Wafer-scale waveguide sidewall roughness scattering loss characterization by image processing
Photonic integrated circuits (PICs) are vital for developing affordable, high-performance optoelectronic devices that can be manufactured at an industrial scale, driving innovation and efficiency in various applications. Optical loss of modes in thin film waveguides and devices is a critical measure of their performance. Thin film growth, lithography, masking, and etching processes are imperfect processes that introduce significant sidewall and top-surface roughness and cause dominating optical losses in waveguides and photonic structures. This roughness, as perturbations couple light from guided to far-field radiation modes, leads to scattering losses that can be estimated from theoretical models. Typically, with UV-based lithography, sidewall roughness is significantly larger than wafer-top surface roughness. Atomic force microscopy (AFM) imaging measurement gives a 3D and high-resolution roughness profile, but the measurement is inconvenient, costly, and unscalable for large-scale PICs and at wafer-scale. Here, we evaluate the sidewall roughness profile based on 2D high-resolution scanning electron microscope (SEM) imaging. We characterized the loss on two homemade nitride and oxide films on 3-inch silicon wafers with 12 waveguide devices on each and correlated the scattering loss estimated from a 2D image-based sidewall profile and theoretical Payne model. The lowest loss of guided fundamental transverse electric (TE 0 ) mode is found at 0.075 dB/cm at 633 nm across 24 devices, a record at visible wavelength. Our work shows 100% success (edge continuity span exceeding 95% of image width/height) in edge detection in image processing of all images to estimate autocorrelation function and optical mode loss. These demonstrations offer valuable insights into waveguide sidewall roughness and a comparison of experimental and 2D SEM image processing based loss estimations with applications in loss characterization at wafer-scale PICs.