DOE OSTI2024

Surface and Bulk Stabilization of Silicon Anodes with Mixed-Multivalent Additives: Ca(TFSI) 2 and Mg(TFSI) 2

Here, silicon is drawing attention as the upcoming anode material for the next generation of lithium-ion batteries due to its higher capacity compared to commercial graphite. However, silicon anions formed during lithiation are highly reactive with binder and electrolyte components creating an unstable SEI layer and limiting the calendar life of silicon anodes. The reactivity of lithium silicide and the formation of an unstable SEI layer is mitigated by utilizing the use of a mixture of Ca and Mg multivalent cations as an electrolyte additive for Si anodes to improve their calendar life. The effect of mixed salts on the bulk and surface of silicon anodes was studied by multiple structural characterization techniques. Ca and Mg ions in the electrolyte formed relatively thermodynamically stable quaternary Li-Ca-Mg-Si Zintl phases in an in-situ fashion and more stable and denser SEI layer on the Si particles. These in turn protect silicon particles against side reactions with electrolytes in a coin cell. The full cell with the mixed cation electrolyte demonstrates enhanced calendar life performance with lower measured current and current leakage than that of the baseline electrolyte due to reduced side reactions. Electron Microscopy, HRXRD, and solid-state NMR results showed that electrodes with mixed cations tended to have less cracking on the electrode surface compared to Si electrodes with Gen2 + FEC and the presence of mixed cations enhances cation migration and formation of quaternary Zintl phases stabilizing bulk and forming a more stable SEI.

25 ENERGY STORAGE↗

DOE OSTI2023

Composite media for non-oxidative ethane dehydrogenation, and related ethane activation systems and method of processing an ethane-containing stream

A composite media for non-oxidative C 2 H 6 dehydrogenation comprises an aluminosilicate zeolite matrix, and an EDH catalyst on one or more of an external surface of the aluminosilicate zeolite matrix and internal surfaces within pores of the aluminosilicate zeolite matrix. The EDH catalyst comprises one or more of Fe, Zn, Pt, Ga, alloys thereof, and oxides thereof. A C 2 H 6 activation system, and a method of processing a C 2 H 6 -containing stream are also described.

Wang, Lucun↗

DOE OSTI2023

Methods for producing hydrocarbon products and hydrogen gas through electrochemical activation of methane

A method of forming a hydrocarbon product and hydrogen gas comprises introducing CH 4 to a positive electrode of an electrochemical cell comprising the positive electrode, a negative electrode, and a proton-conducting membrane between the positive electrode and the negative electrode. The proton-conducting membrane comprises an electrolyte material having an ionic conductivity greater than or equal to about 10 −2 S/cm at one or more temperatures within a range of from about 150° C. to about 600° C. A potential difference is applied between the positive electrode and the negative electrode of the electrochemical cell to produce the hydrocarbon product and the hydrogen gas. A CH 4 activation system and an electrochemical cell are also described.

Ding, Dong↗

DOE OSTI2023

Methods for producing hydrocarbon products and protonation products through electrochemical activation of ethane

A method of forming a hydrocarbon product and a protonation product comprises introducing C2H6 to a positive electrode of an electrochemical cell comprising the positive electrode, a negative electrode, and a proton-conducting membrane between the positive electrode and the negative electrode. The proton-conducting membrane comprises an electrolyte material having an ionic conductivity greater than or equal to about 10−2 S/cm at one or more temperatures within a range of from about 150° C. to about 650° C. A potential difference is applied between the positive electrode and the negative electrode of the electrochemical cell to produce the hydrocarbon product and the protonation product. A C2H6 activation system and an electrochemical cell are also described.

He, Ting↗

DOE OSTI2023

Electrochemical Formation of Li-M-(M')-Si Phases Using Multivalent Electrolyte Salt Additives

Lithium-rich silicides (Li 15 Si 4 ), formed during the electrochemical lithiation of silicon, show high reactivity with electrolyte components that contribute to capacity decay, formal lithium loss, and low coulombic efficiency. Recently, the reactivity of lithium silicides was found to be suppressed by substituting a multivalent cation (i.e. Mg, Ca) for lithium that results in the room temperature formation of a ternary Li-M-Si phase. In this study, we explored a range of multivalent electrolyte salt additives (M = Ni, Cu, La, Ce, Sr, Ba, and Ca-Mg mixed salt) in a lithium-ion cell configuration and identified a room temperature electrochemical route to the formation of new ternary and quaternary lithium silicides. Using this method, both nickel and copper salts were found to plate onto the silicon electrode surface upon lithiation. Further, based on refined synchrotron XRD data, multivalent cations with an ionic radius similar to Na (~1.03 Å) or smaller can be inserted electrochemically into a formally cation-deficient Li 15 Si 4 host lattice to form new ternary (or quartenary) phases. The electrochemical synthesis of a new quaternary Li-M-M’-Si phase represents a facile route to preparing and scaling materials isostructural to the Heusler phase and electron-precise Li 14 MgSi 4 phase that results in enhanced cycling and calendar life performance.

25 ENERGY STORAGE↗

DOE OSTI2021

Silicon Anodes with Improved Calendar Life Enabled By Multivalent Additives

Silicon is widely recognized as the most promising upgrade for graphite anodes due to its much higher capacity, natural abundance, and ability to be directly applied in the slurry-based, roll-to-roll production lines. However, in addition to the fast capacity decay, silicon anodes also suffer from inferior calendar life in practical applications due to the unstable solid-electrode interface (SEI). Until now, strategies to effectively improve the calendar life by tailored SEIs remain largely unclear, especially in high-Si content, zero-graphite anodes. Here, silicon anodes with superior calendar life are developed by adding small concentrations of multivalent salts into the baseline electrolyte. The Ca additive reacts with the F ions in the electrolyte, forming a layer of nanocrystalline CaF 2 that is closely coated around the silicon particles. The CaF 2 -enabled new SEI is strong and dense, which effectively protects the silicon core from side reactions, leading to lower capacity decay after calendar aging at high voltage. More importantly, the Ca additive is effective universally for all available commercial silicon or SiO sources. This study provides a feasible and low-cost solution for developing silicon anodes with long calendar life, paving the way towards commercially viable silicon anodes.

25 ENERGY STORAGE↗

DOE OSTI2021

Probing the Reactivity of the Active Material of a Li-Ion Silicon Anode with Common Battery Solvents

Calculations and modeling have shown that replacing the traditional graphite anode with silicon can greatly improve the energy density of lithium-ion batteries. However, the large volume change of silicon particles and high reactivity of lithiated silicon when in contact with the electrolyte lead to rapid capacity fading during charging/discharging processes. In this report, we use specific lithium silicides (LS) as model compounds to systematically study the reaction between lithiated Si and different electrolyte solvents, which provides a powerful platform to deconvolute and evaluate the degradation of various organic solvents in contact with the active lithiated Si-electrode surface after lithiation. Nuclear Magnetic Resonance (NMR) characterization results show that a cyclic carbonate such as ethylene carbonate is chemically less stable than a linear carbonate such as ethylmethyl carbonate, fluoroethylene carbonate, and triglyme as they are found to be more stable when mixed with LS model compounds. Furthermore, guided by the experimental results, two ethylene carbonate (EC)-free electrolytes are studied, and the electrochemical results show improvements with graphite-free Si electrodes relative to the traditional ethylene-carbonate-based electrolytes. More importantly, the study contributes to our understanding of the significant fundamental chemical and electrochemical stability differences between silicon and traditional graphite lithium-ion battery (LIB) anodes and suggests a focused development of electrolytes with specific chemical stability vs lithiated silicon which can passivate the surface more effectively.

25 ENERGY STORAGE↗

DOE OSTI2021

Robust Solid/Electrolyte Interphase (SEI) formation on Si Anodes Using Glyme-based Electrolytes

Silicon (Si) is the most naturally abundant element possessing 10-fold theoretical capacity than graphitebased anodes. The practicality of implementing Si anodes is, however limited by the unstable solidelectrolyte interphase (SEI) and anode fracturing during continuous lithiation/delithiation. We demonstrate that glyme-based electrolytes (GlyEls) assure a conformal SEI on Si and keep the Si ‘fracture-free’. Benchmarking against the optimal, commonly-used carbonate electrolyte with the fluoroethylene carbonate (FEC) additive, Si anode cycled in a GlyEl exhibits reduced early parasitic current (by 62.5%) and interfacial resistance (by 72.8%), while the cell capacity retention is promoted by >7% over a course of 110 cycles. The mechanistic investigation by X-ray photoelectron spectroscopy (XPS) and energy-dispersive X-ray spectroscopy (EDX) indicates GlyEl enriches Si SEI with elastic polyether but diminishes its carbonate species. Glyme-based electrolytes prove viable in stabilizing the SEI on silicon for future high energy density lithium-ion batteries.

Yang, Guang↗