Additive manufacturing enabled synergetic strengthening of bimodal reinforcing particles for aluminum matrix composites
An additive manufactured TiB 2 /Al-Cu-Mg-Ni composite with a minor amount of Sc was fabricated by laser powder bed fusion (LPBF). The composite shows a yield strength of ~370 MPa, almost doubling the strength of its wrought matrix counterpart, and an elongation of ~7 %. The superior mechanical properties are attributed to a unique micro-nano hierarchical microstructure, consisting of nanoscale and microscale TiB 2 particles dispersed in a matrix of fine aluminum grains (3 µm) together with intragranular intermetallic nanoparticles and nano-cellular networks (cell size 30 nm). The formation of the TiB 2 nanoparticles is the consequence of partial dissolution of the TiB 2 particulates and the enrichment of Sc in the newly formed nanoparticles. Remarkable strengthening effects are achieved by the bimodal TiB 2 particles, intermetallic nanoparticles and intragranular nano-cellular networks. Finally, this study provides new insights into the role of additive manufacturing in tailoring the microstructure of particulate reinforced metal matrix composites (MMCs) with advanced properties.