Single crystal growth and characterization of new Zintl phase Ca 9 Zn 3.1 In 0.9 Sb 9
Complex Zintl phases have yielded a large variety of promising new thermoelectric materials. Here we report the discovery of the new Zintl phase Ca 9 (Zn 1– x In x ) 4 Sb 9 ( x ~ 0.9), needle-like crystals of which were serendipitously obtained from an In- and Sb-rich flux. Although its composition is reminiscent of Ca 9 Zn 4+ x Sb 9 , an excellent thermoelectric material with zT > 1, the substitution of In on the Zn site leads to the formation of an entirely new structure type. Single crystal X-ray diffraction revealed a structure characterized by T Sb 4 tetrahedra ( T = statistically disordered Zn and In atoms) and ZnSb 3 triangular units, which share common corners to form [ T 4 Sb 9 ] 18– polyanions. The average structure was found to have hexagonal symmetry. The valence electron count in this heavily-disordered structure appears to follows the Zintl-Klemm rules, suggesting semiconducting behavior. Single crystal electrical conductivity and Seebeck coefficient measurements support this conclusion, suggesting that the as-grown crystals are degenerate p -type semiconductors.