Weakly solvating ester electrolyte for high voltage sodium-ion batteries
Ethyl acetate (EA) was identified as a promising electrolyte solvent for sodium-ion batteries (SIBs), exhibiting low viscosity, cost-effectiveness, and low toxicity. Despite a significant portion of aggregation being linked to the weak solvation of Na + /EA as revealed by molecular dynamics (MD) simulations, pulsed-field gradient nuclear magnetic resonance (pfg-NMR) analysis identified a noteworthy Na+ diffusion coefficient of 3.95×10 -10 m 2 s -1 at 25°C in the presence of 1 m NaPF 6 salt. Employing fluoroethylene carbonate (FEC) as a film-forming additive to create electrode-electrolyte interphase, this electrolyte surprisingly made ~210 mAh Na 0.97 Ca 0.03 [Mn 0.39 Fe 0.31 Ni 0.22 Zn 0.08 ]O 2 (NCMFNZO)/hard carbon (HC) pouch cells achieve a lengthy cycling lifetime of 250 cycles with ~80 % capacity retention, cycled up to 4.0 V at 40°C. X-ray photoelectron spectroscopy (XPS) revealed increasing interphasial organic species over cycling, augmenting charge transfer resistance on both cathode and anode, particularly during fast charging or low temperatures (<10°C), promoting Na plating. Finally, gas chromatography-mass spectrometry combined with density functional theory identified CO 2 as the major gas generated from charged cathode/electrolyte interactions, exhibiting temperature/voltage dependence.