Microstructure of hot-pressed Al2O3-Si3N4 mixtures as a function of holding temperature

Powder mixtures of 40 m/o Si3N4-60 m/o Al2O3 were hot-pressed at 4000 psi at various holding temperatures from 1100 C to 1700 C. Scanning Electron Microscopy and Transmission Electro Microscopy results were correlated to X-ray phase analysis and density measurements. The progressively developed microstructure was used to interpret the densification behavior of SiAlON. Photomicrographs of microstructures are shown.

Yeh, H. C.↗

NASA NTRS1975

Silicon nitride-aluminum oxide solid solution (SiAION) formation and densification by pressure sintering

Stirred-ball-mill-blended Si3N4 and Al2O3 powders were pressure sintered in order to investigate the mechanism of solid solution formation and densification in the Si3N4-Al2O3 system. Powder blends with Si3N4:Al2O3 mole ratios of 4:1, 3:2, and 2:3 were pressure sintered at 27.6-MN/sq m pressure at temperatures to 17000 C (3090 F). The compaction behavior of the powder blends during pressure sintering was determined by observing the density of the powder compact as a function of temperature and time starting from room temperature. This information, combined with the results of X-ray diffraction and metallographic analyses regarding solutioning and phase transformation phenomena in the Si3N4-Al2O3 system, was used to describe the densification behavior.

Yeh, H. C.↗