Assessing Carrier Mobility, Dopability, and Defect Tolerance in the Chalcogenide Perovskite Ba Zr S 3

The chalcogenide perovskite Ba Zr S 3 has attracted much attention as a promising solar absorber for thin-film photovoltaics. Here we use first-principles calculations to evaluate its carrier transport and defect properties. We find that Ba Zr S 3 has a phonon-limited electron mobility of 37 cm 2 / V s, which is comparable to that in halide perovskites, but lower hole mobility of 11 cm 2 / V s. The defect computations indicate that Ba Zr S 3 is intrinsically n -type due to shallow sulfur vacancies, but that strong compensation by sulfur vacancies will prevent attempts to make it p -type. We also establish that Ba Zr S 3 shows some degree of defect tolerance, presenting only few low formation energy, deep intrinsic defects. Among the deep defects, sulfur interstitials are the dominant nonradiative recombination centers but exhibit a moderate capture coefficient. Our work highlights the material’s intrinsic limitations in carrier mobility and p -type doping, and suggests focusing on suppressing the formation of sulfur interstitials to achieve longer carrier lifetime. Published by the American Physical Society 2024

Yuan, Zhenkun (ORCID:0000000272005973)↗

First-principles study of defects and doping limits in CaO

Calcium oxide (CaO) is a promising host for quantum defects because of its ultrawide bandgap and potential for long spin coherence times. Using hybrid functional calculations, we investigate the intrinsic point defects and how they limit Fermi-level positions and doping in CaO. We find calcium and oxygen vacancies to be the most common intrinsic defects, acting as compensating acceptors and donors, respectively. Oxygen interstitials are also prevailing under O-rich conditions and act as compensating donors. Due to compensation by these defects, O-poor conditions are required to dope CaO n-type, while O-rich conditions are required for p-type doping. We find that, at room temperature, intrinsic CaO can only achieve Fermi-level positions between 1.76 eV above the valence-band maximum (VBM) and 1.73 eV below the conduction-band minimum (CBM). If suitable shallow dopants are found, the allowed range of Fermi levels would increase to between VBM + 0.53 eV and CBM − 0.27 eV and is set by the compensating intrinsic defects. Additionally, we study hydrogen impurities, and show that hydrogen will not only limit p-type doping but can also act as shallow donor when substituting oxygen (HO defects).

Physics↗