Zane A. Grady | Search NASA

NASA NTRS2019

Polymer Infused Composite Metal Foam as a Potential Aircraft Leading Edge Material

The leading edge of the aircraft wings must be free from three-dimensional disturbances caused by insect adhesion, ice accretion, and particle wear in order to improve flight performance, safety, and fuel efficiency of the aircraft. An innovative solution was explored in this work by infusing stainless steel composite metal foam (SS CMF) with a hydrophobic epoxy resin system. S-S CMF was made with 100% stainless steel using a powder metallurgy technique. The infused epoxy filled the macro- and microporosities, unique to SS CMF’s structure, creating a product with a density similar to that of aluminum. The contact angle, wear rate, erosion resistance, and insect adhesion of the novel infused composite metal foam were measured and compared to aluminum, epoxy and stainless steel. The infusion process was determined to fill up to 88% of the pores within the SS CMF and was found to reduce wettability and insect residue accretion. The contact angle of the infused SS CMF was 43% higher than its parent material, stainless steel, and 130% higher than aluminum. Insect residue maximum height and areal coverage were reduced by 60 and 30%, respectively, compared to aluminum. Grit blast experiments to simulate erosion resulted in a greater roughness increase for aluminum than for the parent epoxy resin or the resin-infused SS CMF. These results suggest that the durability and performance of infused SS CMF was superior compared to aluminum, which is the current leading edge material of choice. Based on the promising results under relevant wear and erosion conditions, it is concluded that the infused SS CMF can offer a potential tailored replacement to aluminum leading edge material.

Jacob C. Marx↗

NASA NTRS2018

Topological Control of Polystyrene-Silica Core-Shell Microspheres

Controllable surface morphology is requisite across a gamut of processes, industries, and applications. The surface morphology of silica-coated polystyrene microspheres was controllably modified to enable generation of both smooth and bumpy, or raspberry-like, surfaces. Although smooth and raspberry-like silica shells on polystyrene templates have been demonstrated extensively, the method described here used readily available materials to produce radical changes in surface morphology from a single polystyrene template coated in silica through a facile sol-gel reaction processes. Silica shells were deposited via a sol-gel process (using tetraethyl orthosilicate as the silica precursor) onto 1 to 2 m diameter anionic polystyrene spheres, fabricated by emulsifier-free polymerization. By varying of the concentration of silica precursor and ammonium hydroxide catalyst and altering the electrostatic surface interactions via addition of a cationic polymeric brush, an array of surface topologies was generated. The resulting silica shells ranged from 100 to 200 nm in thickness, as measured by calcination of the polystyrene template. Empirical relations between reaction conditions and the resulting silica colloid diameter were utilized to understand the resultant silica shell topology. These results may serve as a guide to generate a versatile platform for research in the multitude of applications where polystyrene-silica core-shell particles are utilized.

Zane A. Grady↗