Engineering topics

Yang, K. H.

Publications and source records attributed to Yang, K. H..

4 records

NASA NTRS1989

Dynamic crack arrest in ceramics and ceramic composites

The results of past dynamic crack arrest experiments involving structural ceramics and ceramic composites are reviewed and analyzed. The lack of dynamic crack arrest in very brittle materials is discussed and contrasted with dynamic crack arrest in somewhat brittle metallic and polymeric materials. Numerical analyses show that the lack of crack arrest is due to reduced dynamic fracture resistance of the material and is not due to the kinetic energy.

Kobayashi, A. S.↗

NASA NTRS1989

Effects of loading rate and temperature on dynamic fracture of ceramic matrix composites

A hybrid experimental-numerical procedure was used to determine the dynamic fracture initiation toughnesses and the dynamic stress intensity factors of alumina, TiB2-particulate/SiC-matrix, and SiC(w)/Al2O3-matrix composites at room and elevated temperatures under static and impact loadings. The dynamic fracture initiation toughnesses at room and elevated temperatures were greater than the corresponding static fracture toughness. The crack velocity versus the dynamic stress intensity factor relations showed minor differences due to temperature changes but significant differences due to the change in loading rates.

Yang, K. H.↗

NASA NTRS1989

A hybrid procedure for dynamic characterization of ceramics at elevated temperature

A hybrid experimental-numerical procedure to characterize the dynamic fracture response of ceramics and ceramic composites at temperatures in excess of 1400 C is described. This hybrid methodology was developed to characterize dynamic fracture responses and to study the effect of temperature on dynamic fracture responses of ceramics and ceramic matrix composites. The hybrid methodology was used to determine the dynamic stress intensity factors (SIF) associated with a running crack in a three-point bend specimen at elevated temperature. This procedure was utilized to determine the dynamic SIF versus crack velocity relations of alumina, TiB2-particulate/SiC-matrix composite, and SiC-whisker/Al2O3-matrix composite. Minor differences in the dynamic SIF versus crack velocity relations at room and elevated temperature were seen, and significant differences under impact and static loadings were observed in the dynamic SIF versus crack velocity relations.

Yang, K. H.↗

NASA NTRS1988

Dynamic fracture toughness of ceramic composites

The dynamic fracture toughness vs crack velocity relationships of TiB2 particulate-reinforced SiC-matrix and SiC whisker-reinforced Al2O3-matrix composites were determined at both room temperature and 1200 C with impacted, single-edge notched three-point bend specimens. Rapid crack initiation and propagation were monitored by a laser interferometric-displacement gage system. A FEM model that transmitted the measured outside-impact load to the specimen within the furnace was used to characterize the entire loading system-specimen unit. Small differences were measured between the room temperature and 1200 C dynamic responses.

Yang, K. H.↗