Spatiotemporal Reaction Dynamics Control in Two‐Photon Polymerization for Enhancing Writing Characteristics

Since 2001, 3D microfabrication based on two‐photon polymerization (TPP) has drawn extensive attention and interest in biology, optics, photonics, material science, and high‐energy physics. The in‐volume fabrication capability due to the threshold behavior of two‐photon absorption enables TPP higher flexibility compared with other nanofabrication techniques. However, as determined by the in‐volume fabrication feature as well as various reaction dynamics, the writing characteristics of TPP, such as throughput, accuracy, surface quality, and fabrication capability, are still limited. Herein, a comprehensive study is performed on the spatiotemporal behavior of reaction dynamics during TPP fabrication, mainly focusing on spatiotemporal characteristics of radical diffusion, photothermal effect, microscale mechanics, and voxel stacking process. Based on the study, a nonsequential fabrication method is established to simultaneously improve key writing characteristics of TPP and realize sharp features, high speeds, large overhang structure, and smooth surfaces. The method established in this work can be applied to improve the performance of functional devices for various fields.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Direct selective laser sintering of hexagonal barium titanate ceramics

Abstract A direct selective laser sintering (SLS) process was combined with a laser preheating procedure to decrease the temperature gradient and thermal stress, which was demonstrated as a promising approach for additive manufacturing of BaTiO 3 ceramics. The phase compositions in BaTiO 3 ceramics fabricated by SLS were investigated by X‐ray and neutron diffractions. The surface morphologies and cross‐section microstructures were characterized by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). A dense hexagonal h‐BaTiO 3 layer was formed on the surface and extended to a depth of 500 μm, with a relative density higher than 97% and absence of pores or microcracks. SLS resulted in the formation of the high‐temperature phase, h‐BaTiO 3 , which was retained at room temperature possibly due to the high cooling rate. The grain boundaries of SLSed h‐BaTiO 3 ceramics consist of a Ti‐rich secondary phase. Compared with that of the pressureless sintered t‐BaTiO 3 ceramics, the Vickers hardness of SLSed h‐BaTiO 3 is 70% higher.

Zhang, Xiang↗