Zeng, Yachao

Publications and source records attributed to Zeng, Yachao.

12 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2023

Tuning the thermal activation atmosphere breaks the activity–stability trade-off of Fe–N–C oxygen reduction fuel cell catalysts

Fe–N–C catalysts are the most promising platinum group metal-free oxygen-reduction catalysts, but they suffer from a low density of active metal sites and the so-called activity–stability trade-off. Here we report an Fe–N–C catalyst prepared by adding an optimal amount of H 2 to the traditional inert atmosphere during the thermal activation. The presence of H 2 significantly increases the total density of FeN 4 sites, suppressing the unstable pyrrolic-N-coordinated S1 sites and favouring the stable pyridinic-N-coordinated S2 sites with shortened Fe–N bond lengths. Here, we propose that the intrinsically stable S2 sites are probably arranged in well-graphitized carbon layers, and the S1 sites exist in less-graphitized carbon. H 2 could remove unstable S1 sites and retain stable S2 sites during the pyrolysis to break the challenging activity–stability trade-off. The Fe–N–C catalyst in membrane electrode assemblies maintains a current density of 67 mA cm -2 at 0.8 V (H 2 –air) after 30,000 voltage cycles (0.60 to 0.95 V under H 2 –air), achieving encouraging durability and performance simultaneously.

25 ENERGY STORAGE↗
DOE OSTI2023

Chemical Kinetic Method for Active-Site Quantification in Fe-N-C Catalysts and Correlation with Molecular Probe and Spectroscopic Site-Counting Methods

Mononuclear Fe ions ligated by nitrogen (FeN x ) dispersed on nitrogen-doped carbon (Fe-N-C) serve as active centers for electrocatalytic O 2 reduction and thermocatalytic aerobic oxidations. Despite their promise as replacements for precious metals in a variety of practical applications, such as fuel cells, the discovery of new Fe-N-C catalysts has relied primarily on empirical approaches. In this context, the development of quantitative structure–reactivity relationships and benchmarking of catalysts prepared by different synthetic routes and by different laboratories would be facilitated by the broader adoption of methods to quantify atomically dispersed FeN x active centers. In the present study, we develop a kinetic probe reaction method that uses the aerobic oxidation of a model hydroquinone substrate to quantify the density of FeN x centers in Fe- N-C catalysts. The kinetic method is compared with low-temperature Mössbauer spectroscopy, CO pulse chemisorption, and electrochemical reductive stripping of NO derived from NO 2 – on a suite of Fe-N-C catalysts prepared by diverse routes and featuring either the exclusive presence of Fe as FeN x sites or the coexistence of aggregated Fe species in addition to FeN x . The FeN x site densities derived from the kinetic method correlate well with those obtained from CO pulse chemisorption and Mössbauer spectroscopy. The broad survey of Fe-N-C materials also reveals the presence of outliers and challenges associated with each site quantification approach. Furthermore, the kinetic method developed here does not require pretreatments that may alter active-site distributions nor specialized equipment beyond reaction vessels and analytical instrumentation (e.g., NMR).

36 MATERIALS SCIENCE↗
DOE OSTI2023

Pt Nanoparticles on Atomic-Metal-Rich Carbon for Heavy-Duty Fuel Cell Catalysts: Durability Enhancement and Degradation Behavior in Membrane Electrode Assemblies

Proton exchange membrane fuel cells (PEMFCs) are a promising zero-emission power source for heavy-duty vehicles (HDVs). However, long-term durability of up to 25,000 h is challenging because current carbon support, catalyst, membrane, and ionomer developed for traditional light-duty vehicles cannot meet the stringent requirement. Therefore, understanding catalyst degradation mechanisms under the HDV condition is crucial for rationally designing highly active and durable platinum group metal (PGM) catalysts for high-performance membrane electrode assemblies (MEAs). Herein, we report a PGM catalyst consisting of platinum nanoparticles with a high content (40 wt %) on atomic-metal-site (e.g., MnN 4 )-rich carbon support. MEAs with the Pt (40 wt %)/Mn–N–C cathode catalyst achieved significantly enhanced performance and durability, generating 1.41 A cm –2 at 0.7 V under HDV conditions (0.25 mgPt cm –2 and 250 kPa abs pressure) and retaining 1.20 A cm –2 after an extended and accelerated stress test up to 150,000 voltage cycles. Electron microscopy studies indicate that most fine Pt nanoparticles are retained on or/and in the carbon support covered with the ionomer throughout the catalyst layer at the end of life. During the long-term stability test, the observed electrochemical active surface area reduction and performance loss primarily result from Pt depletion in the catalyst layer due to Pt dissolution and redeposition at the interface of the cathode and membrane. Importantly, the first-principle density functional theory calculations further reveal a support entrapment effect of the Mn–N–C, in which the MnN 4 site can specifically adsorb the Pt atom and further retard the Pt dissolution and migration, therefore enhancing long-term MEA durability.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2023

Regulating Catalytic Properties and Thermal Stability of Pt and PtCo Intermetallic Fuel-Cell Catalysts via Strong Coupling Effects between Single-Metal Site-Rich Carbon and Pt

Developing low platinum-group-metal (PGM) catalysts for the oxygen reduction reaction (ORR) in proton-exchange membrane fuel cells (PEMFCs) for heavy-duty vehicles (HDVs) remains a great challenge due to the highly demanded power density and long-term durability. Here, this work explores the possible synergistic effect between single Mn site-rich carbon (Mn SA -NC) and Pt nanoparticles, aiming to improve intrinsic activity and stability of PGM catalysts. Density functional theory (DFT) calculations predicted a strong coupling effect between Pt and MnN 4 sites in the carbon support, strengthening their interactions to immobilize Pt nanoparticles during the ORR. The adjacent MnN 4 sites weaken oxygen adsorption at Pt to enhance intrinsic activity. Well-dispersed Pt (2.1 nm) and ordered L1 2 -Pt 3 Co nanoparticles (3.3 nm) were retained on the Mn SA -NC support after indispensable high-temperature annealing up to 800 °C, suggesting enhanced thermal stability. Both PGM catalysts were thoroughly studied in membrane electrode assemblies (MEAs), showing compelling performance and durability. The Pt@Mn SA -NC catalyst achieved a mass activity (MA) of 0.63 A mg Pt –1 at 0.9 V iR-free and maintained 78% of its initial performance after a 30,000-cycle accelerated stress test (AST). The L1 2 -Pt 3 Co@Mn SA -NC catalyst accomplished a much higher MA of 0.91 A mg Pt –1 and a current density of 1.63 A cm –2 at 0.7 V under traditional light-duty vehicle (LDV) H 2 –air conditions (150 kPa abs and 0.10 mg Pt cm –2 ). Furthermore, the same catalyst in an HDV MEA (250 kPa abs and 0.20 mg Pt cm –2 ) delivered 1.75 A cm –2 at 0.7 V, only losing 18% performance after 90,000 cycles of the AST, demonstrating great potential to meet the DOE targets.

25 ENERGY STORAGE↗
DOE OSTI2022

Atomically dispersed iron sites with a nitrogen–carbon coating as highly active and durable oxygen reduction catalysts for fuel cells

Nitrogen-coordinated single atom iron sites (FeN 4 ) embedded in carbon (Fe–N–C) are the most active platinum group metal-free oxygen reduction catalysts for proton-exchange membrane fuel cells. Still, current Fe–N–C catalysts lack sufficient long-term durability and are not yet viable for practical applications. Here we report a highly durable and active Fe–N–C catalyst synthesized using heat treatment with ammonia chloride followed by high-temperature deposition of a thin layer of nitrogen-doped carbon on the catalyst surface. We propose that catalyst stability is improved by converting defect-rich pyrrolic N-coordinated FeN 4 sites into highly stable pyridinic N-coordinated FeN 4 sites. The stability enhancement is demonstrated in membrane electrode assemblies using accelerated stress testing and a long-term steady-state test (>300 h at 0.67 V), approaching a typical Pt/C cathode (0.1 mg Pt cm -2 ). The encouraging stability improvement represents a critical step in developing viable Fe–N–C catalysts to overcome the cost barriers of hydrogen fuel cells for numerous applications.

08 HYDROGEN↗
DOE OSTI2022

High-Platinum-Content Catalysts on Atomically Dispersed and Nitrogen Coordinated Single Manganese Site Carbons for Heavy-Duty Fuel Cells

Fuel cells for heavy-duty vehicles (HDVs) have attracted considerable attention because of their unique scalability, better fuel economy, the less demand for hydrogen refilling infrastructure. However, the potential application requires more stringent fuel cell durability up to 25,000 h. Membrane electrode assemblies (MEAs) made from platinum group metal (PGM) catalyst with relatively high loading 0.3 mgPt cm –2 play a crucial role in ensuring high-power and long-term durability. Integrating fine PGM nanoparticles and robust carbon support with strengthened interactions is critical for improving MEA performance and durability. Herein, a unique atomically dispersed and nitrogen coordinated single Mn site-rich carbon (M–N–C) support was developed for high content (40 wt%) platinum catalysts for the oxygen reduction reaction (ORR) cathode with reduced thickness. Compared with two controls studied in this work (e.g., a porous graphitic carbon-supported Pt and a commercial TKK Pt/C catalysts), the Pt (40 wt%)/Mn–N–C catalyst exhibited much enhanced catalytic activity and stability for the ORR in both aqueous acidic electrolyte and polymer electrolyte-based MEA. Here, we carefully elucidated the—role of the Mn–N–C support in promoting Pt catalyst concerning its high surface area, partially graphitic structure, and nitrogen dopants, providing better Pt nanoparticle dispersion, and strengthened interactions between Pt and carbon. Consequently, the MEA from the Pt (40 wt%)/Mn–N–C catalyst generated a 1.61 A cm –2 at 0.7 V based on HDV conditions (0.2 mgPt cm –2 and 250 kPa air). More importantly, the MEA is highly durable and can retain 1.31 A cm –2 at 0.7 V after 30,000 voltage cycles (~19% loss), surpassing the commercial Pt/C catalyst (loss of ~56%). Therefore, the Mn–N–C carbon-supported Pt catalyst holds a great promise to meet the challenging DOE target (1.07 A cm –2 at 0.7 V after 150,000 cycles) for HDVs.

25 ENERGY STORAGE↗
DOE OSTI2021

Atomic Structure Evolution of Pt–Co Binary Catalysts: Single Metal Sites versus Intermetallic Nanocrystals

Due to their exceptional catalytic properties for the oxygen reduction reaction (ORR) and other crucial electrochemical reactions, PtCo intermetallic nanoparticle (NP) and single atomic (SA) Pt metal site catalysts have received considerable attention. However, their formation mechanisms at the atomic level during high-temperature annealing processes remain elusive. Furthermore, the thermally driven structure evolution of Pt–Co binary catalyst systems is investigated using advanced in situ electron microscopy, including PtCo intermetallic alloys and single Pt/Co metal sites. The pre-doping of CoN 4 sites in carbon supports and the initial Pt NP sizes play essential roles in forming either Pt 3 Co intermetallics or single Pt/Co metal sites. Importantly, the initial Pt NP loadings against the carbon support are critical to whether alloying to L1 2 -ordered Pt 3 Co NPs or atomizing to SA Pt sites at high temperatures. High Pt NP loadings (e.g., 20%) tend to lead to the formation of highly ordered Pt 3 Co intermetallic NPs with excellent activity and enhanced stability toward the ORR. In contrast, at a relatively low Pt loading (<6 wt%), the formation of single Pt sites in the form of PtC 3 N is thermodynamically favorable, in which a synergy between the PtC 3 N and the CoN 4 sites could enhance the catalytic activity for the ORR, but showing insufficient stability.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Effects of Ink Formulation on the Structure and Performance of PGM-Free Catalyst Layer in PEMFCs

Platinum group metal (PGM) catalysts are the major electrocatalysts for oxygen reduction reaction (ORR) in the polymer electrolyte membrane fuel cells (PEMFCs). The cost becomes unaffordable if the PEMFC is in massive application. The PGM-Free catalyst shows very promising activity in rotation disk electrode (RDE) testing. The half-wave potential could reach 0.91 V versus standard hydrogen electrode (SHE). However, in a membrane electrode assembly (MEA), the performance of PGM-Free catalysts is not good enough to replace the PGM catalysts. Since the PGM-free catalysts are so different from the PGM catalysts in terms of catalytic activity, stability, surface conditions, particle size, etc., the fabrication of PGM-Free catalyst MEA cannot simply copy the method of making PGM MEA. Here we proposed a novel method of fabricating PGM-Free catalyst MEA, so that the intrinsic catalyst activity from RDE can be translated into MEA performance. The method is based on the catalyst coated membrane (CCM) method using optimized ionomer to carbon (I/C) ratio and solvent mixture of catalyst ink. Using this method, the PGM-free catalyst MEA achieved the current density 44.9 mA cm -2 at 0.9 V iR-free in H 2 /O 2 and 150 mA cm -2 at 0.8 V in H 2 /air, which surpassed the performance targets of US Department of Energy (DOE)for PGM-Free catalyst MEA. The property (solvent composition, dispersion of catalyst and ionomer in an ink), structure (pore structure) and the MEA performance have been characterized using, mercury intrusion porosimetry (MIP), MEA testing. A property-structure-performance relationship has been established.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2021

Atomically dispersed single iron sites for promoting Pt and Pt 3 Co fuel cell catalysts: performance and durability improvements

Significantly reducing platinum group metal (PGM) loading while improving catalytic performance and durability is critical to accelerating proton-exchange membrane fuel cells (PEMFCs) for transportation. In this study, we report an effective strategy to boost PGM catalysts through integrating PGM-free atomically-dispersed single metal active sites in the carbon support toward the cathode oxygen reduction reaction (ORR). We achieved uniform and fine Pt nanoparticle (NP) (~2 nm) dispersion on an already highly ORR-active FeN 4 site-rich carbon (FeN 4 –C). Furthermore, we developed an effective approach to preparing a well-dispersed and highly ordered L1 2 Pt 3 Co intermetallic nanoparticle catalyst on the FeN 4 –C support. DFT calculations predicted a synergistic interaction between Pt clusters and surrounding FeN 4 sites through weakening O 2 adsorption by 0.15 eV on Pt sites and reducing activation energy to break O–O bonds, thereby enhancing the intrinsic activity of Pt. Experimentally, we verified the synergistic effect between Pt or Pt 3 Co NPs and FeN 4 sites, leading to significantly enhanced ORR activity and stability. Especially in a membrane electrode assembly (MEA) with a low cathode Pt loading (0.1 mg Pt cm –2 ), the Pt/FeN 4 –C catalyst achieved a mass activity of 0.451 A mg Pt –1 and retained 80% of the initial values after 30 000 voltage cycles (0.60 to 0.95 V), exceeding DOE 2020 targets. Furthermore, the Pt 3 Co/FeN 4 catalyst achieved significantly enhanced performance and durability concerning initial mass activity (0.72 A mg Pt –1 ), power density (824 mW cm –2 at 0.67 V), and stability (23 mV loss at 1.0 A cm –2 ). The approach to exploring the synergy between PGM and PGM-free Fe–N–C catalysts provides a new direction to design advanced catalysts for hydrogen fuel cells and various electrocatalysis processes.

25 ENERGY STORAGE↗
DOE OSTI2021

Advanced Nanocarbons for Enhanced Performance and Durability of Platinum Catalysts in Proton Exchange Membrane Fuel Cells

Insufficient stability of current carbon supported Pt and Pt alloy catalysts is a significant barrier for proton-exchange membrane fuel cells (PEMFCs). As a primary degradation cause to trigger Pt nanoparticle migration, dissolution, and aggregation, carbon corrosion remains a significant challenge. Compared with enhancing Pt and PtM alloy particle stability, improving support stability is rather challenging due to carbon's thermodynamic instability under fuel cell operation. In recent years, significant efforts have been made to develop highly durable carbon-based supports concerning innovative nanostructure design and synthesis along with mechanistic understanding. Here, this review critically discusses recent progress in developing carbon-based materials for Pt catalysts and provides synthesis–structure–performance correlations to elucidate underlying stability enhancement mechanisms. The mechanisms and impacts of carbon support degradation on Pt catalyst performance are first discussed. The general strategies are summarized to tailor the carbon structures and strengthen the metal–support interactions, followed by discussions on how these designs lead to enhanced support stability. Based on current experimental and theoretical studies, the critical features of carbon supports are analyzed concerning their impacts on the performance and durability of Pt catalysts in fuel cells. Finally, the perspectives are shared on future directions to develop advanced carbon materials with favorable morphologies and nanostructures to increase Pt utilization, strengthen metal-support interactions, facilitate mass/charge transfer, and enhance corrosion resistance.

25 ENERGY STORAGE↗