Ion irradiation induced strain and structural changes in LiTaO 3 perovskite
LiTaO 3 crystals irradiated with 3 MeV and 1.162 GeV Au ions were studied by single crystal x-ray diffraction and Raman scattering measurements. The maximum lattice strains after 3 MeV Au ion irradiation to a fluence of 1.2 × 10 13 cm -2 were 1.2% and 0.6% along the c- and a-/b-axes, respectively. Two effects were observed in 1.162 GeV Au ion irradiated samples: (i) the (0006) and (1120) Bragg peaks were split into doublets, which suggested a subtle structural change due to slight modification of chemical composition; and (ii) the pre-damaged 1.2% lattice strain along the c-axis was relaxed to 0.9% after subsequent irradiation with 1.162 GeV Au ions, while relaxation along the a- or b-axis was not obvious. A distinct change in the Raman spectrum of the <0001> oriented LiTaO 3 crystals was observed after 1.162 GeV Au ion irradiation, but no obvious change was observed in the <1120> oriented samples or in 3 MeV Au ion irradiated samples. Strain and structural changes in crystalline LiTaO3, with or without pre-existing defects, upon ion irradiation are delineated in its responding to inelastic ionization and elastic nuclear collisions.