Microstructural Engineering of Cu-Rich Nanoprecipitate formation in NiCoFeCrCu0.12 High-Entropy Alloy via Severe Plastic Deformation for Enhanced Irradiation Tolerance
This study demonstrates a defect-engineering approach for controlling Cu-rich precipitates in FeNiCrCoCu0.2 high-entropy alloys (Cu-HEAs), delivering a novel pathway for next-generation nuclear reactor materials with superior irradiation resistance. This work establishes that severe plastic deformation (SPD) processing via Shear Assisted Processing and Extrusion (ShAPE) and Friction Stir Layer Deposition (FSLD) creates dense dislocation networks and subgrain boundaries that fundamentally alter precipitation behavior under identical thermal treatments. Atom probe tomography (APT) indicates that SPD produces a metastable, atomically homogeneous solid solution that, upon moderate heat treatment (500°C/10 hour), develops remarkedly stronger Cu clustering than the as-cast counterpart. High-temperature exposure (800°C/100 h) produces near-pure Cu precipitates (~90 at% Cu) with significantly enhanced defect-sink efficacy in SPD-processed alloys: precipitate sizes of 50-60 nm and number densities of 2.7-3.8 × 10¹7 m?³, compared to 89 nm and 0.44 × 10¹7 m?³ in as-cast materials. Collectively, the findings establish defect-mediated precipitation control as a scalable, high-impact route to tailor sink density and distribution in HEAs, enabling microstructures optimized for irradiation tolerance and mechanical robustness in nuclear reactor environments.