DOE OSTI2022

Enabling Conversion-Type Iron Fluoride Cathode by Halide-Based Solid Electrolyte

The practical application of low-cost and energy-dense iron fluoride cathodes has been hindered by the first cycle electrochemical irreversibility, cycling instability, and large voltage hysteresis. Here, we report that these challenges may be overcome by the utilization of halide-based solid electrolytes (SEs). The excellent electrochemical stability of halide-based SEs enables a complete conversion and deconversion of FeF 2 which cannot be achieved with sulfide-based SEs. Due to restricted and reversible decomposition of SE, prevention of Fe dissolution, mechanical confinement of active material, as well as improved electrode kinetics, solid-state FeF 2 cathode with halide-based SE demonstrated superior electrochemical performance compared with FeF 2 electrodes in liquid electrolytes, with a high 1st cycle coulombic efficiency (~100 %), high specific capacity (~600 mAh/g), long cycle life (>100 cycles) and high-rate performance (up to 2C). In conclusion, our results suggest solidifying the batteries may be a viable approach to addressing the long-standing key challenges of iron fluoride cathodes.

25 ENERGY STORAGE↗

DOE OSTI2022

Enhancing Li + Transport in NMC811||Graphite Lithium–Ion Batteries at Low Temperatures by Using Low–Polarity–Solvent Electrolytes

LiNi x Co y MnzO 2 (x+y+z=1)||graphite lithium-ion battery (LIB) chemistry promises practical applications. However, its low-temperature (≤ –20°C) performance is poor because the increased resistance encountered by Li + transport in and across the bulk electrolytes and the electrolyte/electrode interphases induces capacity loss and battery failures. Though tremendous efforts have been made, there is still no effective way to reduce the charge transfer resistance (R ct ) which dominates low-temperature LIBs performance. In this work, we propose a strategy of using low-polarity-solvent electrolytes which have weak interactions between the solvents and the Li + to reduce R ct , achieving facile Li + transport at sub-zero temperatures. The exemplary electrolyte enables LiNi 0.8 Mn 0.1 Co 0.1 O 2 ||graphite cells to deliver a capacity of ≈113 mAh g –1 (98% full-cell capacity) at 25°C and to remain 82% of their room-temperature capacity at –20°C without lithium plating at 1/3C. They also retain 84% of their capacity at –30°C and 78% of their capacity at –40°C and show stable cycling at 50°C.

25 ENERGY STORAGE↗