Xiang, Sisi

Publications and source records attributed to Xiang, Sisi.

6 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2022

Micropillar Compression of Additively Manufactured 316L Stainless Steels after 2 MeV Proton Irradiation: A Comparison Study between Planar and Cross-Sectional Micropillars

A micropillar compression study with two different techniques was performed on proton-irradiated additively manufactured (AM) 316L stainless steels. The sample was irradiated at 360 °C using 2 MeV protons to 1.8 average displacement per atom (dpa) in the near-surface region. A comparison study with mechanical test and microstructure characterization was made between planar and cross-sectional pillars prepared from the irradiated surface. While a 2 MeV proton irradiation creates a relatively flat damage zone up to 12 µm, the dpa gradient by a factor of 2 leads to significant dpa uncertainty along the pillar height direction for the conventional planar technique. Cross-sectional pillars can significantly reduce such dpa uncertainty. From one single sample, three cross-sectional pillars were able to show dpa-dependent hardening. Furthermore, post-compression transmission electron microscopy allows the determination of the deformation mechanism of individual micropillars. Cross-sectional micropillar compression can be used to study radiation-induced mechanical property changes with better resolution and less data fluctuation.

transmission electron microscopy↗
DOE OSTI2022

Outgassing of implanted He via short circuit transport along phase and grain boundaries in vapor co-deposited Cu-W nanocomposites

We investigate the response of physical vapor co-deposited copper (Cu)-tungsten (W) nanocomposites to helium (He) implantation. Nuclear reaction analysis (NRA) reveals that a substantial fraction of He implanted into these materials escapes during implantation. Analysis of nanocomposite microstructure shows that the He loss is likely due to its transport out of the material by diffusion along phase and grain boundaries. Lastly, our findings suggest that solid-state interfaces such as phase and grain boundaries are short circuit diffusion pathways for transport of He.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Enhancing the multi-functional properties of renewable lignin carbon fibers via defining the structure–property relationship using different biomass feedstocks

Lignin has been explored extensively as a renewable precursor for carbon materials, considering its abundance as a major component of plant cell walls and its sustainability as a byproduct of both lignocellulosic biorefinery and the paper-making industry. Despite the extensive efforts to define the process–property relationship, it remains largely unknown how lignin biosynthesis and its chemistry would impact the resultant carbon fiber properties, for both mechanical and electroconductive performances. Such inadequate understanding fundamentally limits feedstock design and selection to improve carbon fiber properties toward broader commercial applications. Using lignin from a broad range of biomass feedstocks for carbon fiber manufacturing, we have fundamentally explored the structure–function relationship between lignin chemistry and carbon fiber performance. Specifically, lignin extracted from hardwood (sugar maple), softwood (loblolly pine and red cedar), and herbaceous plants (corn stover and switchgrass) was used for carbon fiber manufacturing, considering the very different lignin structures from these feedstocks. Linear regression models were established to define the relationship between carbon fiber mechanical properties and lignin structural characteristics. The results highlighted that the content of β-O-4 linkages correlates significantly with the tensile strength and elastic modulus of lignin carbon fibers, indicating that more linear β-O-4 linkages would promote the carbon fiber mechanical performance. Moreover, electroconductive properties are essential for broader energy device application of lignin-based carbon fibers, yet the mechanisms controlling their electroconductivity are largely unknown. Furthermore, we hereby demonstrated that a higher β-O-4 content also promotes the electroconductivity of lignin carbon fibers. Microstructure analysis further revealed that the crystallite size and content of the pre-graphitic turbostratic carbon structure in lignin-based carbon fibers were enhanced as the β-O-4 linkages increased. The content of β-O-4 linkages has shown a strong correlation with the crystallite content in a linear regression model. This study thus revealed the underlying mechanisms regarding how the lignin structure in planta defines the resultant carbon fiber properties. Moreover, the study also highlighted the correlation between the mechanical and electroconductive properties of lignin-based carbon fibers, both of which were defined by the lignin structure.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2020

Investigating the compressive strength and strain localization of nanotwinned nickel alloys

Sputter deposited nickel-molybdenum-tungsten (Ni-Mo-W) thin films possess a beneficial suite of properties that stem from the extremely fine growth twins that form during the deposition process. Previously these materi- als were only characterized in tension, however, in this study in situ micropillar compression and post-mortem microstructural analysis of nanotwinned Ni 84 Mo 11 W 5 micropillars were employed to measure the compressive response and elucidate the attendant deformation mechanisms. The pillars exhibit Hookean behavior to com- pressive strengths of 3-3.5 GPa and the onset of non-linear plastic flow was manifest by discrete strain bursts and highly localized shear bands. Plastic deformation was concentrated at the top of the pillar, while the bulk of the micropillar was nominally unaffected. Post-mortem investigations indicate that at sufficiently high stresses shear banding is triggered, resulting in intense and highly localized plastic deformation that led to the formation of twin-free nanocrystalline grains within highly deformed shear bands. By contrast, the regions adjacent to the shear bands were unaffected. The absence of detwinning and dislocation glide mechanisms was unexpected and in direct contrast to what has been observed in nanotwinned Cu-Al. Post-mortem observations of the Ni-Mo-W micropillars suggest that the ultrafine twins create a unique form of dislocation starvation and source-limited plasticity. The ultrahigh compressive strength is governed by the triggering of shear bands rather than the activa- tion of dislocation glide. Finally, the specialized nature of plasticity in nanotwinned Ni-Mo-W is clear, even though the precise trigger for shear band formation in nanotwinned Ni-Mo-W remains to be identified.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Comparative study of helium bubbles in a Ti-Ta alloy and a Ti/Ta nanocomposite

Here, we investigated the size, density, and distribution of helium (He) bubbles in a Ti-Ta single-phase alloy and a Ti/Ta dual-phase nanocomposite using transmission electron microscopy. The Ti/Ta nanocomposite was fabricated via phase separation during high-temperature annealing of the single-phase Ti-Ta alloy. He ion implantation in the Ti-Ta single-phase alloy leads to the formation of nano-scale He bubbles (~1.7 nm in size, ~2.6×10 5 /μm 3 in volumetric density). He bubbles were found to segregate to grain boundaries. Under identical implantation conditions, numerous He bubbles also formed in the Ti/Ta nanocomposite. Closer inspection revealed that He bubbles in the Ti-rich phase are smaller and of higher volumetric density (~1.2 nm, ~8.4×10 5 /μm 3 ) than those in the Tarich phase (~3 nm, ~1.8×10 5 /μm 3 ) and the single-phase alloy. He bubbles were also observed to decorate phase boundaries, but they were generally smaller than those on grain boundaries. These results suggest that Ti/Ta phase boundaries are less conducive to the growth of large He bubbles than grain boundaries in the Ti-Ta single phase alloy.

36 MATERIALS SCIENCE↗