Engineering topics

Zeng, Zuotao

Publications and source records attributed to Zeng, Zuotao.

7 records

DOE OSTI2024

Simulating the effect of grain structure and porosity on creep for powder bed fusion 316H

This report details results from modeling studies focused on identifying the potential factors influencing creep performance of 316H stainless steel manufactured using Laser Powder Bed Fusion (LPBF), with a focus on experimentally-observed and predicted differences between the response of the AM material and conventionally manufactured wrought 316H. The studies presented here systematically look at the role of grain structure, porosity and texture in the anisotropic creep behavior of the material under conditions expected in high temperature advanced nuclear reactors. A physics-based Crystal Plasticity Finite Element modeling approach has allowed us to look at these factors in isolation and study their role in the material's long-term deformation behavior. An update to the precipitation model used in the constitutive framework for 316H is also presented here, with the aim of improving the accuracy of our results from this modeling effort. This work is a step in the direction of gaining mechanistic understanding of the long-term deformation behavior of LPBF 316H, helping us model its long term performance and reducing the qualification time for the material.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Progress Report of Alloy 709 Performance in Liquid Sodium

With improved high-temperature properties, Alloy 709 shows great potential for advanced reactor applications. To understand the effects of sodium on A709, small tensile specimens were machined from two commercial heats and subject to sodium exposure in two forced convection loops operated by Argonne. Thermal aging experiments were also conducted in parallel to isolate any sodium-specific effects. An increasing trend in yield strength and a decrease trend in ultimate tensile strength can be seen with the increasing exposure time, suggesting microstructural changes at these temperatures. Nonetheless, the thermally aged and sodium exposed samples behaved similarly, implying no sodium-specific effect at these temperatures. In contrast, 316H SS exposed to sodium at 650°C showed a strong sodium effect. The different responses of A709 and 316H SS to sodium exposure is of interest and requires additional effort to understand. The cold traps of the sodium loop were replaced early in FY23. During a maintenance operation, an unexpected sodium leak incident occurred at one of the sodium loops, triggering an emergency response. An investigation into the incident revealed that the leak happened at a VCR fitting on the recently replaced cold trap. The metal gasket of the leaked VCR fitting was not compressed sufficiently. A dimensional mismatch between the new component and old piping configuration was responsible for a significant misalignment. A new cold trap with improved design is in production. The new design provides additional flexibility and an access point for post-installation helium leak check and for venting of trapped gas. These design features will make the system more error-tolerant and the installation quality verifiable. A thermodynamic analysis was performed to understand the carburization-decarburization behavior of A709 in sodium environment. The equilibrium carbon activity in the alloy was evaluated with M 23 C 6 , TiC, and NbC. The carburization-decarburization boundary was calculated with different methods developed previously. The results suggests that A709 will be carburized in SMT-1 and SMT-2, and can be decarburized in low-carbon-activity environments such as EBR-II at temperatures above 620-650°C. Nonetheless, A709 should be less likely to be decarburized than 316H SS when exposed to the same low-carbon-activity environment.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2022

Effects of Sodium Exposure on the Tensile Properties of Grade 91 steel

Two heats of G91 steel have been investigated in liquid sodium at 550- 650°C to understand their corrosion behaviour, microstructural evolution, and tensile properties. Sodium exposure experiments of subsized, sheet-type tensile specimens of G91 were performed in Argonne’s forced convection sodium materials testing loops, SMT-1 and SMT-2. Maximum exposure times of ~49,000 h at ~38,000 h, and ~20,000 h have been achieved at 550, 600, and 650°C, respectively. Thermal aging experiments of G91 steel were also conducted in parallel, and the results were compared with those of the sodium-exposed specimens to isolate the effect of thermal aging from the effect of sodium exposure. It was found that the yield stress and ultimate tensile strength of G91 were reduced by more than 50% after sodium exposures at 650°C due to decarburization. The reduction in tensile strength was accompanied by the dissolution of M 23 C 6 carbides and excessive grain growth. The effect of sodium at 550 and 600°C was insignificant for exposure times up to ~49,000 h and ~38,000 h, respectively. The effect of sodium on the microstructural stability and tensile properties of G91 is largely dependent on the carbon mass transfer in the alloy-sodium system.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗

DOE OSTI2022

Carburization and decarburization behavior of Grade 91 ferritic-martensitic steel in liquid sodium environments

Here, this paper presents a study of carbon transfer and its effect on microstructure and tensile properties of Grade 91 (G91) ferritic-martensitic steel exposed to sodium at 550–650 °C. Sodium exposure tests were conducted in Argonne's forced convection sodium loops up to exposure times of ~40,000 h. Thermal aging study of G91 steel was conducted in parallel to isolate the thermal aging effect from the sodium effect. It was found that sodium exposures at 650 °C dissolved M 23 C 6 carbides, eliminated the martensite subgrain structure resulting in excessive grain growth and reduced the tensile strength by >50%, while sodium exposures at 550 and 600 °C had an insignificant effect on its microstructure and tensile properties. These effects were attributed to the carburization/decarburization process of G91 steel in sodium environments. Carbon concentrations in sodium were determined by a foil equilibration method. The estimated carbon concentration was in the range of 0.8–1.2 ppm in the SMT-1 loop and 0.3–0.7 ppm in the SMT-2 loop. Thermodynamic analysis of the carburization – decarburization process was conducted for G91 steels exposed in sodium environments. The carbon activity-concentration relationship for G91 was evaluated by considering four phases in G91, i.e. bcc ferrite, M 23 C 6 , NbC and VC carbides. It was found that the carburization-decarburization process in G91 steel was dictated by M 23 C 6 carbides at high carbon activities, while NbC and VC carbides dominated the process at low carbon activities. The calculated carburization-decarburization boundary showed that G91 would undergo decarburization at 650 °C and carburization at 550 °C in the sodium loop environments, which was consistent with our experimental observations. This experimental and theoretical analysis provided a basis for predicting the effect of carbon transfer on the integrity of reactor components in sodium environments and for the design of new alloys used in sodium-cooled fast reactors.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Progress Report on Performance of A709 and G91 Steels in Sodium

Specimens in six different processing and heat treatment conditions of A709 H58776 were exposed to sodium at 550, 600, and 650°C, respectively for various exposure times. G91 base metal was tested in sodium at 550, 600, and 650°C, and G91 weldment at 550 and 600°C, respectively. Parallel thermal aging experiments were conducted on G91 and A709 to obtain thermal aging data for comparison with sodium exposure results to separate the thermal and sodium effects. The corrosion data obtained on A709 steel continue to show low corrosion rates, which indicate good compatibility of A709 with sodium when oxygen content is controlled. G91 has also shown acceptable corrosion rates over the temperature range of 550-650°C in sodium. Thermal aging or sodium exposures reduced the tensile strength, uniform elongation, and total elongation for A709 ESR, AOD specimens. These specimens consistently showed higher yield stress and tensile strength and lower uniform and total elongations after sodium exposure than after thermal aging under comparable testing conditions. It implies that there was an additional effect of sodium exposure that gave rise to an increase in tensile strength of A709. Dynamic strain aginginduced flow serrations were completely removed by either thermal aging or sodium exposure at 650°C, which imply that carbon or nitrogen in solution was removed from the solution and formed precipitates during aging or sodium exposures. The tensile data ruled out the possibility of decarburization under the sodium exposure conditions. The HOMO specimens behaved somewhat differently from the ESR and AOD specimens in sodium. While thermal aging and sodium exposures at 550 and 600°C decreased the yield stress and the ultimate tensile strength of G91, there was virtually no additional effect resulting from sodium exposures at these two temperatures. In contrast, sodium exposures at 650°C had a drastic effect on the yield stress and the ultimate tensile strength of G91. It is suggested that G91 experienced decarburization in the 650°C sodium environments. Carbon concentrations in sodium in the SMT-1 and SMT-2 loops were determined by a foil equilibration method. The estimated carbon concentration was in the range of 0.8-1.2 ppm in the SMT-1 loop and 0.3-0.7 ppm in the SMT-2 loop. The carbon activity in sodium in the SMT-2 loop was estimated to be 0.03-0.08 at 600°C, and 0.08-0.2 at 550°C. The carbon activity in sodium at 650°C in the SMT-1 loop was 0.04-0.07. Equilibrium simulation of the carburization – decarburization processes was conducted for A709 and G91 steels exposed in sodium environments at temperatures of 550-700°C. The carbon activity-concentration relationship for G91 was re-evaluated by considering four phases in G91, i.e. bcc ferrite, M 23 C 6 , NbC and VC carbides. It was found that the carburization-decarburization process in G91 steel was dictated by M 23 C 6 carbides at high carbon activities, while NbC carbides dominated the process at low carbon activities. Formation of NbC increases the decarburization resistance of G91 steel. It remains to be understood whether the decarburization resistance provided by MC carbides in G91 can be maintained during long-term operations of SFRs. The carbon concentration-activity relationship for A709 was calculated based on the equilibrium of fcc-austenite and M 23 C 6 carbide phase. The calculations showed that A709 decarburizes at 650°C in the SMT-1 loop environments, which is different from the experimental findings. The carbon concentration-activity relationship in A709 was further evaluated by considering four phases, including fcc-austenite, M 23 C 6 , NbC, and TiC carbide phases. TiC is the most stable carbides among the three carbide phases. The carburization-decarburization process in A709 is dictated by M 23 C 6 carbides at high carbon activities and by TiC at low carbon activities. Formation of TiC increases the decarburization resistance of A709 steel. Because of the complexity of the precipitation process in A709 during sodium exposures, detailed characterization of precipitates in sodium-exposed specimens and improved thermodynamic models are needed to understand the carburization-decarburization behavior of A709. Kinetic analysis of carbon transfer will be investigated for G91 and A709 in future work.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗

DOE OSTI2020

Decarburization and Carburization Behavior of Grade 91 Steel in Sodium Environments

Two heats of G91 steel have been investigated in sodium at 550-650°C to understand its corrosion behaviour, microstructural evolution, and tensile properties. Sodium exposure tests of subsized tensile and coupon specimens of G91 base metal and weldment were conducted in Argonne’s forced convection sodium materials testing loops. Maximum exposure times of ~39,000 h at 550°C, ~37,000 h at 600°C, and ~20,000 h at 650°C have been achieved, respectively. Thermal aging experiments of G91 steel were conducted in parallel, and the data of the sodium-exposed specimens were compared with the thermal aging data of the same heat to isolate the thermal aging effect from the effect of sodium exposure. It was found that the tensile strength of G91 steel can be reduced by more than 50% after sodium exposures at 650°C. The effect of a sodium environment on tensile properties is largely dependent on the carburization/decarburization behavior of G91 steel exposed to sodium. The carbon concentrations in sodium in Argonne’s SMT-1 and SMT-2 loops were determined by the equilibration method. The carbon activity in sodium was established by equilibrating high-purity nickel in sodium, analyzing the material for carbon, and using the reported data on the carbon solubility for this material. The carbon activity results were combined with the carbon solubility data in sodium to establish the carbon concentration in sodium. The carbon concentrations in the SMT-1 and SMT-2 loop were estimated to be 1.23 and 0.25 ppm, respectively. With this initial success, we will continue to monitor the carbon contents in the two loops to correlate the microstructural and mechanical property changes with the sodium purity. Future experiments will also consider sodium exposure tests in controlled carbon activities. Online monitoring and control of carbon contents in sodium in nuclear reactors would also be of interest. Thermodynamic analysis was conducted to understand the carburization-decarburization behavior of G91 steel exposed to sodium in the SMT-1 and SMT-2 loops. The equilibrium carbon activity in the alloy was evaluated by the thermodynamics of M 23 C 6 carbides. The calculated carburization-decarburization boundary showed that G91 would undergo decarburization at 650°C in the SMT-1 loop and carburization at 600°C in the SMT-2 loop, which is consistent with our findings from the sodium exposure tests. Future work will include thermodynamic analysis of the carbon concentration – activity relationship including the effect of carbide-forming elements, vanadium and niobium in G91 steel. Kinetics of carbon diffusion and the effect on microstructure and mechanical performance under various service conditions will also be investigated. The ultimate goal is to understand the mechanisms and the kinetics of carbon transfer in the sodium-steel system and to provide a basis for predicting the effect of long-term decarburization-carburization process on the integrity of reactor components.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗

DOE OSTI2019

Planned FY19 Sodium Compatibility Testing of Grade 91 Steel

This report provides an update on the understanding of the effect of sodium exposures on microstructure and tensile properties of Grade 91 (G91) steel in support of the design and operation of G91 components in sodium-cooled fast reactors (SFRs). The report is a Level 2 deliverable in FY19 (M2AT- 19AN020503011), under the Work Package AT-19AN02050301, “G91 Sodium Compatibility - ANL”, as part of the Advanced Materials Development Program for Fast Reactors.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗