DOE OSTI2024

Microstructural Passivation of Patterned Al 2 O 3 Back Contacts on CdS/CdTe Solar Cells

Abstract Patterned aluminum oxide (Al 2 O 3 ) back contact on cadmium telluride (CdTe) solar cells can effectively mitigate the loss of the majority carriers while retaining the passivation benefits for minority carriers. This study investigates the impact of the point‐contact geometry on cell performance, where the spacing of the microholes is systematically varied at a constant microhole diameter (≈16 µm). Microhole arrays are created on an evaporated Al 2 O 3 layer (≈30 nm) on CdTe using laser‐beam lithography and selective wet etching processes. Comparative analysis indicates a significant decrease in fill factor (FF) and short‐circuit current ( I SC ) when the contact fraction falls below 30%, likely due to the Al 2 O 3 barrier impeding majority carriers. Above this fraction, FF and I SC are comparable to those of baseline CdTe cells without Al 2 O 3 . Open‐circuit voltage ( V OC ) shows a gradual decrease as Al 2 O 3 coverage is reduced but exhibits a slight increase (<15 mV) when the contact fraction exceeds 30%. Cathodoluminescence (CL) characterization reveals that significantly improved radiative recombination occurs within the CdTe grain bulk with Al 2 O 3 , whereas this effect on grain boundaries is minimal. The findings imply complex local carrier dynamics in the patterned back‐contact region, closely tied to the microstructural properties of CdTe‐based solar cells.

Roy, Etee Kawna↗

DOE OSTI2023

Subsurface Characteristics of Metal-Halide Perovskites Polished by an Argon Ion Beam

Focused ion beam (FIB) techniques have been frequently used to section metal-halide perovskites for microstructural investigations. However, the ion beams directly irradiating the sample surface may alter its properties far different from those of pristine, potentially leading to modified deterioration mechanisms under aging stressors. Here, we combine complementary approaches to measure the subsurface characteristics of polished perovskites and identify the chemical species responsible for the measured properties. Analysis of the experimental results in conjunction with Monte Carlo simulations indicates that atomic displacements and local heating occur in the first ≈15 nm of the subsurface of methylammonium lead iodide (MAPbI 3 ) by glancing-angle Ar + beam irradiation (4 kV at 3°). The lead-rich, iodine-deficient surface promotes rapid phase segregation under thermal aging conditions. On the other hand, despite the subsurface modification, our experiments confirm that the rest of the MAPbI 3 bulk retains the material integrity. Our observation supports that polished perovskites could serve in studying the properties of bulk or buried junctions far away from the altered subsurface with care.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

Resolving surface potential variation in Ge/MoS 2 heterostructures with Kelvin probe force microscopy

In this work, we employ an atomic force microscopy-based technique, Kelvin probe force microscopy, to analyze heterogeneities of four different 2D/3D Ge/MoS 2 heterostructures with Ge chemical vapor deposition (CVD) time. High-contrast spatially resolved contact potential difference (CPD) maps reveal the evolution of the samples by Ge deposition. The CPD map in an as-prepared sample does not display any heterogeneity, but CPD contrasts along the grain boundaries are obviously noticed as Ge is deposited on MoS 2 . With a sufficiently long Ge CVD deposition time, strong grain-to-grain CPD variations over the 2D/3D heterostructures are observed. The results show the variations of the work function from grain to grain that are attributed to the strain induced by the Ge island formation on the cracked MoS2 initiated by sulfur vacancies.

36 MATERIALS SCIENCE↗