Solid-state reaction mediated microstructural evolution in a spark plasma sintered in situ Ti–B 4 C composite
For this study, a novel porosity-free in situ Ti–B 4 C composite was fabricated via spark plasma sintering (SPS). Detailed analysis of the phase evolution, coupling results from XRM, XRD and SEM-EBSD-EDS, indicate that primarily TiB 2 precipitates formed due to the in-situ reactions between the boron-carbide and titanium powders. The precipitation of TiB 2 resulted in the formation of a graphitic C-rich thin layer circumscribing the partially reacted B 4 C particles. Further progression of the in-situ reaction leads to the out-diffusion of the excess carbon from the B 4 C particles, across the graphite and TiB 2 phases, forming TiC upon reacting with the titanium matrix. Therefore, the final microstructure primarily consisted of TiB 2 , TiC, and partially reacted B 4 C phases, with small amounts of TiB, α-Ti, and graphite. Furthermore, the microstructure in these SPS processed in situ composites appeared to be the product of a solid-state Ti–B 4 C diffusion couple, substantially different from their fusion-based additively manufactured counterparts. Nano-indentation tests revealed a remarkably high average hardness of ~25 GPa for this SPS-processed Ti–B 4 C composite and comparable (with literature) phase-specific hardness and modulus values for the constituent TiB 2 , TiC, and B 4 C phases.