Zaplatynsky, I.

Publications and source records attributed to Zaplatynsky, I..

At least 19 records
All sourcesNASA NTRSDOE OSTI
NASA NTRS1986

The effect of Cr, Co, Al, Mo and Ta on a series of cast Ni-base superalloys on the stability of an aluminide coating during cyclic oxidation in Mach 0.3 burner rig

The influence of varying the content of Co, Cr, Mo, Ta, and Al in a series of cast Ni-based gamma/gamma'superalloys on the behavior of aluminide coatings was studied in burner rig cyclic oxidation tests at 1100 C. The alloys had nominally fixed levels of Ti, W, Cb, Zr, C, and B. The alloy compositions were based on a full 2(sup 5)-fractional statistical design supplemented by 10 star point alloys and a center point alloy. This full central composite design of 43 alloys plus two additional alloys with extreme Al levels allowed a complete second degree estimating equation to be derived from the 5-compositional variables. The weight change/time data for the coated samples fitted well to the paralinear oxidation model and enabled a modified oxidation attack parameter, K'(sub a) to be derived to rank the alloys and log K' (sub a ) to be used as the dependent variable in the estimating equation to determine the oxidation resistance of the coating as a function of the underlying alloy content. The most protective aluminide coatings are associated with the highest possible base ally contents of CR and Al and at a 4 percent Ta level. The Mo and Co effects interact but at fixed levels of 0, 5, or 10% Co. A 4% Mo level is optimum.

Zaplatynsky, I.↗
NASA NTRS1986

The effect of laser glazing on life of ZrO2 TBCs in cyclic burner rig tests

The performance of laser glazed zirconia (containing 8 wt% Y2O3) TBC's was evaluated in burner rig cyclic oxidation tests at 1000 and 1050 C. It was found that the cycle duration has no effect on life of TBC's and that the increase in thickness of the glazed layer caused a slight reduction in life.

Zaplatynsky, I.↗
NASA NTRS1984

Method and apparatus for coating substrates using a laser

Metal substrates, preferably of titanium and titanium alloys, are coated by alloying or forming TiN on a substrate surface. A laser beam strikes the surface of a moving substrate in the presence of purified nitrogen gas. A small area of the substrate surface is quickly heated without melting. This heated area reacts with the nitrogen to form a solid solution. The alloying or formation of TiN occurs by diffusion of nitrogen into the titanium. Only the surface layer of the substrate is heated because of the high power density of the laser beam and short exposure time. The bulk of the substrate is not affected, and melting of the substrate is avoided because it would be detrimental.

Zaplatynsky, I.↗
NASA NTRS1983

Shrinkage of amorphous silica fibers

By the application of a new technique, the viscosity of amorphous silica fibers was determined in the 1100-1350 C temperature range. An equation was derived that describes the kinetics of shrinkage of the fibers in terms of their radius, viscosity, and surface tension.

Zaplatynsky, I.↗
NASA NTRS1982

Performance of laser glazed Zr02 TBCs in cyclic oxidation and corrosion burner test rigs

The performance of laser glazed zirconia thermal barrier coatings (TBCs) was evaluated in cyclic oxidation and cyclic corrosion tests. Plasma sprayed zirconia coatings of two thicknesses were partially melted with a CO2 laser. The power density of the focused laser beam was varied from 35 to 75 W/sq mm, while the scanning speed was about 80 cm per minute. In cyclic oxidation tests, the specimens were heated in a burner rig for 6 minutes and cooled for 3 minutes. It is indicated that the laser treated samples have the same life as the untreated ones. However, in corrosion tests, in which the burner rig flame contained 100 PPM sodium fuel equivalent, the laser treated samples exhibit nearly a fourfold life improvement over that of the reference samples vary. In both tests, the lives of the samples inversely with the thickness of the laser melted layer of zirconia.

Zaplatynsky, I.↗
NASA NTRS1981

Review of NASA progress in thermal barrier coatings for stationary gas turbines

Ceramic thermal barrier coatings for industrial/utility gas turbines were investigated. In burner rig tests of a zirconia yttria/nickel chromium aluminum yttrium ZrO2-12w/0Y2O3/NiCrAlY coating system on air cooled superalloy specimens, ceramic coating life (spallation) was sensitive to Na and V concentration in the fuel. The locations of coating spallation correspond to areas where combustion products were predicted to condense. Three new thermal barrier coating systems were identified. These are based on calcium silicate, ZrO2-8w/0Y2O3, and a MgO-NiCrAlY cermet. The spall resistance can be increased by reducing the ceramic layer thickness from 0.038 to 0.013 cm and by the use of more oxidation/corrosion resistant bond coats.

Hodge, P. E.↗
NASA NTRS1980

Comparative evaluation of insulating properties of plasma-sprayed ceramic coatings

A simple method for evaluating the thermal insulating capability of ceramic coatings was devised. It is based on monitoring the temperature of the uncoated back surface of a thin superalloy disk while its front surface, coated with the ceramic material, is exposed to the high-temperature environment of an electric muffle furnace. The results obtained indicate that zirconia containing 8 wt% Y2O3 is a better thermal insulator than barium zirconate or calcium orthosilicate.

Zaplatynsky, I.↗
NASA NTRS1980

Thermal barrier coatings - Burner rig hot corrosion test results

A Mach 0.3 burner rig test program was conducted to examine the sensitivity of thermal barrier coatings to Na- and V-contaminated combustion gases simulating potential utility gas turbine environments. Coating life of the standard ZrO2-12Y2O3/Ni-16.2Cr-5.6Al-0.6Y (composition in wt %) NASA thermal barrier coating system which was developed for aircraft gas turbines was significantly reduced in such environments. Two thermal barrier coating systems, Ca2SiO4/Ni-16.2Cr-5.6Al-0.6Y and ZrO2-8Y2O3/Ni-16.4Cr-5.1Al-0.15Y and a less insulative cermet coating system, 50 vol % MgO-50 vol % Ni-19.6Cr-17.1Al-0.97Y/Ni-16.2Cr-5.6Al-0.6Y, were identified as having much improved corrosion resistance compared to the standard coating.

Hodge, P. E.↗
NASA NTRS1979

Reactions of calcium orthosilicate and barium zirconate with oxides and sulfates of various elements

Calcium orthosilicate and barium zirconate were evaluated as the insulation layer of thermal barrier coatings for air cooled gas turbine components. Their reactions with various oxides and sulfates were studied at 1100 C and 1300 C for times ranging up to 400 and 200 hours, respectively. These oxides and sulfates represent potential impurities or additives in gas turbine fuels and in turbine combustion air, as well as elements of potential bond coat alloys. The phase compositions of the reaction products were determined by X-ray diffraction analysis. BaZrO3 and 2CaO-SiO2 both reacted with P2O5, V2O5, Cr2O3, Al2O3, and SiO2. In addition, 2CaO-SiO2 reacted with Na2O, BaO, MgO, and CoO and BaZrO3 reacted with Fe2O3.

Zaplatynsky, I.↗
NASA NTRS1978

Thermal barrier coatings: Burner rig hot corrosion test results

A Mach 0.3 burner rig test program was conducted to examine the sensitivity of thermal barrier coatings to Na and V contaminated combustion gases simulating potential utility gas turbine environments. Coating life of the standard ZrO2-12Y2O3/Ni-16.2Cr-5.6Al-0.6Y NASA thermal barrier coating system which was developed for aircraft gas turbines was significantly reduced in such environments. Two thermal barrier coating systems, Ca2SiO4/Ni-16.2Cr-5.6Al-0.6Y and ZrO2-8Y2O3/Ni-16.4Cr-5.1Al-0.15Y and a less insulative cermet coating system, 50 volume percent MgO-50 volume percent Ni-19.6Cr-17.1Al-0.97Y/Ni-16.2Cr-5.6Al-0.6Y, were identified as having much improved corrosion resistance compared to the standard coating.

Hodge, P. E.↗
NASA NTRS1978

Reactions of yttria-stabilized zirconia with oxides and sulfates of various elements

The reactions between partially stabilized zirconia, containing 8 weight-percent yttria, and oxides and sulfates of various elements were studied at 1200, 1300, and 1400 C for times to 800, 400, and 200 hours, respectively. These oxides and sulfates represent impurities and additives potentially present in gas turbine fuels or impurities in the turbine combustion air as well as the elements of the substrate alloys in contact with zirconia. Based on the results, these compounds can be classified in four groups: (1) compounds which did not react with zirconia (Na2SO4, K2SO4, Cr2O3, Al2O3 and NiO); (2) compounds that reached completely with both zirconia phases (CaO, BaO, and BaSO4); (3) compounds that reacted preferentially with monoclinic zirconia (Na2O, K2O, CoO, Fe2O3, MgO, SiO2, and ZnO); and (4) compounds that reacted preferentially with cubic zirconia (V2O5, P2O5).

Zaplatynsky, I.↗
NASA NTRS1977

Volatilization of oxides during oxidation of some superalloys at 1200 C

Volatilization of oxides during cyclic oxidation of commercial Nichrome, Inconel 750, Rene 41, Stellite 6B, and GE-1541 was studied at 1200 C in static air. Quantitative analysis of oxide vapor deposits revealed that oxides of tungsten, molybdenum, niobium, manganese, and chromium volatilized preferentially from the oxide scales. Aluminum and silicon were not detected in vapor deposits. For all the alloys except GE-1541 chromium was found to be the main metallic element in the oxide scales.

Zaplatynsky, I.↗
NASA NTRS1977

Volatilization of oxides during oxidation of some superalloys at 1200 C

Volatilization of oxides during cyclic oxidation of commercial Nichrome, Inconel 750, Rene 41, Stellite 6B, and GE-1541 was studied at 1200 C in static air. Quantitative analysis of oxide vapor deposits revealed that oxides of tungsten, molybdenum, niobium, manganese, and chromium volatilized preferentially from the oxide scales. Aluminum and silicon were not detected in vapor deposits. For all the alloys except GE-1541, chromium was found to be the main metallic element in the oxide scales.

Zaplatynsky, I.↗
NASA NTRS1976

Oxidation behavior of nickel-chromium-aluminum-yttrium - Magnesium oxide and nickel-chromium-aluminum-yttrium - zirconate type of cermets

The 1100 and 1200 C cyclic oxidation resistance of dense Ni-Cr-Al-Y - MgO, Ni-Cr-Al-Y - CaZrO3, Ni-Cr-Al-Y - SrZrO3, Ni-Cr-Al-Y - MgZro3 cermets and a 70 percent dense Ni-Cr-Al-Y developmental material was determined. The cermets contained 60 and 50 volume percent of Ni-Cr-Al-Y which formed a matrix with the oxide particles imbedded in it. The cermets containing MgO were superior to cermets based on zirconates and to the porous Ni-Cr-Al-Y material.

Zaplatynsky, I.↗
NASA NTRS1975

Effect of magnesium oxide content on oxidation behavior of some superalloy-base cermets

The effect of increasing magnesium oxide (MgO) content on the cyclic oxidation resistance of hot-pressed cermets of MgO in NiCrAlY, MgO in Hoskins-875, MgO in Inconel-702, and MgO in Hastelloy-X was investigated. The cermets with magnesium oxide levels of 5, 10, 20, and 40 vol percent were examined. The cyclic oxidation behavior of these cermets at 1100 and 1200 C in still air was determined by a thermogravimetric method supplemented by X-ray diffraction analysis and light and electron microscopy. In all instances, MgO prevented grain growth in the metallic phase. No evidence of oxidation along interphase boundaries was detected. Cermets of MgO in NiCrAlY and MgO in Hoskins-875 were superior to cermets of MgO in Inconel-702 and MgO in Hastelloy-X. Their oxidation resistance was degraded only when the MgO content was 40 vol percent. The oxidation behavior of MgO-in-Inconel-702 powder cermets containing 5- and 10-vol percent MgO was approximately similar to that of pure Inconel-702 compacts. The 20- and 40-vol percent MgO content reduced the oxidation resistance of MgO-in-Inconel-702 powder cermets relative to that of pure Inconel-702.

Zaplatynsky, I.↗