Zhang, Bao

Publications and source records attributed to Zhang, Bao.

9 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Surface Atomic Rearrangement with High Cation Ordering for Ultra-Stable Single-Crystal Ni-Rich Co-Less Cathode Materials

It is crucial to minimize cobalt content in Ni-rich layered single-crystal cathodes due to their high price and limited availability, yet it will inevitably lead to cation disordering, capacity degradation, and thermal issues. Herein, to overcome the intrinsic trade-off between performance and composition of Ni-rich Co-less single-crystal cathodes, a precursor engineering strategy with an epitaxially grown cobalt enrichment on the surface is innovatively proposed. In contrast to traditional coating modifications with random orientation and rigid surface-bulk boundary, the epitaxially enriched surface cobalt layer on the precursor undergoes rapid interdiffusion with the internal Ni 3+ during the optimized sintering process. This interdiffusion eliminates the surface-bulk boundary, promoting the uniform distribution of cobalt and synergistically addressing the Li/Ni intermixing. Moreover, an enhanced surface Li + diffusion is obtained, thereby suppressing the Li + concentration gradient and intragranular cracks generation. Consequently, the modified LiNi 0.7 Co 0.07 Mn 0.23 O 2 exhibits impressive cycling stability with increased capacity retention in both coin-type half-cells and pouch-type full-cells (91% after 1000 cycles), even under the harsh condition of high-temperature, surpassing the majority of previously reported Ni-rich cathodes. Finally, this work opens new avenues toward the low cost, high energy density, thermal stability, and long cyclic life for Ni-rich Co-less cathodes and sheds light on large-scale commercial production.

25 ENERGY STORAGE↗
DOE OSTI2024

NaSICON-type materials for lithium-ion battery applications: Progress and challenges

Lithium-ion batteries (LIBs) are widely used in electric vehicles, energy storage, smart grids, and portable devices due to their high average output voltage and energy density. NaSICON-type materials have been identified as potential candidates for electrode and solid electrolyte materials for LIBs due to their 3D framework, which contains Li + ions, excellent ionic conductivity, and thermal stability. NaSICON-type materials have a 3D framework and a fast Li + diffusion pathway, making them suitable for use in LIBs. However, their application as solid electrolytes is limited due to poorer ionic conductivity and interfacial stability compared to commercialized liquid electrolytes. Furthermore, their use as electrode materials is restricted by their low electronic conductivity. Here, this review provides an overview of NaSICON-type materials, including their common structure, Li + diffusion mechanism, and preparation strategies. The article also discusses the application and modification strategies of NaSICON-type materials for LIBs, classifying them as anode materials, cathode materials, and solid electrolyte materials. Additionally, the potential use of NaSICON-type materials as modification materials for cathode materials for LIBs is briefly mentioned. Building on previous work on NaSICON-type materials, we propose potential areas for further development and wider applications of these materials in LIBs.

25 ENERGY STORAGE↗
DOE OSTI2024

Optimized In Situ Doping Strategy Stabling Single-Crystal Ultrahigh-Nickel Layered Cathode Materials

Single-crystal Ni-rich cathodes offer promising prospects in mitigating intergranular microcracks and side reaction issues commonly encountered in conventional polycrystalline cathodes. However, the utilization of micrometer-sized single-crystal particles has raised concerns about sluggish Li + diffusion kinetics and unfavorable structural degradation, particularly in high Ni content cathodes. Herein, we present an innovative in situ doping strategy to regulate the dominant growth of characteristic planes in the singlecrystal precursor, leading to enhanced mechanical properties and effectively tackling the challenges posed by ultrahigh-nickel layered cathodes. Compared with the traditional dry-doping method, our in situ doping approach possesses a more homogeneous and consistent modifying effect from the inside out, ensuring the uniform distribution of doping ions with large radius (Nb, Zr, W, etc). Further, this mitigates the generally unsatisfactory substitution effect, thereby minimizing undesirable coating layers induced by different solubilities during the calcination process. Additionally, the uniformly dispersed ions from this in situ doping are beneficial for alleviating the two-phase coexistence of H2/H3 and optimizing the Li + concentration gradient during cycling, thus inhibiting the formation of intragranular cracks and interfacial deterioration. Consequently, the in situ doped cathodes demonstrate exceptional cycle retention and rate performance under various harsh testing conditions. Our optimized in situ doping strategy not only expands the application prospects of elemental doping but also offers a promising research direction for developing high-energy-density single-crystal cathodes with extended lifetime.

25 ENERGY STORAGE↗
DOE OSTI2023

Interface Design for High‐Performance All‐Solid‐State Lithium Batteries

All‐solid‐state batteries suffer from high interface resistance and lithium dendrite growth leading to low Li plating/stripping Coulombic efficiency (CE) of <90% and low critical current density at high capacity. Here, in this work, both challenges are simultaneously addressed and the Li plating/stripping CE is significantly increased to 99.6% at 0.2 mA cm −2 /0.2 mAh cm −2 , and critical current density (CCD) of > 3.0 mA cm −2 /3.0 mAh cm −2 by inserting a mixed ionic‐electronic conductive (MIEC) and lithiophobic LiF‐C‐Li 3 N‐Bi nanocomposite interlayer between Li 6 PS 5 Cl electrolyte and Li anode. The highly lithiophobic LiF‐C‐Li 3 N‐Bi interlayer with high ionic conductivity (10 −5 S cm −1 ) and low electronic conductivity (3.4×10 −7 S cm −1 ) enables Li to plate on the current collector (CC) surface rather than on Li 6 PS 5 Cl surface avoiding Li 6 PS 5 Cl electrolyte reduction. During initial Li plating on CC, Li penetrates into porous LiF‐C‐Li 3 N‐Bi interlayer and lithiates Bi nanoparticles into Li 3 Bi. The lithiophilic Li 3 Bi and Li 3 N nanoparticles in LiF‐C‐Li 3 N‐Li 3 Bi sub‐interlayer will move to CC along with plated Li, forming LiF‐C/Li 3 N‐Li 3 Bi lithiophobic/lithiophilic sublayer during the following Li stripping. This interlayer enables Co 0.1 Fe 0.9 S 2 /Li 6 PS 5 Cl/Li cell with an areal capacity of 1.4 mAh cm −2 to achieve a cycle life of >850 cycles at 150 mA g −1 . The lithiophobic/lithiophilic interlayer enables solid‐state metal batteries to simultaneously achieve high energy and long cycle life.

25 ENERGY STORAGE↗
DOE OSTI2023

Achieving Thermodynamic Stability of Single-Crystal Co-Free Ni-Rich Cathode Material for High Voltage Lithium-Ion Batteries

Ni-rich layered cathode materials are progressively considered as the standard configuration of high-energy electric vehicles by virtues of their high capacity and eliminated “range anxiety.” However, the poor cyclic stability and severe cobalt supply crisis would restrain their wide commercial applicability. Here, a cost-effective single-crystal Co-free Ni-rich cathode material LiNi 0.8 Mn 0.18 Fe 0.02 O 2 (NMF), which outperforms widely commercial polycrystalline LiNi 0.83 Co 0.11 Mn 0.06 O 2 (MNCM) and single-crystal LiNi 0.83 Co 0.11 Mn 0.06 O 2 (SNCM) is reported. Surprisingly, NMF can compensate for the reversible capacity loss under the designed conditions of high-temperature and elevated-voltage, achieving a competitive energy density compared with conventional MNCM or SNCM. Further, combining operando characterizations and density functional theory calculation, it is revealed that NMF cathode with improved dynamic structure evolution largely alleviates the mechanical strain issue commonly found in Ni-rich cathode, which can reduce the formation of intragranular cracks and improve the safety performance. Consequently, this new Co-free NMF cathode can achieve a perfect equilibrium between material cost and electrochemical performance, which not only reduces the production cost by >15%, but also demonstrates excellent thermal stability and cycling performance.

25 ENERGY STORAGE↗
DOE OSTI2023

Constructing stable interface layer for boosting high-voltage cycling performance of single-crystal Ni-rich cathodes

Increasing demand for electric vehicles (EVs) worldwide and the requirements for environmental protection have greatly promoted the development of low-Co, Ni-rich layered cathodes due to their high energy density, reasonable cost, and less environmental pollution. Nevertheless, serious performance degradation and safety concerns resulting from structural/interfacial instability under high operating voltages (≥4.3 V) have greatly hindered its commercialization. Herein, we propose a feasible surface modification strategy by introducing a multifunctional Li 2 SiO 3 (LSO) coating layer onto the surface of Co less single-crystalline LiNi 0.63 Co 0.07 Mn 0.3 O 2 (NCM) to solve the above challenges. Additionally, the uniform Li 2 SiO 3 coating layer has a unique three-dimensional (3D) ion diffusion channel, which greatly promotes the transmission of Li + and alleviates interfacial stress accumulation. Equally important, the electrochemically inert Li 2 SiO 3 coating layer has a stable structure framework with strong Si-O bonds, which inhibit anisotropic particle volume expansion and the occurrence of side reactions during long-term cycling. As a consequence, LSO modified NCM exhibits greatly improved electrochemical properties even at harsh testing conditions and achieves capacity retention of 79.1% after 200 cycles at 25°C within 2.95-4.5 V in half cells. Furthermore, it provides an outstanding capacity retention of 94.7% after 300 cycles at 25°C within 2.95-4.4 V when tested in pouch full cells.

25 ENERGY STORAGE↗
DOE OSTI2022

Enabling high energy lithium metal batteries via single-crystal Ni-rich cathode material co-doping strategy

High-capacity Ni-rich layered oxides are promising cathode materials for secondary lithium-based battery systems. However, their structural instability detrimentally affects the battery performance during cell cycling. Here, we report an Al/Zr co-doped single-crystalline LiNi<:sub>0.88 Co 0.09 Mn 0.03 O 2 (SNCM) cathode material to circumvent the instability issue. We found that soluble Al ions are adequately incorporated in the SNCM lattice while the less soluble Zr ions are prone to aggregate in the outer SNCM surface layer. The synergistic effect of Al/Zr co-doping in SNCM lattice improve the Li-ion mobility, relief the internal strain, and suppress the Li/Ni cation mixing upon cycling at high cut-off voltage. These features improve the cathode rate capability and structural stabilization during prolonged cell cycling. In particular, the Zr-rich surface enables the formation of stable cathode-electrolyte interphase, which prevent SNCM from unwanted reactions with the non-aqueous fluorinated liquid electrolyte solution and avoid Ni dissolution. To prove the practical application of the Al/Zr co-doped SNCM, we assembled a 10.8 Ah pouch cell (using a 100 μm thick Li metal anode) capable of delivering initial specific energy of 504.5 Wh kg- 1 at 0.1 °C and 25 °C.

25 ENERGY STORAGE↗