DOE OSTI2021

Positive Role of Fluorine Impurity in Recovered LiNi 0.6 Co 0.2 Mn 0.2 O 2 Cathode Materials

Lithium-ion battery (LIB) recycling is considered as an important component to enable industry sustainability. A massive number of LIBs in portable electronics, electric vehicles, and grid storage will eventually end up as wastes, leading to serious economic and environmental problems. Hence, tremendous efforts have been made to improve the hydrometallurgical recycling process because it is the most promising option for handling end-of-life LIBs owing to its wide applicability, low cost, and high productivity. Despite these advantages, some extra elements (Al, Fe, C, F, and so forth) remain as impurities in the removal process and are retained in the solution, which is a great challenge to obtain high-quality cathode materials. In this work, the impacts caused by fluorine impurity on the LiNi 0.6 Co 0.2 Mn 0.2 O 2 (NCM622) cathode are intensively investigated via hydrometallurgical coprecipitation for the first time. Our results show that up to 1 at. % fluorine impurity brings a positive influence on the recovered material due to a higher Ni 2+ ratio on the surface of cathode particles. In addition, the presence of fluoride ions during coprecipitation could lead to the formation of holes in cathode particles, which improves the rate capability and cyclability dramatically. Compared to the virgin material, the capacity of the NCM622 material with 0.2 at. % fluorine impurity is boosted by ~8% (167.7 mA h/g) with a remarkable capacity retention of 98.0% after 100 cycles at 0.33 C. Besides, the cathode with 0.2 at. % fluorine impurity shows a far better rate performance, especially at high rates (~7% increased at 5 C) than that of virgin. Furthermore, these results convince that a low concentration of fluorine impurity is desirable in the hydrometallurgical recycling process. More importantly, this study offers implications in the design of high-performance NCM622 cathode materials via coprecipitation production with ion doping in the near future.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

Building a spontaneously formed and self-healing protective layer with an F-rich electrochemically active organic molecule for ultra-stable Li metal batteries

Additives in the electrolyte act as engineers in Li metal batteries. Inspired by the superior cycle performance of organic materials in half cells, tetrafluoro-1,4-benzoquinone (TFBQ), the main structure of which has been widely applied as an organic cathode material, is utilized for the first time as an additive for Li metal protection. By chemical and electrochemical reactions between TFBQ and the Li metal surface, an F-rich interface layer is in situ formed on the Li metal surface during the charge and discharge process. From electrochemical tests and characterization, the powerful self-healing ability of the interface layer enabled by TFBQ is revealed, making an extremely stable Li metal anode. By using a lean electrolyte with 0.1 M TFBQ, the cycle life of Li|Li symmetric cells is increased at least 6 times compared to the control group. Moreover, impressive full cell performance was achieved. Ultra-stable Li–LFP cells showed a 0.026% average degradation for 600 cycles at 1C and Li–NMC622 cells showed a 36.8% higher capacity compared to the control group over 200 cycles at 0.5C, which are among the best results reported. Furthermore, this work efficiently and conveniently provides a new research direction to Li metal protection and Li metal batteries.

25 ENERGY STORAGE↗

DOE OSTI2021

Valence Effects of Fe Impurity for Recovered LiNi 0.6 Co 0.2 Mn 0.2 O 2 Cathode Materials

Iron impurities are generally included in the obtained leaching liquor solution during the hydrometallurgical recycling method of spent lithium-ion batteries (LIBs) due to the usage of iron in battery casings and machinery parts of recycling equipment, which would definitely affect the physical and electrochemical features of the recovered active materials. In this paper, the effects of iron impurity with different valence states (Fe 2+ and Fe 3+ ) and gradient concentrations (0.2, 1.0, and 5.0 at. %) for the obtained LiNi 0.6 Co 0.2 Mn 0.2 O 2 (NCM622) cathodes are fully studied. It is found that Fe3+ impurity could easily lower the tap density and average size of NCM622 particles and even introduce some impurity phases in the NCM622 structure at high concentration (5.0 at. %), leading to much lower specific capacity, worse rate capability, and cycling performance of the Fe 3+ -based NCM622 cathode. On contrast, with certain concentrations of Fe 2+ impurity (0.2 and 1.0 at. %), the NCM622 cathode material exhibits comparable and much better electrochemical properties compared with the virgin NCM622 materials. Based on these results, the valence of Fe impurity should be considered and controlled as well as its concentration during the recycling process design for spent LIBs.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

A universal etching method for synthesizing high-performance single crystal cathode materials

LiNi x MnyCo 1-x-y O 2 (NMC) is considered the most appealing cathode material due to its high energy density and low cost. However, the stability and safety concerns, caused by the degradation of polycrystalline cathode materials during cycling, have restricted their practical applications. To overcome this shortcoming, converting polycrystalline cathode to high-performance single-crystal cathode materials becomes an appealing solution. In this work, a universal etching approach is firstly developed to synthesize single-crystal cathode materials. The rate performance of the obtained single-crystal NMC111 is 10–15% more than that of polycrystalline NMC111 whereas the capacity retention of single-crystal NMC111 is enhanced by ~12% after 300 cycles at 0.5C. The obtained single-crystal NMC622 exhibits a pronounced improvement in rate performance, especially at high rates (~28.6% better at 5C and ~129% better at 10C) and has a comparable cycle performance compared to polycrystalline NMC622. Altogether, the findings propose an alternative approach to generate single-crystal particles with high energy density and cycle stability for the next generation lithium-ion batteries.

25 ENERGY STORAGE↗

DOE OSTI2021

Unveiling the Influence of Carbon Impurity on Recovered NCM622 Cathode Material

With the proliferation of market demand for lithium-ion batteries (LIBs) over the past decades, battery recycling has aroused extensive attention due to the environmental, supply, and economic issues caused by waste batteries. Here, the hydrometallurgical recycling method has been widely adopted to recover cathode materials as a result of its wide applicability and high productivity. However, it is hard to completely eliminate impurities such as copper, aluminum, and carbon, which could bring significant impacts on recovered materials. Here, the influence of the carbon impurity on recovered LiNi 0.6 Co 0.2 Mn 0.2 O 2 (NCM622) cathode material is systematically investigated. It shows that the carbon impurity promotes nucleation during coprecipitation and forms holes in the cathode secondary particles after sintering which could enhance cyclability of the NCM622 cathode. The cathode with 0.2 atom % of carbon impurity displays the highest capacity of 159.9 mAh/g with a striking capacity retention rate of 97.9% after 100 cycles at 0.33C, but performs worse at high rates. Nonetheless, excess carbon (5 atom %) results in severe cation disorder and lattice distortion which significantly deteriorates the electrochemical properties of the NCM622 cathode. Therefore, it is important to strictly control carbon impurity during the recycling process for spent LIBs.

25 ENERGY STORAGE↗

DOE OSTI2020

Metal oxide supported Ni-impregnated bifunctional catalysts for controlling char formation and maximizing energy recovery during catalytic hydrothermal liquefaction of food waste

Nickel (Ni)-impregnated metal oxide catalysts, Ni/CeZrO x , Ni/ZrO 2 , and Ni/CeO 2 , were investigated to maximize energy recovery and reduce char yield during catalytic hydrothermal liquefaction (CHTL) of food waste. Yields of char, biocrude, water soluble products, and gas were measured at 300 °C and 1 hour for both the parent oxides (CeZrO x , ZrO 2 , and CeO 2 ) and the Ni-impregnated versions. Using Ni-based catalysts reduced the carbon-weighted char yield from 16–24% to <10% and decreased the energy recovery of char from 39–47% to <21%, as compared with control tests. In particular, using Ni/ZrO 2 resulted in the greatest biocrude yield, greatest reduction of char yield, and greatest energy recovered as biocrude (39.2%). After factoring in all forms of usable energy produced from food waste, the total energy recovery obtained for the catalysts studied here was >60%. Ni/ZrO 2 and Ni/CeO 2 show the greatest potential for controlling char growth and maximizing energy recovered from food waste. The crystalline structures of all three oxides were hydrothermally stable. Catalyst reuse tests indicate that the biocrude and char yields remained the same for the first and second use (within uncertainty) and that the catalyst retains its initial crystallinity and 93% of its initial Ni content. Molecular composition of biocrudes analyzed by the state-of-the-art analytical platforms (including GC-MS, GC × GC, FT-ICR MS, and 1H NMR) revealed minor differences in the chemical constituents of biocrudes obtained using different catalysts and provided some insight regarding reaction mechanism.

09 BIOMASS FUELS↗