Can chemical short-range order be transformed into a practical alloy-engineering tool?
Explore the source record for details and available documents.
Pei, Zongrui (ORCID:0000000307484629)↗
Engineering topics
Xie, Qingge
Publications and source records attributed to Xie, Qingge.
Self-equilibrated backstresses induce compensation between hardening and softening: Micromechanical and microstructural features
For crystal plasticity formulation neglecting the strain gradients at the dislocation scale, backstresses are necessary to satisfy the mesoscopic stress equilibrium and strain compatibility requirements. Backstresses in a material point and those between neighboring points are treated separately. Physically backstresses can dynamically induce either hardening or softening effects to adjust the dislocation hardening of slip systems, whereas the sum of the stresses resulting in backstresses in the representative volume element (RVE) is zero. Backstress hardening suppresses certain slip activities, while backstress softening triggers excess dislocations. A two-phase brass is studied. Backstresses make the hard phase deform smaller and the soft phase deform more than those without employing backstresses in a model. In the former, more homogeneous lattice strain and higher yield stress are obtained. Backstress has limited effects on the evolution of the critical resolved shear stress and crystallographic texture. Furthermore, it is a major cause of the banded structures featuring sharp crystallographic contrasts which are not parallel to the slip planes. Tests indicate that backstress induces a serrated behavior at the early stages of deformation and induces the geometrically necessary bands (GNBs), which are parallel to the macroscopic axes.
36 MATERIALS SCIENCE↗
Crystallographic orientation and spatially resolved damage in a dispersion-hardened Al alloy
The in-situ neutron diffraction technique, in combination with both the full-field crystal elasto-viscoplastic finite element model and microstructural characterization, was used to study the deformation-induced damage anisotropy in a commercial Al alloy, subjected to uniaxial tensile and cyclic loading. The simulations capture well the crystallographic-orientation-dependent lattice strain behavior. The hard grains, e.g. those orientated with the <111> and <422> orientations parallel with the uniaxial loading direction (LD), feature large Taylor factors and seem more prone to form damage-related band structures. Their effective elastic moduli decrease with the accumulation of damage, which are different from the soft grains orientated with the <200> orientation along the LD. Correlation between the distribution of voids and that of the residual lattice strain developed after failure may exist. The maximum tensile type residual lattice strain observed after failure may be resulted from the band structure formed in the hardest <111> grains. It was revealed that the band structure triggered by the hard particles could be one of sources of damage. In addition, while the specimen was obviously damaged, a fast stress relief was evidenced after unloading from the tension, especially at the beginning of unloading. Our present investigations provide a novel method for exploring the damage mechanisms of polycrystalline materials during plastic deformation.
36 MATERIALS SCIENCE↗