Search NASA⌕ Search

Engineering topics

Zhang, Hengzhong

Publications and source records attributed to Zhang, Hengzhong.

Pressure-induced suppression of Jahn–Teller distortions and enhanced electronic properties in high-entropy oxide (Mg 0.2 Ni 0.2 Co 0.2 Zn 0.2 Cu 0.2 )O

Jahn–Teller distortions are often observed in Cu II -containing complex oxides resulting in remarkable changes of physical properties. Tuning the Jahn–Teller distortions with pressure has attracted considerable interest but is less studied in Cu II -containing high-entropy oxides (HEOs). We found that pressure can suppress the structural distortions originating from the Jahn–Teller effect of CuO 6 octahedra in the rock salt-type (Mg 0.2 Ni 0.2 Co 0.2 Zn 0.2 Cu 0.2 )O HEO and significantly modify its electronic properties. Synchrotron x-ray diffraction shows that the structural distortions arising from the Jahn–Teller effect of CuO 6 octahedra are progressively suppressed, and the distorted structure evolves into a nearly ideal form under compression. Alternating current impedance and ultraviolet-visible absorption measurements reveal a dramatic resistance drop by more than three orders of magnitude and an obvious bandgap decrease in ~0.1 eV, respectively, accompanied by the pressure-induced suppression of structural distortions. Our study presents a promising route for tuning the structural distortions and the electronic structures of Cu II -containing HEOs for optimizing materials functionalities.

36 MATERIALS SCIENCE↗

High-pressure strengthening in ultrafine-grained metals

The Hall–Petch relationship, according to which the strength of a metal increases as the grain size decreases, has been reported to break down at a critical grain size of around 10 to 15 nanometres. As the grain size decreases beyond this point, the dominant mechanism of deformation switches from a dislocation-mediated process to grain boundary sliding, leading to material softening. In one previous approach, stabilization of grain boundaries through relaxation and molybdenum segregation was used to prevent this softening effect in nickel–molybdenum alloys with grain sizes below 10 nanometres. Here we track in situ the yield stress and deformation texturing of pure nickel samples of various average grain sizes using a diamond anvil cell coupled with radial X-ray diffraction. Our high-pressure experiments reveal continuous strengthening in samples with grain sizes from 200 nanometres down to 3 nanometres, with the strengthening enhanced (rather than reduced) at grain sizes smaller than 20 nanometres. Here, we achieve a yield strength of approximately 4.2 gigapascals in our 3-nanometre-grain-size samples, ten times stronger than that of a commercial nickel material. A maximum flow stress of 10.2 gigapascals is obtained in nickel of grain size 3 nanometres for the pressure range studied here. We see similar patterns of compression strengthening in gold and palladium samples down to the smallest grain sizes. Simulations and transmission electron microscopy reveal that the high strength observed in nickel of grain size 3 nanometres is caused by the superposition of strengthening mechanisms: both partial and full dislocation hardening plus suppression of grain boundary plasticity. These insights contribute the ongoing search for ultrastrong metals via materials engineering.

36 MATERIALS SCIENCE↗