Rapid Open-Air Fabrication of Stable Perovskite Solar Modules
Open-air plama processing for large-area solar modules
Rolston, Nicholas↗
Engineering topics
Zhang, Jinbao
Publications and source records attributed to Zhang, Jinbao.
Low-temperature sprayed SnO x nanocomposite films with enhanced hole blocking for efficient large area perovskite solar cells
Scalable fabrication of charge transport layers with high uniformity and compactness is essential for the commercialization of perovskite solar cells (PSCs). Cost-effective deposition of high-quality electron transport layers (ETLs) is a particularly important step to achieve low-cost, efficient and large-area PSCs. Here, an open-air (relative humidity of 40–50%) and low-temperature (≤100 °C) ultrasonic spray coating of tin oxide (SnO 2 ) nanocomposite films incorporating nanocrystalline SnO 2 nanoparticles in an amorphous SnO x matrix is demonstrated to fabricate large-area ETLs for planar PSCs. The optimized SnO 2 /SnO x nanocomposite exhibits significantly enhanced hole-blocking and high-power conversion efficiencies of 18% and 16% for planar PSCs with an active area of 0.2 cm 2 and 1 cm 2 , respectively. More importantly, the devices show little current–voltage hysteresis as well as good shelf-life stability by maintaining ~90% of the initial performance without encapsulation after 2500 hours storage under inert conditions. Additionally, high voltages of >6.0 V have been obtained for solar modules of 2.1 cm 2 aperture area comprising six sub-cells in series, suggesting that the low-temperature, open-air and fast spray coating is suitable and transferable to deposit large-area charge transport layers for scalable PSCs or other optoelectronic devices.
32 ENERGY CONSERVATION, CONSUMPTION, AND UTILIZATI↗
Low temperature open-air plasma deposition of amorphous tin oxide for perovskite solar cells
Not provided.
Materials Science↗
Accelerated Scaling to Rapid Open-Air Fabrication of Durable Perovskite Solar Modules
By using an ultra-fast scalable open-air plasma deposition technique to deposit the perovskite layer and combining that with monolithic scribing, we are able to achieve high efficiency and large area perovskite solar modules.
Rolston, Nicholas↗
Perspectives on intrinsic toughening strategies and passivation of perovskite films with organic additives
We report on the inclusion of 5-aminovaleric acid (5-AVA)—a bulky, long-chained organic molecule—as an additive to enhance the mechanical integrity of hybrid perovskite films. We studied a range of organic cation additives and found that 5-AVA was the most effective at improving cohesion energy, a key metric of mechanical reliability. MAPbI 3 films reinforced with 5-AVA added in 5% concentration increased cohesion energy 12-fold from 0.53 J/m 2 to 6.04 J/m 2 , an effect which is attributed to increased plasticity and crack deflection around grain boundaries of the additive-containing perovskite. The addition of 5-AVA also improves V oc in perovskite solar cells and carrier lifetimes with a minimal decrease in PCE, attributed to passivation reducing defect and trap densities. A Tauc plot analysis of the bandgap shows that 5-AVA increases the band gap of the perovskite, correlating with reduced film stress compared to MAPbI 3 . Finally, the usage of 5-AVA improves the intrinsic thermomechanical reliability, but this improvement comes at the penalty of slightly reduced device efficiency due to reduced charge extraction from the presence of the bulky, insulating organic additive.
14 SOLAR ENERGY↗