Phase Stability and Kinetics of Topotactic Dual Ca 2+ –Na + Ion Electrochemistry in NaSICON NaV 2 (PO 4 ) 3
Recent reports of reversible calcium plating and stripping have rekindled interest in the development of Ca-ion batteries (CIBs) as next-generation energy storage devices. This technology has the potential to overcome the limitations of conventional Li-ion batteries, but CIBs are plagued by a paucity of suitable cathode materials. To date, NaSICON-structured NaV 2 (PO 4 ) 3 has been demonstrated as a successful cathode candidate, exhibiting reversible (de)intercalation of 0.6 mol Ca 2+ along with stable cycling performance. However, a complex multiphase mixture forms on discharge so the Ca-ion charge storage mechanism in the NaSICON framework is poorly understood. Here in this work, we report on an investigation of the structure and/or Na + /Ca 2+ environment(s) of a variety of chemically prepared NaSICON Ca x Na y V 2 (PO 4 ) 3 phases which were characterized using synchrotron XRD, SEM-EDS, 23 Na NMR, and TEM. Highly calciated CaV 2 (PO 4 ) 3 , Ca 1.5 V 2 (PO 4 ) 3 , and CaNaV 2 (PO 4 ) 3 phases can be prepared at high temperature, but -unlike Ca 0.6 NaV 2 (PO 4 ) 3 -these materials are electrochemically inactive. To better understand the fundamental factors impacting successful Ca 2+ electrochemistry in this system, DFT was employed to examine the Ca x Na y V 2 (PO 4 ) 3 phase diagram and Ca 2+ diffusion mechanism. Theoretical insights show that phase separation into Na-rich and Ca-rich phases is a reason for the capacity limitation and demonstrate that Na + ions in the host materials assist the migration of neighboring Ca 2+ ions, enabling reversible electrochemistry in Ca x Na y V 2 (PO 4 ) 3 . This investigation of fundamental principles affecting reversible Ca 2+ (de)intercalation in Ca x Na y V 2 (PO 4 ) 3 allows for the development of design principles to enable the discovery of a variety of successful cathodes for CIBs.