Ex situ bismuth doping for efficient CdSeTe thin-film solar cells with open-circuit voltages exceeding 900 mV
We dope CdTe solar cells with Bi after the device structure is completed using a solution process.
CdTe solar cell↗
Engineering topics
Xiong, Gang
Publications and source records attributed to Xiong, Gang.
Microstructural Passivation of Patterned Al 2 O 3 Back Contacts on CdS/CdTe Solar Cells
Abstract Patterned aluminum oxide (Al 2 O 3 ) back contact on cadmium telluride (CdTe) solar cells can effectively mitigate the loss of the majority carriers while retaining the passivation benefits for minority carriers. This study investigates the impact of the point‐contact geometry on cell performance, where the spacing of the microholes is systematically varied at a constant microhole diameter (≈16 µm). Microhole arrays are created on an evaporated Al 2 O 3 layer (≈30 nm) on CdTe using laser‐beam lithography and selective wet etching processes. Comparative analysis indicates a significant decrease in fill factor (FF) and short‐circuit current ( I SC ) when the contact fraction falls below 30%, likely due to the Al 2 O 3 barrier impeding majority carriers. Above this fraction, FF and I SC are comparable to those of baseline CdTe cells without Al 2 O 3 . Open‐circuit voltage ( V OC ) shows a gradual decrease as Al 2 O 3 coverage is reduced but exhibits a slight increase (<15 mV) when the contact fraction exceeds 30%. Cathodoluminescence (CL) characterization reveals that significantly improved radiative recombination occurs within the CdTe grain bulk with Al 2 O 3 , whereas this effect on grain boundaries is minimal. The findings imply complex local carrier dynamics in the patterned back‐contact region, closely tied to the microstructural properties of CdTe‐based solar cells.
Roy, Etee Kawna↗
Status report on emerging photovoltaics
This report provides a snapshot of emerging photovoltaic (PV) technologies. It consists of concise contributions from experts in a wide range of fields including silicon, thin film, III-V, perovskite, organic, and dye-sensitized PVs. Strategies for exceeding the detailed balance limit and for light managing are presented, followed by a section detailing key applications and commercialization pathways. A section on sustainability then discusses the need for minimization of the environmental footprint in PV manufacturing and recycling. The report concludes with a perspective based on broad survey questions presented to the contributing authors regarding the needs and future evolution of PV.
14 SOLAR ENERGY↗
Photovoltaic device innovation for a solar future
Photovoltaics (PV), also known as solar cells, are now found everywhere - in utility plants; on roofs of homes and commercial buildings; on platforms at sea; in agricultural fields; on vehicles, buildings, drones, and backpacks; and, in their longest running application, providing power in space. Continuous device innovation has led to increased efficiency and improved reliability for multiple PV technologies. Confronted with an urgent need to deploy PV at multiterawatt (TW) scale over the next two decades to mitigate greenhouse gas emissions, PV device innovation takes on new urgency and impact. This perspective reviews recent progress in device design and performance for PV technologies that are currently in commercial production at greater than 1 GW/year or enabling significant space-based power generation - Si, CdTe, CIGS, and multijunction III-V - and looks ahead to the next 5 years. In conclusion, we also identify device-related topics requiring cross-cutting research and innovation.
14 SOLAR ENERGY↗
Cracked Film Lithography with CuGaO x Buffers for Bifacial CdTe Photovoltaics
Abstract Bifacial CdTe solar cells with greater power density than the monofacial baselines are demonstrated by using a CuGaO x rear interface buffer that passivates while reducing sheet resistance and contact resistance. Inserting CuGaO x between the CdTe and Au increases mean power density from 18.0 ± 0.5 to 19.8 ± 0.4 mW cm −2 for one sun front illumination. However, coupling CuGaO x with a transparent conductive oxide leads to an electrical barrier. Instead, CuGaO x is integrated with cracked film lithography (CFL)‐patterned metal grids. CFL grid wires are spaced narrowly enough (≈10 µm) to alleviate semiconductor resistance while retaining enough passivation and transmittance for a bifacial power gain: bifacial CuGaO x /CFL grids generate 19.1 ± 0.6 mW cm −2 for 1 sun front + 0.08 sun rear illumination and 20.0 ± 0.6 mW cm −2 at 1 sun front + 0.52 sun rear—the highest reported power density at field albedo conditions for a scaled polycrystalline absorber.
14 SOLAR ENERGY↗
CdTe-based thin film photovoltaics: Recent advances, current challenges and future prospects
Cadmium telluride (CdTe)-based cells have emerged as the leading commercialized thin film photovoltaic technology and has intrinsically better temperature coefficients, energy yield, and degradation rates than Si technologies. More than 30 GW peak (GWp) of CdTe-based modules are installed worldwide, multiple companies are in production, modules are shipping at up to 18.6% efficiency, and lab cell efficiency is above 22%. We review developments in the science and technology that have occurred over approximately the past decade. These achievements were enabled by manufacturing innovations and scaling module production, as well as maximizing photocurrent through window layer optimization and alloyed CdSe x Te 1-x (CST) absorbers. Improved chlorine passivation processes, film microstructure, and serendipitous Se defect passivation significantly increased minority carrier lifetime. Efficiencies >22% have been realized for both Cu and As doped CST-based cells. The path to further efficiency gains hinges primarily on increasing open circuit voltage (V oc ) and fill factor (FF) through innovations in materials, fabrication methods, and device stacks. Replacing the longstanding Cu doping with As doping is resulting in better module stability and is being translated to large-scale production. To realize 25% efficiency and >1 V V oc , research and development is needed to increase the minority carrier lifetime beyond 100 ns, reduce grain boundary and interface recombination, and tailor band diagrams at the front and back interfaces. Many of these goals have been realized separately however combining them together using scalable manufacturing approaches has been elusive to date. We review these achievements and outstanding opportunities for this remarkable photovoltaic technology.
14 SOLAR ENERGY↗
Band Bending at CdTe Solar Cell Contacts: Correlating Electro‐Optical and X‐Ray Photoelectron Spectroscopy Analyses of Thin Film Solar Cells
With the semiconductor bulk properties reaching target values for highly efficient solar cells, efforts are applied to reduce losses at solar cell interfaces and contacts. Advances in understanding back contacts in thin‐film polycrystalline CdTe solar cells, a leading thin‐film PV technology, are reported. By using X‐Ray photoelectron spectroscopy, Kelvin probe spectroscopy, time‐ and energy‐resolved photoluminescence, defects at the back contact are analyzed. Densities of recombination centers and charged defects that induce near‐back‐contact band bending, both resulting in recombination losses, were estimated. Electro‐optical and surface analysis results are integrated into a device model, simulating the performance of CdSeTe/CdTe solar cells with 902 mV open circuit voltage.
14 SOLAR ENERGY↗
Understanding What Limits the Voltage of Polycrystalline CdSeTe Solar Cells
The origin of voltage deficits in polycrystalline cadmium selenide telluride (CdSeTe) solar cells is unclear. Here, we present a comprehensive voltage loss analysis performed on state-of-the-art CdSeTe devices - fabricated at Colorado State University and First Solar - using photoluminescence techniques, including external radiative efficiency (ERE) measurements. More specifically, we report the thermodynamic voltage limit Voc,ideal, internal voltage iVoc and external voltage Voc of partially and fully finished cells fabricated with different dopant species, dopant concentrations and back contacts. Arsenic-doped aluminium-oxide-passivated cells made at Colorado State University present remarkably high ERE (>1%) - translating into iVoc above 970 mV - but suffer from poor back-contact selectivity. On the other hand, arsenic-doped devices from First Solar present almost perfect carrier selectivity (Voc=iVoc), leading to Voc above 840 mV, and are limited by recombination in various parts of the device. Thus, development of contact structures that are both passivating and selective in combination with highly luminescent absorbers is key to reducing voltage losses.
CdSeTe devices↗
Impact of dopant-induced optoelectronic tails on open-circuit voltage in arsenic-doped Cd(Se)Te solar cells
Fluctuations refer to inhomogeneity in the distribution of donors and acceptors at the nanometer scale and occur in many compound solar cell materials such as Cu(In,Ga)Se 2 , Cu 2 ZnSn(S,Se) 4 , and CdSe x Te 1-x . In this work, numerical simulations show that these fluctuations produce not only electrostatic potential variation, but also, local changes in the carrier density and effective bandgap. For a CdSe x Te 1-x absorber doped with arsenic, simulations and cathodoluminescence data within single grains demonstrate how donor and acceptor densities—consistent with capacitance-voltage and secondary-ion mass-spectrometry data—produce tails in photoluminescence, quantum efficiency, and absorption measurements. Using multiple theoretical approaches, we demonstrate that the fluctuations can hinder expected performance gains from increased carrier density, and we describe the significant open-circuit voltage deficit observed in the CdSe x Te 1-x :As solar technology. Our results demonstrate that it is critical to characterize and reduce carrier compensation to realize a higher efficiency.
14 SOLAR ENERGY↗
The 2020 photovoltaic technologies roadmap
Over the past decade, the global cumulative installed photovoltaic (PV) capacity has grown exponentially, reaching 591 GW in 2019. Rapid progress was driven in large part by improvements in solar cell and module efficiencies, reduction in manufacturing costs and the realization of levelized costs of electricity that are now generally less than other energy sources and approaching similar costs with storage included. Given this success, it is a particularly fitting time to assess the state of the photovoltaics field and the technology milestones that must be achieved to maximize future impact and forward momentum. This roadmap outlines the critical areas of development in all of the major PV conversion technologies, advances needed to enable terawatt-scale PV installation, and cross-cutting topics on reliability, characterization, and applications. Each perspective provides a status update, summarizes the limiting immediate and long-term technical challenges and highlights breakthroughs that are needed to address them. In total, this roadmap is intended to guide researchers, funding agencies and industry in identifying the areas of development that will have the most impact on PV technology in the upcoming years.
14 SOLAR ENERGY↗