragmented second phase dispersoids and (ii) Orowan looping for the alloy with a continuous second phase network. In conclusion, the present design of an AM-processable multicomponent eutectic alloy with high creep resistance can be applied to other metallic systems exhibiting eutectic reactions, with expected extreme creep resistance.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Microstructure and strengthening of Al-6Ce-3Ni-0.7Fe (wt%) alloy manufactured by laser powder-bed fusion

In this study, an Al-6Ce-3Ni-0.7Fe (wt%) alloy was fabricated via laser powder-bed fusion and its microstructure, thermal stability, tensile properties, and creep properties are investigated for two rapid-solidification rates with different eutectic spacings. For both faster- and slower-cooled states, the as-fabricated alloy mostly shows elongated grains with very fine eutectic networks (~40 nm lamellar width) comprising a high-volume fraction (~18 %) of intermetallic phases. Faster-cooled samples, however, display a less continuous eutectic network with finer spacing (~100 nm), leading to higher Orowan strengthening and therefore superior microhardness and yield stress up to ~350 °C. Upon aging (300 - 450 °C), micron-size Al 9 (Ni,Fe) 2 needle-like precipitates form within grains, and the Al 11 Ce 3 eutectic network spheroidizes, while retaining a submicron width and spacing, resulting in 33–37 % drop in microhardness after 144 h aging at 400 °C. Limited tensile ductility (~6 %) and creep ductility (~1-2 %) are measured for both faster- and slower-cooled alloys due to an inhomogeneous microstructure, where cavitation preferentially initiates at melt-pool boundaries, precipitate-free zones, and/or denuded zones, eventually leading to local fracture. Denuded zones, induced by stress, form due to diffusional flow with stress-dependent orientations, and are identified as microstructurally weak regions leading to strain localization. The present alloy does not show a significant difference in 300 °C creep resistance between: (i) tensile and compressive loading, (ii) faster- and slower-cooled samples, and (iii) continuous and spheroidized eutectics. Creep resistance at 300 °C is comparable to that of a Ce-richer Al-10.5Ce-3.1Ni-1.2Mn (wt%) alloy, despite the formation of denuded zones and needle-like Al 9 (Ni,Fe) 2 precipitates.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Microstructure and mechanical properties of hypoeutectic Al–6Ce–3Ni-0.7Fe (wt.%) alloy

Here, a hypoeutectic, Fe-modified Al–Ce–Ni alloy (Al–6Ce–3Ni-0.7Fe, wt.%) is studied in terms of microstructure, thermal stability, ambient temperature strengthening, and creep resistance. The as-cast microstructure consists of primary Al dendrites and interdendritic binary eutectic regions (Al–Al11Ce3 and/or Al–Al9(Fe,Ni)2), with micron/submicron lamellar spacing, depending on the location along the height of the ingot. The cast alloy exhibits excellent coarsening resistance at 400 °C, with mostly unchanged microstructure and microhardness after 6 weeks of aging, indicating good thermal stability of Al11Ce3 and Al9(Fe,Ni)2. Orowan strengthening and load transfer are identified as strengthening mechanisms at ambient and elevated temperature. A high volume fraction of the intermetallic phases (providing load transfer) and relatively coarse eutectic spacing (for modest Orowan strengthening) result in a moderate as-cast microhardness of 566 ± 32 MPa. Creep resistance at 300 and 350 °C is similar to a binary Al-12.5Ce eutectic alloy (with twice the Ce content) because of two countering effects: Al–6Ce–3Ni-0.7Fe shows a higher volume fraction of strengthening intermetallic phases, but it also exhibits a large fraction of primary Al dendrites which weaken the alloy. By contrast, the alloy, when laser-remelted at the surface, has a fully eutectic microstructure without primary aluminum dendrites achieved by high undercooling on solidification, with a refined network of eutectic phases that doubles the microhardness as compared to the cast alloy. Whereas coarsening is faster due to the shorter diffusion distances between the eutectic phases, hardness remains ~30% higher than the as-cast alloy after ~6 weeks aging at 400 °C.

36 MATERIALS SCIENCE↗
DOE OSTI2023

PYK-SubstitutionOME: an integrated database containing allosteric coupling, ligand affinity and mutational, structural, pathological, bioinformatic and computational information about pyruvate kinase isozymes

Interpreting changes in patient genomes, understanding how viruses evolve and engineering novel protein function all depend on accurately predicting the functional outcomes that arise from amino acid substitutions. To that end, the development of first-generation prediction algorithms was guided by historic experimental datasets. However, these datasets were heavily biased toward substitutions at positions that have not changed much throughout evolution (i.e. conserved). Although newer datasets include substitutions at positions that span a range of evolutionary conservation scores, these data are largely derived from assays that agglomerate multiple aspects of function. To facilitate predictions from the foundational chemical properties of proteins, large substitution databases with biochemical characterizations of function are needed. We report here a database derived from mutational, biochemical, bioinformatic, structural, pathological and computational studies of a highly studied protein family—pyruvate kinase (PYK). A centerpiece of this database is the biochemical characterization—including quantitative evaluation of allosteric regulation—of the changes that accompany substitutions at positions that sample the full conservation range observed in the PYK family. We have used these data to facilitate critical advances in the foundational studies of allosteric regulation and protein evolution and as rigorous benchmarks for testing protein predictions. We trust that the collected dataset will be useful for the broader scientific community in the further development of prediction algorithms.

59 BASIC BIOLOGICAL SCIENCES↗
DOE OSTI2021

Microstructure and creep properties of cast near-eutectic Al–Ce–Ni alloys

This study investigates the as-cast and aged microstructures, thermal stability, ambient temperature strengthening, and creep resistance of three ternary Al–Ce–Ni alloys (wt%): near-eutectic Al–10Ce–5Ni (with both eutectic and hypoeutectic regions), hypoeutectic Al-7.5Ce-3.75Ni (with numerous primary Al dendrites), and hypereutectic Al-12.5Ce-6.25Ni (with coarse, blocky primary Al3Ni and Al11Ce3 precipitates and some primary Al dendrites). Depending on the alloy composition and local solidification conditions, the following eutectic morphologies are found: (i) coarse Al–Ce eutectic colonies where Al 11 Ce 3 is in the form of “Chinese script”, (ii) intermingled regions of binary Al–Ce and Al–Ni eutectic colonies, with finer Al 3 Ni and Al 11 Ce 3 fibers, (iii) large ternary eutectic colonies, where the binary Al 3 Ni and Al 11 Ce 3 phases are alternating or intertwining within the individual, fine fibers (diameters of ~60–170 nm, depending on solidification rates), and (iv) ternary eutectic zones (between primary Al dendrites), where fine Al 3 Ni and Al 11 Ce 3 build up a 3D-interconnected network. The high volume fraction of intermetallic phases and extremely fine eutectic spacing/fiber diameter both contribute to high ambient strengthening (higher as-cast microhardness than binary Al–Ce or Al–Ni), and also provide enhanced creep resistance at 300 and 350 °C. Additionally, the alloys are coarsening-resistant up to 425 °C for extended periods, with a gradual decrease in microhardness. The alloys aged at 400 °C to 1050 h show fiber fragmentation and coarsening of the resulting particles, with the faster-diffusing Ni driving more rapid coarsening of the Al 3 Ni particles which engulf finer, more stable Al 11 Ce 3 particles. Severe overaging (performed at 590 °C for 24 h) leads to Al 3 Ni and Al 11 Ce 3 spheroids which remain submicron-sized in eutectic colonies, but micron-sized at colony boundary and at Al dendrite-eutectic interface. Creep resistance at 300 °C of overaged Al–10Ce–5Ni remains substantial, consistent with load-transfer based composite strengthening being an important strengthening mechanism in these alloys, making them excellent candidates for replacement of heavier steel or titanium parts operating under stress up to 300 °C.