On the length scale and rate-dependent mechanical behavior of monolithic (oxy)sulfidic glassy solid-state electrolytes

In the controlled atmosphere of a dedicated glove box, nanoindentation performed with a diamond Berkovich indenter tip has been used to examine the mechanical behavior of three (oxy)sulfide solid-state electrolytes (SSEs), 70Li 2 S·(30–x)P 2 S 5 ·xP 2 O 5 (x = 0, 2, and 5). At a drive frequency of 120 Hz, the elastic modulus is found to be predominantly depth independent over the range of 100 nm to 1 μm and generally insensitive to the varying mol fraction of oxygen (0, 2, and 5%) as well as the imposed strain rates of 0.025, 0.05, and 0.1 1/s. All three SSEs exhibit significant room-temperature creep. Strain burst activity observed during loading (potentially representative of pore collapse or cracking) is attenuated with the addition of oxygen. The hardness is found to be insensitive to the imposed strain rates but varying with depth and oxygen content. Furthermore, the highest oxygen concentration yields the lowest hardness and strongest depth dependence.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Sulfide glass solid-state electrolyte separators for Li metal batteries: using an interlayer to increase rate performance and reduce stack pressure

We report on the solubility of (Li 2 S) 60 (SiS 2 ) x (P 2 S 5 ) 40–x , (0 ≤ x ≤ 40) sulfide glass solid-state electrolytes in the 1:1 (v/v) DME:DOL solvent mixture, a popular choice for lithium metal battery liquid electrolytes. SiS 2 -rich glasses within the compositional range of (Li 2 S) 60 (SiS 2 ) x (P 2 S 5 ) 40–x (28 ≤ x ≤ 40) were found to be functionally insoluble in DME:DOL. Hybrid symmetric test cells with a thin liquid electrolyte layer (0.6 M LiTFSI + 0.4 M LiNO 3 in 1:1 (v/v) DME:DOL) at the interface between lithium metal electrodes and an insoluble (Li 2 S) 60 (SiS 2 ) 28 (P 2 S 5 ) 12 glass wafer were tested. Hybrid test cells delivered a critical current density of 3.0 mA cm –2 at 25 °C and 0.1 MPa, which is nearly double the CCD of comparable dry symmetric test cells cycled at 10× higher stack pressure.

25 ENERGY STORAGE↗

DOE OSTI2022

Moisture Stability of Sulfide Solid-State Electrolytes

In this report we detail a comprehensive study on the moisture stability of sulfide solid-state electrolytes in dry room environments. Although sulfide SSEs have many favorable attributes, this class of materials suffers from poor stability with water. Sulfide SSEs react with water to form gaseous H 2 S and a variety of solid byproducts like Li 3 PO 4 and LiOH, which go on to increase the interfacial impedance of solid-state batteries. Lab-scale research typically utilizes gloveboxes with <1 ppm water, however, the large-scale manufacturing of Li-ion batteries occurs in –40°C dewpoint dry rooms with around 126 ppm water. Consequently, the moisture stability of sulfide SSEs must be addressed if the manufacture of solid-state batteries based on sulfide SSEs is to be scaled up. Here, we are the first to characterize the moisture stability of sulfide SSEs according to both H 2 S and the degradation of ionic conductivity at different moisture setpoints ranging from –76°C to –40°C dewpoint. A variety of different SSE compositions are studied; namely, (Li 2 S) 75 (P 2 S 5 ) 25 , (Li 2 S) 70 (P 2 S 5 ) 30 , (Li 2 O) 7 (Li 2 S) 68 (P 2 S 5 ) 25 , (Li 2 O) 7 (Li 2 S) 63 (P 2 S 5 ) 30 , and (Li 2 S) 75 (P 2 S 5 ) 25 + 20 mol% LiI. We find that moisture stability improves with 75 mol% Li2S modifier content and the introduction of a Li 2 O co-modifier. After a 30 min exposure in a –40°C dewpoint dry room environment we found that (Li 2 S) 75 (P 2 S 5 ) 25 + 20 mol% LiI powder generated 0.1 cc/g H 2 S and its ionic conductivity decreased by over 50%. However, when SSE powder was exposed as a slurry in a dodecane carrier the same SSE composition generated 0 cc/g H 2 S and its ionic conductivity only dropped by 14%. Our results show that sulfide SSEs have acceptable moisture stability when appropriately processed in a dry room environment.

25 ENERGY STORAGE↗

DOE OSTI2022

Consolidation of composite cathodes with NCM and sulfide solid-state electrolytes by hot pressing for all-solid-state Li metal batteries

In this study, hot pressing was evaluated as a method of cell fabrication to increase the energy density of next-generation all-solid-state batteries with NCM active material and sulfide solid-state electrolyte. Hot pressing involves consolidating glassy sulfide electrolyte by the application of pressure at a temperature above the electrolyte’s glass transition temperature. Typically, cell stacks are formed at room temperature and retain 15–30% porosity that limits cell energy density. On the other hand, the porosity of hot-pressed cell stacks is reduced to less than 10%. The electrochemical function of hot-pressed cathode composites was assessed as a function of active material and solid-state electrolyte compositions. Specifically, LiNi 0.85 Co 0.10 Mn 0.05 O 2 and LiNi 0.6 Co 0.2 Mn 0.2 O 2 were studied in combination with either glassy Li 7 P 3 S 11 , glassy Li 3 PS 4 , or β-Li 3 PS 4 solid-state electrolytes. Cathode composites composed of LiNi 0.6 Co 0.2 Mn 0.2 O 2 and Li 3 PS 4 maintained the best function after hot pressing at 200 °C and 370 MPa for 10 min. It was found that LiNi 0.6 Co 0.2 Mn 0.2 O 2 ’s resistance to microcracking and the inherent stability of Li 3 PS 4 ’s fully de-networked local structure are critical to maintain good electrochemical function after hot pressing. Furthermore, the results of this study show that hot pressing reduces porosity in the cathode composite and confirms the feasibility of cathode support of consolidated, reinforced glass separators.

25 ENERGY STORAGE↗