Engineering topics

Zheng, Shiyao

Publications and source records attributed to Zheng, Shiyao.

4 records

DOE OSTI2023

Realizing high-capacity all-solid-state lithium-sulfur batteries using a low-density inorganic solid-state electrolyte

Abstract Lithium-sulfur all-solid-state batteries using inorganic solid-state electrolytes are considered promising electrochemical energy storage technologies. However, developing positive electrodes with high sulfur content, adequate sulfur utilization, and high mass loading is challenging. Here, to address these concerns, we propose using a liquid-phase-synthesized Li 3 PS 4 -2LiBH 4 glass-ceramic solid electrolyte with a low density (1.491 g cm −3 ), small primary particle size (~500 nm) and bulk ionic conductivity of 6.0 mS cm −1 at 25 °C for fabricating lithium-sulfur all-solid-state batteries. When tested in a Swagelok cell configuration with a Li-In negative electrode and a 60 wt% S positive electrode applying an average stack pressure of ~55 MPa, the all-solid-state battery delivered a high discharge capacity of about 1144.6 mAh g −1 at 167.5 mA g −1 and 60 °C. We further demonstrate that the use of the low-density solid electrolyte increases the electrolyte volume ratio in the cathode, reduces inactive bulky sulfur, and improves the content uniformity of the sulfur-based positive electrode, thus providing sufficient ion conduction pathways for battery performance improvement.

25 ENERGY STORAGE↗

DOE OSTI2020

Counter-Intuitive Structural Instability Aroused by Transition Metal Migration in Polyanionic Sodium Ion Host

The structure of polyanionic materials is conventionally known to be free of transition metal migration and structurally stable when storing/releasing sodium ions. Herein, the observation of enhanced cycling stability of a typical polyanionic cathode, Na 3 VCr(PO 4 ) 3 (NVCP) at lower temperature (-15 degrees C vs 30 degrees C), triggers the exploration of its structural origins with a surprising finding that the migratable nature of vanadium in NVCP leads to detrimental structural degradation of the polyanionic host upon cycling. The correlation between long range and short range structural change associated with this atomic migration is established via a strong combination of various in situ/ex situ characterization tools, revealing the essential V-to-Na1 site migration. Such transition metal migration is effectively suppressed when V atoms are pinned to their original position in the lattice by lowering the temperature. More importantly and practically, a room temperature-based deep sodiation strategy is further developed to recover the structure. Overall, this work challenges the long-standing assumption of the stability of the polyanionic framework structure and calls for urgent attention to the structural understanding of the NVCP system as well as strategy development for property enhancement.

25 ENERGY STORAGE↗

DOE OSTI2020

Suppression of voltage-decay in Li 2 MnO 3 cathode via reconstruction of layered-spinel coexisting phases

Voltage decay, i.e., the voltage decrease during electrochemical cycling, has been a decade-long challenge for lithium-ion batteries. This issue not only leads to a substantial loss of energy density, but also raises challenges for the battery management system, hindering the commercial application of high capacity lithium-rich oxide. Here, we show that through a combination of electrochemical conditioning and thermal treatment, Li 2 MnO 3 , the parent compound of lithium-rich oxide, which typically displays severe voltage and capacity decay, could be converted into a new phase that essentially suppresses the voltage decay with improved capacity retention and rate performance. Furthermore, by combining atomic-sensitive nuclear magnetic resonance, differential electrochemical mass spectrometry and synchrotron-based resonant inelastic X-ray scattering, we disclose that treatment triggers the formation of three-coexisting phases, i.e., the lithium-rich layered, spinel and defect spinel phases, which enables improved reversibility of the oxygen redox activity and enhanced manganese redox reactions in the initial cycle. Our findings suggest the key role of the local structure in the voltage decay problem and provide insights for material optimizations towards lithium- and manganese-rich cathodes without the voltage decay.

25 ENERGY STORAGE↗

DOE OSTI2020

Fluorination effect for stabilizing cationic and anionic redox activities in cation-disordered cathode materials

We see that cation-disordered Li-excess cathodes with oxygen redox reactions are promising candidates for high-energy-density Li ion batteries. Nevertheless, the oxygen redox process that is required for the high capacity often comes with the oxygen loss, which leads to severe capacity degradation and voltage decay. In this work, we have successfully synthesized a series of Li-excess cation-disordered cathodes (Li 1.2 Mn 0.4+x Ti 0.4-x O 2-x Fx) (0 ≤ x ≤ 0.2) with different fluorine (F) contents. The electrochemical performance results show that the Li 1.2 Mn 0.55 Ti 0.25 O 1.85 F 0.15 (LMTOF0.15) exhibits the highest reversible capacity (275 mAh g -1 , under 30 mA g -1 ), cyclability, and voltage retentions. The mapping of resonant inelastic X-ray scattering (mRIXS) and differential electrochemical mass spectroscopy (DEMS) results reveal that the fluorination enhances the reversible lattice oxygen redox reaction while suppressing irreversible gas release and surface reactions. The X-ray Absorption Spectroscopy (XAS) during the initial two cycles shows that F-substitution alleviates the reduction of the Mn valence state during the whole (dis)charge processes in the bulk and at the surface of the material, results in higher average discharge voltage. In addition, the introduction of F improves the structural stability and suppresses local lattice distortion of the material. Therefore, LMTOF 0.15 is able to cycle with smaller polarization, less interfacial side reaction and Mn dissolution, and therefore results in enhanced cyclability. This work provides a comprehensive understanding of the fluorination effect on the cationic and anionic redox activities in cation-disordered Li-excess cathodes.

25 ENERGY STORAGE↗