Engineering topics

Zhang, Xuanyi

Publications and source records attributed to Zhang, Xuanyi.

6 records

DOE OSTI2024

Tuning the interlayer coupling in La 0.7 Sr 0.3 Mn 0.95 Ru 0.05 O 3 / LaNiO 3 multilayers with perpendicular magnetic anisotropy

In ferromagnetic oxide epitaxial multilayers, magnetic properties and interlayer coupling are determined by a variety of factors. Beyond the contribution of interlayer exchange coupling, strain and interfacial effects, such as structural reconstructions or charge transfer, play significant roles, resulting in complex magnetic behavior. In this study, the interlayer coupling of ferromagnetic La 0.7 ⁢Sr 0.3⁢ Mn 0.95 ⁢Ru 0.05 ⁢O 3 (LSMRO) layers (8 nm thick) was investigated, when separated by epitaxial spacers of paramagnetic metallic LaNiO 3 (LNO), in stacks exhibiting perpendicular magnetic anisotropy. By varying the thickness of the spacer, it was found that the coupling between two LSMRO layers changes from antiferromagnetic (with a 4-unit-cell-thick LNO spacer) to ferromagnetic (with a 6-unit-cell-thick LNO spacer). For multilayers comprising five LSMRO layers and a 4-unit-cell-thick LNO spacer, the antiferromagnetic coupling was preserved. However, the effective magnetic anisotropy changed, causing the magnetization to cant more towards the in-plane direction. Further, this behavior was corroborated by X-ray magnetic circular dichroism (XMCD) investigations at the Mn and Ni L 3 edges. The XMCD results indicated that the 4-unit-cell-thick LNO spacer in the multilayer become magnetically ordered, closely following the magnetization of adjacent LSMRO layers.

36 MATERIALS SCIENCE↗

DOE OSTI2024

The Role of Interfacial Interactions and Oxygen Vacancies in Tuning Magnetic Anisotropy in LaCrO 3 /LaMnO 3 Heterostructures

The interplay of lattice, electronic, and spin degrees of freedom at epitaxial complex oxide interfaces provides a route to tune their magnetic ground states. Unraveling the competing contributions is critical for tuning their functional properties. The relationship between magnetic ordering and magnetic anisotropy and the lattice symmetry, oxygen content, and film thickness in compressively strained LaMnO 3 (LMO)/LaCrO 3 (LCO) superlattices is investigated. Mn–O–Cr antiferromagnetic superexchange interactions across the heterointerface result in a net ferrimagnetic magnetic structure. Bulk magnetometry measurements reveal isotropic in-plane magnetism for as-grown oxygen-deficient thin samples due to equal fractions of orthorhombic a+a-c-, and a-a+c- twin domains. As the superlattice thickness is increased, in-plane magnetic anisotropy emerges as the fraction of the a+a-c- domain increases. On annealing in oxygen, the suppression of oxygen vacancies results in a contraction of the lattice volume, and an orthorhombic to rhombohedral transition leads to isotropic magnetism independent of the film thickness. The complex interactions are investigated using high-resolution synchrotron diffraction and X-ray absorption spectroscopy. These results highlight the role of the evolution of structural domains with film thickness, interfacial spin interactions, and oxygen-vacancy-induced structural phase transitions in tuning the magnetic properties of complex oxide heterostructures.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Thickness-Dependent Thermal Conductivity and Phonon Mean Free Path Distribution in Single-Crystalline Barium Titanate

Nanosized perovskite ferroelectrics are widely employed in several electromechanical, photonics, and thermoelectric applications. Scaling of ferroelectric materials entails a severe reduction in the lattice (phonon) thermal conductivity, particularly at sub-100 nm length scales. Such thermal conductivity reduction can be accurately predicted using the information of phonon mean free path (MFP) distribution. The current understanding of phonon MFP distribution in perovskite ferroelectrics is still inconclusive despite the critical thermal management implications. Here, high-quality single-crystalline barium titanate (BTO) thin films, a representative perovskite ferroelectric material, are grown at several thicknesses. Using experimental thermal conductivity measurements and first-principles based modeling (including four-phonon scattering), the phonon MFP distribution is determined in BTO. The simulation results agree with the measured thickness-dependent thermal conductivity. The results show that the phonons with sub-100 nm MFP dominate the thermal transport in BTO, and phonons with MFP exceeding 10 nm contribute ≈35% to the total thermal conductivity, in significant contrast to previously published experimental results. The experimentally validated phonon MFP distribution is consistent with the theoretical predictions of other complex crystals with strong anharmonicity. This work paves the way for thermal management in nanostructured and ferroelectric-domain-engineered systems for oxide perovskite-based functional materials.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Ferroelectric Domain Wall Engineering Enables Thermal Modulation in PMN–PT Single Crystals

Acting like thermal resistances, ferroelectric domain walls can be manipulated to realize dynamic modulation of thermal conductivity ( k ), which is essential for developing novel phononic circuits. Despite the interest, little attention has been paid to achieving room-temperature thermal modulation in bulk materials due to challenges in obtaining a high thermal conductivity switching ratio ( k high / k low ), particularly in commercially viable materials. Here, room-temperature thermal modulation in 2.5 mm-thick Pb(Mg 1/3 Nb 2/3 )O 3 – x PbTiO 3 (PMN– x PT) single crystals is demonstrated. With the use of advanced poling conditions, assisted by the systematic study on composition and orientation dependence of PMN– x PT, a range of thermal conductivity switching ratios with a maximum of ≈1.27 is observed. Further, simultaneous measurements of piezoelectric coefficient (d 33 ) to characterize the poling state, domain wall density using polarized light microscopy (PLM), and birefringence change using quantitative PLM reveal that compared to the unpoled state, the domain wall density at intermediate poling states (0< d 33 33,max ) is lower due to the enlargement in domain size. At optimized poling conditions (d 33,max ), the domain sizes show increased inhomogeneity that leads to enhancement in the domain wall density. This work highlights the potential of commercially available PMN– x PT single crystals among other relaxor-ferroelectrics for achieving temperature control in solid-state devices.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Superconducting phase of Ti x O y thin films grown by molecular beam epitaxy

Here we investigate the complex relationship between the growth conditions and the structural and transport properties of Ti x O y thin films grown by molecular beam epitaxy. Transport properties ranging from metallicity to superconductivity and insulating states are stabilized by effectively tuning the O/Ti ratio via the Ti flux rate and the O partial pressure P Ox for films grown on (0001)-Al 2 O 3 substrates at 850° C. A cubic c-TiO 1±δ buffer layer is formed for low O/Ti ratios, while a corundum cr-Ti 2 O 3 layer is formed under higher-oxidizing conditions. Metallicity is observed for c-TiO 1-δ buffer layers. The superconducting γ -Ti 3 O 5 Magnéli phase is found to nucleate on a c-TiO 1-δ buffer for intermediate POx conditions, and an insulator-superconducting transition is observed at 4.5 K (T$^{onset}_{C}$ = 6K) for 85 nm thick films. Strain relaxation of γ -Ti 3 O 5 occurs with increasing film thickness and correlates with a thickness-dependent increase in T C observed for Ti x O y thin films.

71 CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSIC↗

DOE OSTI2022

Thickness and temperature dependence of the atomic-scale structure of SrRuO 3 thin films

The temperature-dependent layer-resolved structure of 3 to 44 unit cell thick SrRuO 3 (SRO) films grown on Nb-doped SrTiO 3 substrates is investigated using a combination of high-resolution synchrotron x-ray diffraction and high-resolution electron microscopy to understand the role that structural distortions play in suppressing ferromagnetism in ultra-thin SRO films. The oxygen octahedral tilts and rotations and Sr displacements characteristic of the bulk orthorhombic phase are found to be strongly dependent on temperature, the film thickness, and the distance away from the film–substrate interface. For thicknesses, t, above the critical thickness for ferromagnetism (t > 3 uc), the orthorhombic distortions decrease with increasing temperature above T C . Below T C , the structure of the films remains constant due to the magneto-structural coupling observed in bulk SRO. The orthorhombic distortions are found to be suppressed in the 2–3 interfacial layers due to structural coupling with the SrTiO 3 substrate and correlate with the critical thickness for ferromagnetism in uncapped SRO films.

36 MATERIALS SCIENCE↗