Tunable structural and magnetic properties of NiAs-type Mn x Sb (1.00≤x≤1.30) compounds
Mn-based alloys can exhibit a variety of magnetic properties related to their tunable exchange interactions. Here, structural and magnetic properties of hexagonal NiAs-type Mn x Sb (1.00≤x≤1.30) compounds are studied with a combination of X-ray diffraction, neutron diffraction, and magnetic measurements. It is found that the magnetization, Curie temperature, and magnetocrystalline anisotropy of Mn x Sb compounds can be tuned by controlling Mn concentration and doping at interstitial (2d) sites. With increasing Mn concentration, magnetic moments of Mn atoms decrease and deviate gradually from the ab-plane to the c-axis for 1.20≤x≤1.22 at room temperature, which leads to a decrease of the Curie temperature T c and the spin reorientation temperature T SR . By doping with nonmagnetic elements, a substantial room-temperature magnetocaloric effect without magnetic hysteresis was achieved for Mn 1.12 Zr 0.1 Sb compound, which is highly beneficial to the practical magnetic refrigeration application.