Lithium metal negative electrode and method of manufacturing the same

A negative electrode for an electrochemical cell of a secondary lithium metal battery is manufactured by a method in which a precursor solution is applied to a major surface of a lithium metal substrate to form a precursor coating thereon. The precursor solution includes an organophosphate, a nonpolar organic solvent, and a lithium-containing inorganic ionic compound dissolved therein. At least a portion of the nonpolar organic solvent is removed from the precursor coating to form a protective interfacial layer on the major surface of the lithium metal substrate. The protective interfacial layer exhibits a composite structure including a carbon-based matrix component and a lithium-containing dispersed component. The lithium-containing dispersed component is embedded in the carbon-based matrix component and includes a plurality of lithium-containing inorganic ionic compounds, e.g., lithium phosphate (Li3PO4) and lithium nitrate (LiNO3).

Xiao, Xingcheng↗
DOE OSTI2022

Consolidation of composite cathodes with NCM and sulfide solid-state electrolytes by hot pressing for all-solid-state Li metal batteries

In this study, hot pressing was evaluated as a method of cell fabrication to increase the energy density of next-generation all-solid-state batteries with NCM active material and sulfide solid-state electrolyte. Hot pressing involves consolidating glassy sulfide electrolyte by the application of pressure at a temperature above the electrolyte’s glass transition temperature. Typically, cell stacks are formed at room temperature and retain 15–30% porosity that limits cell energy density. On the other hand, the porosity of hot-pressed cell stacks is reduced to less than 10%. The electrochemical function of hot-pressed cathode composites was assessed as a function of active material and solid-state electrolyte compositions. Specifically, LiNi 0.85 Co 0.10 Mn 0.05 O 2 and LiNi 0.6 Co 0.2 Mn 0.2 O 2 were studied in combination with either glassy Li 7 P 3 S 11 , glassy Li 3 PS 4 , or β-Li 3 PS 4 solid-state electrolytes. Cathode composites composed of LiNi 0.6 Co 0.2 Mn 0.2 O 2 and Li 3 PS 4 maintained the best function after hot pressing at 200 °C and 370 MPa for 10 min. It was found that LiNi 0.6 Co 0.2 Mn 0.2 O 2 ’s resistance to microcracking and the inherent stability of Li 3 PS 4 ’s fully de-networked local structure are critical to maintain good electrochemical function after hot pressing. Furthermore, the results of this study show that hot pressing reduces porosity in the cathode composite and confirms the feasibility of cathode support of consolidated, reinforced glass separators.

25 ENERGY STORAGE↗