Endurance and failure characteristics of modified Vasco X-2, CBS 600 and AISI 9310 spur gears

Gear endurance tests and rolling-element fatigue tests were conducted to compare the performance of spur gears made from AISI 9310, CBS 600 and modified Vasco X-2 and to compare the pitting fatigue lives of these three materials. Gears manufactured from CBS 600 exhibited lives longer than those manufactured from AISI 9310. However, rolling-element fatigue tests resulted in statistically equivalent lives. Modified Vasco X-2 exhibited statistically equivalent lives to AISI 9310. CBS 600 and modified Vasco X-2 gears exhibited the potential of tooth fracture occurring at a tooth surface fatigue pit. Case carburization of all gear surfaces for the modified Vasco X-2 gears results in fracture at the tips of the gears.

Townsend, D. P.↗
NASA NTRS1980

Some limitations in applying classical EHD film-thickness formulae to a high-speed bearing

Elastohydrodynamic film thickness was measured for a 20 mm ball bearing using the capacitance technique. The bearing was thrust loaded to 90, 448, and 778 N. The corresponding maximum stresses on the inner race were 1.28, 2.09, and 2.45 GPa. Test speeds ranged from 400 to 14,000 rpm. Film thickness measurements were taken with four different lubricants: (1) synthetic paraffinic; (2) synthetic paraffinic with additives; (3) neopentylpolyol (tetra) ester; and (4) synthetic cycloaliphatic hydrocarbon traction fluid. The test bearing was mist lubricated. Test temperatures were 300, 338, and 393 K. The measured results were compared to theoretical predictions and are presented.

Coy, J. J.↗
NASA NTRS1979

NASA gear research and its probable effect on rotorcraft transmission design

The NASA Lewis Research Center devised a comprehensive gear technology research program beginning in 1969, the results of which are being integrated into the NASA civilian Helicopter Transmission System Technology Program. Attention is given to the results of this gear research and those programs which are presently being undertaken. In addition, research programs studying pitting fatigue, gear steels and processing, life prediction methods, gear design and dynamics, elastohydrodynamic lubrication, lubrication methods and gear noise are presented. Finally, the impact of advanced gear research technology on rotorcraft transmission design is discussed.

Zaretsky, E. V.↗
NASA NTRS1979

Evaluation of CBS 600 carburized steel as a gear material

Gear endurance tests were conducted with one lot of consumable-electrode vacuum-melted (CVM) AISI 9310 gears and one lot of air-melt CBS 600 gears. The gears were 8 pitch with a pitch diameter of 8.89 centimeters (3.5 in.). Bench-type rolling-element fatigue tests were also conducted with one lot of CVM AISI 9310, three lots of CVM CBS 600, and one of air-melt CBS 600 material. The rolling-element bars were 0.952 centimeter (0.375 in.) in diameter. The CBS 600 material exhibited pitting fatigue lives in both rolling-element specimens and gears at least equivalent to that of CVM AISI 9310. Tooth fracture failure occurred with the CBS 600 gears after overrunning a fatigue spall, but it did not occur with the CVM AISI 9310 gears. Tooth fracture in the CBS 600 was attributed to excessive carbon content in the case, excessive case depth, and a higher than normal core hardness.

Townsend, D. P.↗
NASA NTRS1979

NASA gear research and its probable effect on rotorcraft transmission design

The results of the NASA gear research is reviewed as well as those programs which are presently being undertaken. Research programs studying pitting fatigue, gear steels and processing, life prediction methods, gear design and dynamics, elastohydrodynamic lubrication, lubrication methods and gear noise are presented. The impact of advanced gear research technology on rotorcraft transmission design is discussed.

Zaretsky, E. V.↗
NASA NTRS1978

Predicted and experimental performance of jet-lubricated 120-millimeter-bore ball bearings operating to 2.5 million DN

Bearing inner- and outer-race temperatures and friction power losses were calculated using two computer programs. The values obtained were compared with previously reported experimental data for 120 mm bore bearings which operated at thrust loads to 22 240 N (5000 lb), shaft speeds to 20 800 rpm, and with two lubricant flow rates. One program severely underestimated the power loss, while the other, called SHABERTH, provided a good prediction of both race temperatures and power losses.

Coe, H. H.↗
NASA NTRS1978

Rolling-element fatigue life of AISI M-50 and 18-4-1 balls

Rolling element fatigue studies were conducted with AISI M-50, EFR 18-4-1, and VAR 18-4-1. Groups of 12.7 mm (1/2-in) diameter balls of each material were tested in the five ball fatigue tester. Test conditions included a load of 1540 N (347 lbf) giving a maximum Hertz stress of 5520 MPa (800 000 psi), a shaft speed of 10,700 rpm, and a contact angle of 30 deg. Tests were run at a race temperature of 339 K (150 F) with a type 2 ester lubricant. The rolling element fatigue life of AISI M-50 was not significantly different from that of EFR 18-4-1 or VAR 18-4-1 based on a statistical comparison of the test results.

Parker, R. J.↗
NASA NTRS1977

Restoration of bearings

Process consisting of grinding raceways to oversize but original quality condition and installing new oversize balls or bearings restores wornout ball and roller bearings to original quality, thereby doubling their operating life. Evaluations reveal process results in restoration of 90% of replaced bearings at less than 50% of new-bearing costs.

Parker, R. J.↗
NASA NTRS1977

Experimental and Analytical Load-Life Relation for AISI 9310 Steel Spur Gears

Life tests were conducted at three different loads with three groups of 8.9 cm pitch diameter spur gears made of vacuum arc remelted VAR AISI 9310 steel. Life was found to vary inversely with load to the 4.3 and 5.1 power at the L10 sub and L50 sub life levels, respectively. The Weibull slope varied linearly with maximum Hertz contact stress, having an average value of 2.5. The test data when compared to AGMA standards showed a steeper slope for the load-life diagram.

Townsend, D. P.↗
NASA NTRS1977

Experimental and analytical load-life relation for AISI 9310 steel spur gears

Life tests were conducted at three different loads with three groups of 8.9 cm, pitch diameter spur gears made of vacuum arc remelted AISI 9310 steel. Life was found to vary inversely with load to the 4.3 and 5.1 power at the L-10 and L-50 life levels, respectively. The Weibull slope varied linearly with maximum Hertz contact stress, having an average value of 2.5. The test data when compared to AGMA standards showed a steeper slope for the load-life diagram.

Townsend, D. P.↗
NASA NTRS1977

Life analysis of restored and refurbished bearings

An analysis of the potential life of refurbished and restored bearings was performed. The sensitivity of 10-percent life and mean-time-between-failure to the effects of cumulative fatigue damage and the amount of stressed volume removed in the restoration process were examined. A modified Lundberg-Palmgren theory was used to predict that the expected 10-percent life of a restored bearing, which is dependent on the previous service time and the volume of material removed from the race surfaces, can be between 74 and 100 percent of the new bearing life. Using renewal theory, it is found that the mean time between failure ranged from 90 to 100 percent of that for a new bearing.

Coy, J. J.↗
NASA NTRS1976

Fatigue life analysis for traction drives with application to a toroidal type geometry

A contact fatigue life analysis for traction drives was developed which was based on a modified Lundberg-Palmgren theory. The analysis was used to predict life for a cone-roller toroidal traction drive. A 90-percent probability of survival was assumed for the calculated life. Parametric results were presented for life and Hertz contact stress as a function of load, drive ratio, and size. A design study was also performed. The results were compared to previously published work for the dual cavity toroidal drive as applied to a typical compact passenger vehicle drive train. For a representative duty cycle condition wherein the engine delivers 29 horsepower at 2000 rpm with the vehicle moving at 48.3 km/hr (30 mph) the drive life was calculated to be 19,200 km (11 900 miles).

Coy, J. J.↗
NASA NTRS1976

Bearing restoration by grinding

A joint program was undertaken by the NASA Lewis Research Center and the Army Aviation Systems Command to restore by grinding those rolling-element bearings which are currently being discarded at aircraft engine and transmission overhaul. Three bearing types were selected from the UH-1 helicopter engine (T-53) and transmission for the pilot program. No bearing failures occurred related to the restoration by grinding process. The risk and cost of a bearing restoration by grinding programs was analyzed. A microeconomic impact analysis was performed.

Hanau, H.↗
NASA NTRS1976

Evaluation of ball and roller bearings restored by grinding

A joint program was undertaken to restore by grinding those rolling-element bearings which are currently being discarded at aircraft engine and transmission overhaul. Three bearing types were selected from the UH-1 helicopter engine (T-53) and transmission for the pilot program. Groups of each of these bearings were visually and dimensionally inspected for suitability for restoration. A total of 250 bearings were restored by grinding. Of this number, 30 bearings from each type were endurance tested to a TBO of 1600 hours. No bearing failures occurred related to the restoration by grinding process. The two bearing failures which occurred were due to defective rolling elements and were typical of those which may occur in new bearings. The restorable component yield to the three groups was in excess of 90 percent.

Parker, R. J.↗
NASA NTRS1976

Endurance and failure characteristic of main-shaft jet engine bearing at 3 million DN

Groups of thirty 120-mm bore angular-contact ball bearings were endurance tested at a speed of 12,000 and 25,000 rpm (1.44 million and 3.0 million DN, where DN is the product of the bearing bore in mm and the shaft speed in rpm) and a thrust load of 66,721 N. The bearings were manufactured from a single heat of VIM-VAR AISI M-50 steel. At 1.44 million and 3.0 million DN, 84,483 and 74,800 bearing test hours were accumulated, respectively. Test results were compared with similar bearings made from CVM AISI M-50 steel run under the same conditions. Bearing lives at speeds of 3 million DN with the VIM-VAR AISI M-50 steel were nearly equivalent to those obtained at lower speeds. A combined processing and material life factor of 44 was found for VIM-VAR AISI M-50 steel. Continuous running after a spall has occurred at 3.0 million DN can result in a destructive fracture of the bearing inner race.

Bamberger, E. N.↗
NASA NTRS1976

Endurance and failure characteristics of main-shaft jet engine bearings at 3x10 to the 6th power DN

Groups of thirty 120-mm bore angular contact ball bearings were endurance tested at a speed of 12,000 and 25,000 rpm and a thrust load of 66 721 N. The bearings were manufactured from a single heat of VIM-VAR AISI M-50 steel. At 1.44X1 million and 3.0x1 million DN, 84 483 and 74 800 bearing test hours were accumulated, respectively. Test results were compared with similar bearings made from CVM AISI M-50 steel run under the same conditions. Bearing lives at speeds of 3x1 million DN with the VIM-VAR AISI M-50 steel were nearly equivalent to those obtained at lower speeds. A combined processing and material life factor of 44 was found for VIM-VAR AISI M-50 steel. Continuous running after a spall has occurred at 3.0x1 million DN can result in a destructive fracture of the bearing inner race.

Bamberger, E. N.↗
NASA NTRS1976

Evaluation of ball and roller bearings restored by grinding

The restoration by grinding of those rolling element bearings which are currently being discarded at aircaft engine and transmission overhaul is considered. Three bearing types were selected from the UH-1 helicopter engine and transmission for the pilot program. Groups of each of these bearings were visually and dimensionally inspected for suitability for restoration. A total of 250 bearings were restored by grinding. Of this number, 30 bearings from each type were endurance tested to a TBO of 1600 hours. No bearing failures occurred related to the restoration by grinding process. The two bearing failures which occurred were due to defective rolling elements and were typical of those which may occur in new bearings. The restorable component yield to the three groups was in excess of 90 percent.

Parker, R. J.↗