Solid-to-Solid Diffusion Bond Between SA508 Low Alloy Steel to 316L Stainless Steel by Hot Isostatic Pressing
Not provided.
Materials Science↗
Engineering topics
Yang, Jingfan
Publications and source records attributed to Yang, Jingfan.
Dislocation channel broadening–A new mechanism to improve irradiation-assisted stress corrosion cracking resistance of additively manufactured 316 L stainless steel
Additively manufactured (AM) 316 L stainless steel (SS) after hot isostatic pressing (HIP) was found to exhibit superior resistance to irradiation-assisted stress corrosion cracking (IASCC) in high-temperature water, as compared to wrought 316 L SS. The well-accepted IASCC factors of radiation-induced segregation (RIS) and radiation hardening are not accurate descriptions of IASCC susceptibility in this case. A decreased strain localization along grain boundaries, caused by dislocation channel broadening, was confirmed to suppress crack initiation. A unique distribution of irradiation-induced defects in HIP AM 316 L SS eased dislocation cross-slip compared to those in the wrought counterpart, thus increasing the channel width near the grain boundaries. Here for the first time, this study highlights the importance of dislocation channel broadening as a potential mechanism to further improve the IASCC resistance of 316 L SS and provides direct experimental evidence based on commercial-grade materials.
316L stainless steel↗
Pulsed Laser Additive Manufacturing for 316L Stainless Steel: A New Approach to Control Subgrain Cellular Structure
Not provided.
Materials Science↗
The effect of secondary phases on microstructure and irradiation damage in an as-built additively manufactured 316 L stainless steel with a hafnium compositional gradient
Additive manufacturing (AM) or rapid prototyping has become a crucial tool for reducing both cost and time while increasing efficiency in qualifying structural materials for reactor use. In this study, directed energy deposition (DED) was used to develop an as-built 316 L stainless steel sample with three regions of increasing Hf-dopant to study the effects of Hf on the irradiation response of the material. Morphological and microstructural changes were analyzed before and after 2 MeV proton irradiation at 360 °C to a damage of 2.5 dpa at ~ 10 µm below the surface. The addition of Hf effectively suppressed radiation-induced damage (dislocation loops, radiation-induced segregation) due to enhanced point defect recombination. The radiation damage seen in the as-built sample was further compared to a thermo-mechanically treated counterpart of the same fabrication and irradiation parameters which was found to behave superiorly. In conclusion, the increased radiation resistance of this material may be attributed to the as-built microstructure, which includes undissolved Hf particles, delta ferrite grains and cellular sub-grain boundaries that can hinder defect motion.
316L Stainless Steel↗
SA508 low alloy steel to 316L stainless steel dissimilar metal joint made by powder metallurgy hot isostatic pressing
Joining ferritic SA508 low alloy steel (LAS) and austenitic 316 L stainless steel (SS) via powder metallurgy hot isostatic pressing (PM-HIP) was evaluated as an alternative method to welding. This study investigated the mechanical and microstructural evolutions of the bimetallic interface under different joint designs and heat treatments. Here, the direct joining of dissimilar metal alloys by PM-HIP method resulted in two designs: 1) powder SA508 to solid bar 316 L (P508–B316L) and 2) powder 316 L solid bar SA508 (P316L-B508). In both cases, P508–B316L and P316L-demonstrated satisfactory tensile strength, however, high hardness and severe depreciation in toughness were located on the bimetallic interface. The mechanisms responsible for the detrimental mechanical properties were verified. Large oxides were observed in P508–B316L due to the prior powder boundary (PPB) oxides present in SA508 powder. The intense sensitization occurred from the formation of M 23 C 6 carbides, consequently from the slow cooling after PM-HIP in P316L-B508. Post-HIP heat treatments were explored to reduce the distance of carbide formation; however, the heat treatment could not eliminate the carbides. The experimental results were compared to the diffusion couple simulation as a function of carbide formation with distance. The analysis also showed the high hardness at the bimetallic interface was primarily contributed by solid solution strengthening. In conclusion, the direct joining of P316L-B508 and P508–B316L via PM-HIP was deemed to be unfeasible, and a transitional material is necessary to impede the diffusion of carbon.
316L stainless Steel↗
Carbon nanotube (CNT) reinforced 316L stainless steel composites made by laser powder bed fusion: Microstructure and wear response
Carbon nanotube (CNT) reinforced 316L stainless steel (SS) composites were fabricated by laser powder bed fusion (LPBF) additive manufacturing (AM). This study focuses on microstructure evolution, hardness, and wear behavior. The wear behavior for AM 316L SS and 1 wt% CNT/316L SS was studied by a dry sliding test under normal loads of 10, 15, and 25 N. The addition of CNT to 316L SS led to the change of solidification mode from cellular/columnar to dendritic growth, producing grain refinement. Nanoscale dendrites were observed. Although TEM characterization confirmed the existence of CNT in cell interior, most CNT were damaged, resulting in carbon material segregation along cellular/dendritic boundaries. The wear rate was found dramatically decreased due to the improved hardness. Compared to the adhesive and abrasive wear in AM 316L SS, the wear mechanism of CNT/316L composite was adhesion and oxidative wear. Furthermore, enhanced cellular/dendritic boundary strengthening by carbon segregation was the main strengthening mechanism of CNT/316L composite.
36 MATERIALS SCIENCE↗
On the thermal coarsening and transformation of nanoscale oxide inclusions in 316L stainless steel manufactured by laser powder bed fusion and its influence on impact toughness
The thermal evolution of nanoscale oxide inclusions in 316L stainless steel (SS) manufactured by laser powder bed fusion additive manufacturing (AM) was explored. The size, chemical composition, morphology, and distribution of the oxides were characterized as the function of heat treatment conditions. The study revealed the mechanistic driving force of the rapid oxide coarsening during recrystallization. Ostwald ripening governs oxide coarsening. The active grain boundary-oxide interaction at the early stage of recrystallization accelerated oxide coarsening via enhanced solute diffusion along grain boundaries. Pipe diffusion along dislocation cellular boundaries has a negligible contribution to oxide coarsening. At high temperatures (T> 1065 °C), although lattice diffusion primarily controlled the oxide growth, the contribution from the grain-boundary diffusion was necessary. The transformation from MnSiO 3 to CrMn 2 O 4 took place in the un-recrystallized grains but was not observed when recrystallization started. The interaction of grain boundary and oxides during recrystallization resulted in a high fraction of oxides accumulated at grain boundaries. While oxide coarsening does not significantly alter the toughness value, grain-boundary oxides promote microvoid formation and intergranular fracture under Charpy impact in the recrystallized AM 316L SS.
36 MATERIALS SCIENCE↗