A product includes a solid state electrolyte particle coated with a coating consisting essentially of metal oxide. A method includes depositing a coating on a solid state electrolyte particle by atomic layer deposition. A method includes fabricating a product using a plurality of solid state electrolyte particles coated with a coating consisting essentially of metal oxide.
Fast charging and stable lithium-ion batteries (LIBs) require prompt Li ion transport between electrodes. 3D porous separators can potentially improve ion transport at both the microscale and macroscale levels. Additive manufacturing (AM) is an ideal tool to produce and study 3D porous separators of LIBs, although little work has been reported in this area. Here, we demonstrate porous structural control in layer-by-layer printed hexanediol diacrylate (HDDA) separators using a projection micro stereolithography (PμSL) AM technology and present their corresponding battery performance in lithium nickel manganese cobalt oxide (NMC)/graphite full cells. The composition of photocurable resin determines the porous morphology (e.g., bicontinuous and droplet-like), while the settings of printing layer thickness and number of exposures can be used to adjust the porosity (e.g., from 27% to 63%). Optimal resin and print conditions are determined, and the resulting separator exhibits superior Li ion conductivity and therefore higher rate performance and longer cycling life. Compared with a Celgard 2325 separator, the optimized porous HDDA separator increases the 10C-rate capacity by 34% and decreases the capacity degradation rate at the 1C-rate by 4.9%. In conclusion, this work paves the way for future AM of 3D separators for high-energy, high-power, and long-cycling-life LIBs.
Ti5553 (Ti-5Al-5Mo-5V-3Cr wt%) is a titanium alloy widely used for its high strength-to-weight ratio and good formability at elevated temperatures. Unlike Ti-6Al-4V, Ti5553 does not undergo martensitic transformation, preventing cracking of brittle martensite upon rapid cooling. This makes it a strong candidate for additive manufacturing (AM), particularly laser powder bed fusion (L-PBF). L-PBF offers the unique opportunity to make fine lattice structures to reduce component weight. Despite the growing field of AM, there have been limited studies on L-PBF Ti5553 lattices and how their properties differ from the bulk. Here the present work addresses this knowledge gap by investigating microstructures and properties of L-PBF bulk and lattice parts and the effect of post L-PBF heat treatments. Electron microscopy and mechanical testing show that the high dislocation density formed during L-PBF increases bulk part’s yield strength by approximately 100 MPa compared to the conventional alloy. Digital image correlation during compression testing of octet truss lattices reveals a layer-by-layer failure mode. Compared to the bulk, the lattice contains copious ω nanoprecipitation, weaker <001> texture, smaller average grain sizes, and larger content of high-angle grain boundaries. These features elicit differences in Taylor factor distributions for the lattice depending on load direction, underlining challenges in predicting lattice mechanical response based on bulk properties. By examining the processing-structure-property relationships in the bulk and lattice, the present results delineate their microstructural and mechanical differences and establish a benchmark for the future design applications of L-PBF Ti5553.
The project has two primary objectives: (1) down select three-dimensional (3D) printing and post-processing approaches for solid-state electrolyte (SSE) / cathode integration, and (2) understand battery failure mechanisms via ex situ and in situ characterization.
According to one aspect of an inventive concept, an ink includes a base catalyst, a sol gel precursor composition, and a block copolymer. According to another aspect of an inventive concept, an aerogel includes a three-dimensional printed structure having printed ligaments geometrically arranged, where an average diameter of the printed ligaments is in a range of greater than 0 microns and less than 50 microns. In addition, an average distance between a center of a first of the printed ligaments and a center of a second of the printed ligaments is at least equal to the average diameter of the printed ligaments, where the first and the second of the printed ligaments are adjacent. Each printed ligament includes of a plurality of random pores, where an average diameter of the random pores is less than 50 nanometers.
The present disclosure relates to a system for laser processing of a ceramic electrolyte material. The system may include a controller, a laser responsive to the controller for generating a beam, and a beam forming subsystem. The beam forming subsystem controls a parameter of the beam generated by the laser. The beam forming subsystem further controls the beam to provide a laser fluence sufficient to produce densification of the ceramic electrolyte material.
All-solid-state lithium metal batteries (ASSLBs) have attracted attention due to their potential for mitigating safety issues and addressing energy density limitations of conventional lithium-ion batteries (LIBs). While solid state electrolytes (SSEs) with room-temperature ionic conductivities greater than that of their liquid electrolyte counterparts have been discovered, integration of the different solid components of ASSLBs is not trivial. Taking garnet Li 7 La 3 Zr 2 O 12 (LLZO) electrolyte as an example, problems for this SSE include brittleness, high temperature processing for densification, poor contact with electrodes, and lack of scalable manufacturing methods. These obstacles must be overcome before LLZO becomes commercially viable for ASSLB applications.
The project has two primary objectives: (1) down select three-dimensional (3D) printing and post processing approaches for solid-state electrolyte (SSE) / cathode integration, and (2) understand battery failure mechanisms via ex situ and in situ characterization.
The project has two primary objectives: (1) down select three-dimensional (3D) printing and post-processing approaches for solid-state electrolyte (SSE) / cathode integration, and (2) understand battery failure mechanisms via ex situ and in situ characterization.
The goal of this internship was to develop a solid polymer electrolyte with a suitable ionic conductivity and mechanical properties and integrate it with 3D printed cathode for solid state lithium batteries. While liquid electrolytes will have much higher conductivities and therefore higher power densities than solid electrolytes, batteries with such electrolytes suffer from extreme dendritic growth, short-circuiting, and general failure. Typically, batteries prevent this by including a solid yet porous separator somewhere between the anode and cathode to suppress dendritic growth. Solid polymer electrolyte acts as the conductive medium between electrodes as well as the separator that prevents failure from short-circuiting. The specific system explored is a vinyl ethylene carbonate (VEC) and polyethylene glycol diacrylate (PEGDA) mixed polymer solution using both 2,2’-azobis(2-methylpropionitrile) (AIBN) and Irgacure 819, respectively as thermal and photo- initiators. Electrochemical and rheological techniques were used to determine the optimal polymer solution and curing conditions. Through this research, multiple new pathways of exploration have been determined to create a usable solid polymer electrolyte through a combination of varying cure intensities and initiator concentrations.
All solid-state lithium-ion batteries (ASSLIBs) have gained significant interest in recent years due to their wide range of applications, including mobile devices, electric vehicles, and grid storage. Garnet-type Li 7 La 3 Zr 2 O 12 (LLZO) solid-state electrolyte (SSE) continues to be a significant player in the fabrication of ASSLIBs with excellent ionic conductivity on the order of 10 -3 S•cm -1 with the integration of dopants and sintering aids to assist conductivity and structural evolution during the sintering procedure. Traditional sintering techniques, such as solid-state sintering (SSS), have been proven to yield desirable crystal structures. However, the low ionic conductivity results from inferior microstructure, and lithium loss is a significant challenge. Recently, a relatively novel sintering process called rapid laser sintering (RLS) has shown great potential for achieving fully dense solid oxide electrolytes with less lithium loss, resulting in high ionic conductivity [1] [2] [3] [4]. Here, we applied a modified RLS method using precursor powders instead of pre-synthesized LLZO powders to fabricate Al-doped LLZO (Li 6.1 La 3 Zr 2 Al 0.3 O 12 + 13 wt% Li 2 CO 3 ) and Ta-doped LLZO (Li 6.4 La 3 Zr 1.4 Ta 0.6 O 12 + 5 wt% LiOH•H 2 O) dense electrolytes. This rapid laser reactive sintering (RLRS) could potentially reduce the number of processing steps and therefore lower the manufacturing cost. We hope the rapid high-temperature sintering can densify the electrolyte and avoid the lithium loss for achieving high lithium-ion conductivity. In this work, we optimized a combination of laser parameters (speed and power), initial precursor composition, and controlled atmospheres to discover the optimal conditions for reaching the efficacious crystal structure, microstructure, and ionic conductivity.
Performance improvements in UV-cured solid state lithium batteries
Abstract not provided.
The project has two primary objectives: (1) down select three-dimensional (3D) printing and post-processing approaches for solid-state electrolyte (SSE) / cathode integration, and (2) understand battery failure mechanisms via ex situ and in situ characterization.
Large-scale production of vertically aligned single-walled carbon nanotubes (VA-SWCNTs) on metal foils promises to enable technological advancements in many fields, from functional composites to energy storage to thermal interfaces. In this work, we demonstrate growth of high-quality (G/D > 6, average diameters ~ 2–3 nm, densities > 10 12 cm –2 ) VA-SWCNTs on Inconel metal for use as a lithium-ion battery (LIB) anode. Scale-up of SWCNT growth on Inconel 625 to 100 cm 2 exhibits nearly invariant CNT structural properties, even when synthesis is performed near atmospheric pressure, and this robustness is attributed to a growth kinetic regime dominated by the carbon precursor diffusion in the bulk gas mixture. SWCNT forests produced on large-area metal substrates at close to atmospheric pressure possess a combination of structural features that are among the best demonstrated so far in the literature for growth on metal foils. Leveraging these achievements for energy applications, we demonstrate a VA-SWCNT LIB anode with capacity >1200 mAh/g at 1.0C and stable cycling beyond 300 cycles. Furthermore, this robust synthesis of high-quality VA-SWCNTs on metal foils presents a promising route toward mass production of high-performance CNT devices for a broad range of applications.
We report catalyst surface area and wetting behavior are key factors in determining the performance of gas diffusion electrode (GDE) electrolyzers for electrochemical CO 2 reduction. In this work, we report the integration of sub-1 μm thick nanoporous gold (npAu) catalyst coatings into a large-area (25 cm 2 ) zero-gap electrolyzer. The npAu coatings were prepared by magnetron sputtering (MS) of thin AgAu alloy films on the microporous carbon layer of a gas diffusion layer (GDL) followed by Ag leaching. Compared to MS Au films of the same thickness, npAu catalyst coatings enable higher Faradaic efficiencies and improved catalyst stability for CO 2 -to-CO reduction with Faradaic efficiencies of up to 88% at 100 mA/cm 2 . For a 800 nm npAu coating, the device level energy efficiency for CO 2 to CO conversion reaches 45% (52% for CO + H 2 ) at 100 mA/cm 2 with a single pass CO 2 conversion efficiency of ~12%. Contact angle measurements reveal that npAu coatings provide a more hydrophobic electrode interface compared to MS Au coatings, suggesting that the more hydrophobic interfacial environment of npAu coatings helps mitigating electrode flooding which is associated with performance deterioration over time.
We report the processing of garnet-type solid-state electrolytes remains challenging as densification conventionally requires high sintering temperatures and long processing times, which can result in severe Li loss, the formation of secondary phases, and thus high porosity and low ionic conductivity. Here, we report an ultrafast sintering method based on CO 2 laser scanning with the assistance of a heating stage. We demonstrate the rapid densification of low-packing-density Li 6.4 La 3 Zr 1.4 Ta 0.6 O 12 (LLZTO) films, which are difficult to densify by conventional furnace sintering methods. This unique approach has three fingerprint characteristics: (1) mitigation of Li loss through ultrafast sintering (dwelling time $\ll$1 s); (2) a unique anisotropic shrinkage behavior that greatly reduces film thickness; (3) wave-like surface topology from point scanning strategy that enables 3D interfacial contacts with electrode materials. Herein, highly dense (95.68%) and highly conductive (0.26 mS·cm –1 at 25 °C) LLZTO films are obtained through CO2 laser sintering. This work provides a unique, scalable, and widely applicable ultrarapid laser sintering technique to overcome the difficulties associated with classic methods for the integration of SSEs for practical all-solid-state Li-metal battery applications.
Here we review the progress of additive manufacturing effort on refractory metal tungsten and tungsten alloys. These materials are excellent candidates for a variety of high temperature applications but extremely challenging to fabricate via additive manufacturing due to a series of existing issues during the manufacturing. We outline these issues and discuss the current understanding and progress to tackle them. Laser powder-bed-fusion, laser directed-energy-deposition, and electron beam powder-bed-fusion are three common techniques that have been applied to additively manufacture pure tungsten. This overview discusses current observations and understanding on the issues associated with each of these techniques. We identify future research opportunities in additive manufacturing of refractory metals.