Engineering topics
Yang, Yutong
Publications and source records attributed to Yang, Yutong.
Bicontinuous substrates with reduced pore restriction for CO 2 -selective composite membranes
A substrate with bicontinuous structure is attractive for thin-film composite (TFC) membrane synthesis due to its high surface porosity and well-interconnected bulk morphology. In this study, the vapor-induced phase separation (VIPS) of the casting solution comprising water, 2-pyrrolidone, and polyethersulfone (PES) was studied. By tuning the water addition in the casting solution and water vapor exposure time, the optimized substrate exhibited a bicontinuous surface with a high porosity of 24.2% (or 216/µm 2 pore density), thereby mitigating pore restriction and showing a high CO 2 permeance of 2.94×10 5 GPU. Compared to the benchmark PES substrate with cellular surface pores and lower gas permeance, the use of the bicontinuous substrate led to a 12% increase in the CO 2 permeance of the TFC membrane. The mitigated pore restriction was further rationalized by a resistance-in-series model. The analysis of the lateral diffusion and substrate resistances indicates that an even higher surface pore density of the substrate is required to fully realize the potential of ultra-permeable, CO 2 -selective polymers in the TFC configuration. As a result, the scalability of the VIPS process was demonstrated by the roll-to-roll fabrication of the optimized bicontinuous substrate with a width of 21" and a length of >100'.
Matrimid substrates with bicontinuous surface and macrovoids in the bulk: A nearly ideal substrate for composite membranes in CO 2 capture
Scalable fabrication of thin-film composite (TFC) membrane for post-combustion carbon capture is often limited by the availability of high-performance nanoporous substrate. Ideally, the substrate should allow for fast gas transport at the selective layer/substrate interface as well as in the bulk of the substrate. In this study, highly permeable Matrimid substrates were prepared via vapor- and nonsolvent-induced phase separations. The phase separation mechanism of the Matrimid®/N-methyl-2-pyrrolidone casting solution was modulated by the addition of LiCl to control the solution thermodynamic stability, and nanoporous Matrimid substrates were formed with a bicontinuous surface and macrovoids in the bulk. This hierarchically optimized structure resulted in a CO 2 permeance of 2.60 × 10 5 GPU (1 GPU = 1 × 10 –6 cm 3 (STP) cm –2 s –1 cmHg –1 = 3.349 × 10 –10 mol m –2 s –1 Pa –1 ), which was ca. 11 times more permeable than a benchmark polyethersulfone substrate with cellular pores. The benefit of using this new substrate was demonstrated by coating a 170-nm amine-containing polymer to form a TFC facilitated transport membrane. The membrane exhibited a CO 2 permeance of 932 GPU at 57°C, which was 72 GPU higher than the counterpart coated on the benchmark substrate. Meanwhile, the CO 2 /N 2 selectivity was remained at 158. This permeance improvement could be well explained by the resistance-in-series model, where the improved permeance was attributed to the reductions in substrate and lateral diffusion mass transfer resistances. The upper bound (UB) analysis indicates that the Matrimid substrate is nearly ideal for the state-of-the-art polymers for CO 2 /N 2 separation. Here, the substrate improvement could also reduce the parasitic energy associated with the membrane process due to the reduced membrane cost and flue gas compression requirement.
Recent Progress in the Engineering of Polymeric Membranes for CO2 Capture from Flue Gas
CO2 capture from coal- or natural gas-derived flue gas has been widely considered as the next opportunity for the large-scale deployment of gas separation membranes. Despite the tremendous progress made in the synthesis of polymeric membranes with high CO2/N2 separation performance, only a few membrane technologies were advanced to the bench-scale study or above from a highly idealized laboratory setting. Therefore, the recent progress in polymeric membranes is reviewed in the perspectives of capture system energetics, process synthesis, membrane scale-up, modular fabrication, and field tests. These engineering considerations can provide a holistic approach to better guide membrane research and accelerate the commercialization of gas separation membranes for post-combustion carbon capture.