DOE OSTI2024

Understanding the Effects of Bi Modification on the Properties of Ni-Rich Cathodes

With the skyrocketing market demands for energy storage, lithium ions batteries (LIB) with higher energy density are urgently needed. Cathodes play a critical role in determining the energy density of LIB, and the most popular one is Ni-rich cathode due to its high capacity. However, due to the fast structural degradation, Ni-rich cathode materials should be further modified to achieve higher stability. Herein, we introduce bismuth ions in LiNi 0.83 Co 0.11 Mn 0.06 O 2 cathodes by adding Bi 2 O 3 during sintering to optimize the specific capacity and cycle stability. By adding 0.1% mol Bi, the Li + diffusion and structural stability are effectively optimized, leading to improved electrochemical performances. Further, the modified sample delivers much higher specific capacity (222.9 mAhg -1 , 0.05 C) than unmodified sample (204 mAhg -1 , 0.05 C). Meanwhile, the specific capacity of optimized sample after 100 cycles at 0.33 C is 27.75 mAhg -1 higher than that of unmodified sample. Therefore, this work demonstrates that Bi modification can be regarded as a possible solution to optimizing the electrochemical performance of Ni-rich cathodes.

25 ENERGY STORAGE↗

DOE OSTI2023

Unraveling the nature of sulfide ions in hydrometallurgical recycling of NCM622 cathode material

The use of lithium-ion batteries (LIBs) has increased dramatically since its initial inception in the late 20th century. Such a surge in the LIB market and industry has resulted in a huge demand for mineral resources. Besides, the large scale of production will lead to massive amounts of waste batteries in the end. As such, recycling is seen as an end-of-pipe process to resolve sustainability and environmental concerns. The hydrometallurgical recycling is considered to be the most prominent method to recover cathode materials from spent LIBs owing to its high leaching efficiency and low energy costs. A series of procedures including pretreatment of the spent LIBs, acid leaching of the black mass, chemical co-precipitation of the hydroxide precursor, and sintering of the cathode active material need to be operated precisely. In this aspect, the impurities introduced during the process could pose a serious threat to the reaction stability as well as recycling consistency. Here, the impact of sulfide ions on recovered LiNi 0.6 Co 0.2 Mn 0.2 O 2 (NCM622) cathode material with the method of hydrometallurgy is first investigated in detail. This study shows that hydrometallurgical process is not obviously influenced by sulfide impurity. No signs of secondary phase or impurity inclusion are spotted in synthesized cathodes. Under 5 at % sulfide concentration conditions, the obtained NCM622 cathode exhibits a capacity of 159.4 mAh/g after 100 cycles at 1/3C, which is at the same level as virgin benchmark. The difference in rate performance between cathodes with and without additional sulfide is less than 2 % or even smaller. In short, the results indicate a neutral status of sulfide ions in hydrometallurgical recycling.

25 ENERGY STORAGE↗

DOE OSTI2022

The Effects of Phosphate Impurity on Recovered LiNi 0.6 Co 0.2 Mn 0.2 O 2 Cathode Material via a Hydrometallurgy Method

From portable electronics to electric vehicles, lithium-ion batteries have been deeply integrated into our daily life and industrial fields for a few decades. The booming field of battery manufacturing could lead to shortages in resources and massive accumulation of battery waste, hindering sustainable development. Therefore, hydrometallurgy-based approaches have been widely used in industrial recycling to recover cathode materials due to their high efficiency and throughput. Further, impurities have always been a great challenge for hydrometallurgical recycling, introducing challenges to maintain the consistency of product quality because of potential unintended effects caused by impurities. Herein, after comprehensive investigation, we first report the impacts of phosphate impurity on a recycled LiNi 0.6 Co 0.2 Mn 0.2 O 2 ("NCM622") cathode via a hydrometallurgy method. We demonstrate that a passivation layer of Li 3 PO 4 is formed at grain boundaries during sintering, which significantly raises the activation barrier and hinders lithium diffusion. In addition, the distinct degradation of cathode electrochemical properties is observed from poor particle morphology and high cation mixing as a result of phosphate impurity. Cathode powders with 1 at. % phosphate impurity retain a capacity of 146 mAh/g after 100 cycles at 0.33C, 6% less than that of a virgin cathode. Furthermore, cathodes with higher phosphate concentrations perform even worse in electrochemical tests. Therefore, phosphate impurities are detrimental to the hydrometallurgical recycling of NCM cathode materials and need to be excluded from the recycling process.

25 ENERGY STORAGE↗

DOE OSTI2021

Positive Role of Fluorine Impurity in Recovered LiNi 0.6 Co 0.2 Mn 0.2 O 2 Cathode Materials

Lithium-ion battery (LIB) recycling is considered as an important component to enable industry sustainability. A massive number of LIBs in portable electronics, electric vehicles, and grid storage will eventually end up as wastes, leading to serious economic and environmental problems. Hence, tremendous efforts have been made to improve the hydrometallurgical recycling process because it is the most promising option for handling end-of-life LIBs owing to its wide applicability, low cost, and high productivity. Despite these advantages, some extra elements (Al, Fe, C, F, and so forth) remain as impurities in the removal process and are retained in the solution, which is a great challenge to obtain high-quality cathode materials. In this work, the impacts caused by fluorine impurity on the LiNi 0.6 Co 0.2 Mn 0.2 O 2 (NCM622) cathode are intensively investigated via hydrometallurgical coprecipitation for the first time. Our results show that up to 1 at. % fluorine impurity brings a positive influence on the recovered material due to a higher Ni 2+ ratio on the surface of cathode particles. In addition, the presence of fluoride ions during coprecipitation could lead to the formation of holes in cathode particles, which improves the rate capability and cyclability dramatically. Compared to the virgin material, the capacity of the NCM622 material with 0.2 at. % fluorine impurity is boosted by ~8% (167.7 mA h/g) with a remarkable capacity retention of 98.0% after 100 cycles at 0.33 C. Besides, the cathode with 0.2 at. % fluorine impurity shows a far better rate performance, especially at high rates (~7% increased at 5 C) than that of virgin. Furthermore, these results convince that a low concentration of fluorine impurity is desirable in the hydrometallurgical recycling process. More importantly, this study offers implications in the design of high-performance NCM622 cathode materials via coprecipitation production with ion doping in the near future.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

Valence Effects of Fe Impurity for Recovered LiNi 0.6 Co 0.2 Mn 0.2 O 2 Cathode Materials

Iron impurities are generally included in the obtained leaching liquor solution during the hydrometallurgical recycling method of spent lithium-ion batteries (LIBs) due to the usage of iron in battery casings and machinery parts of recycling equipment, which would definitely affect the physical and electrochemical features of the recovered active materials. In this paper, the effects of iron impurity with different valence states (Fe 2+ and Fe 3+ ) and gradient concentrations (0.2, 1.0, and 5.0 at. %) for the obtained LiNi 0.6 Co 0.2 Mn 0.2 O 2 (NCM622) cathodes are fully studied. It is found that Fe3+ impurity could easily lower the tap density and average size of NCM622 particles and even introduce some impurity phases in the NCM622 structure at high concentration (5.0 at. %), leading to much lower specific capacity, worse rate capability, and cycling performance of the Fe 3+ -based NCM622 cathode. On contrast, with certain concentrations of Fe 2+ impurity (0.2 and 1.0 at. %), the NCM622 cathode material exhibits comparable and much better electrochemical properties compared with the virgin NCM622 materials. Based on these results, the valence of Fe impurity should be considered and controlled as well as its concentration during the recycling process design for spent LIBs.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

Unveiling the Influence of Carbon Impurity on Recovered NCM622 Cathode Material

With the proliferation of market demand for lithium-ion batteries (LIBs) over the past decades, battery recycling has aroused extensive attention due to the environmental, supply, and economic issues caused by waste batteries. Here, the hydrometallurgical recycling method has been widely adopted to recover cathode materials as a result of its wide applicability and high productivity. However, it is hard to completely eliminate impurities such as copper, aluminum, and carbon, which could bring significant impacts on recovered materials. Here, the influence of the carbon impurity on recovered LiNi 0.6 Co 0.2 Mn 0.2 O 2 (NCM622) cathode material is systematically investigated. It shows that the carbon impurity promotes nucleation during coprecipitation and forms holes in the cathode secondary particles after sintering which could enhance cyclability of the NCM622 cathode. The cathode with 0.2 atom % of carbon impurity displays the highest capacity of 159.9 mAh/g with a striking capacity retention rate of 97.9% after 100 cycles at 0.33C, but performs worse at high rates. Nonetheless, excess carbon (5 atom %) results in severe cation disorder and lattice distortion which significantly deteriorates the electrochemical properties of the NCM622 cathode. Therefore, it is important to strictly control carbon impurity during the recycling process for spent LIBs.

25 ENERGY STORAGE↗

DOE OSTI2020

Understanding fundamental effects of Cu impurity in different forms for recovered LiNi 0.6 Co 0.2 Mn 0.2 O 2 cathode materials

When identifying and developing lithium ion battery recycling technologies, understanding the role of impurities is always a concern as they may have an impact on electrochemical performance, material stability, or lifetime for recovered active materials. In this work we show that Cu impurity in different forms could play very different roles on the recovered LiNi 0.6 Co 0.2 Mn 0.2 O 2 (NCM622). Cu metal impurity could easily short the cell, while Cu ion impurity could play a positive role due to partially substitution of the Ni 2+ sites to lower the cation mixing degree. In specific, NCM622 material with certain amount (0.34 at%) of Cu ion impurity delivers high initial specific charge/discharge capacity of 211.8 and 186.0 mAh g -1 at 0.05 C, which are 12.2 and 14.1 mAh g -1 higher than those of virgin NCM622 cathode. Moreover, a superior retention capacity of 171.3 mAh g -1 after 90 cycles at 0.33 C, and striking rate capability are achieved in this NCM622 cathode sample. These results clearly indicate that Cu metal impurity should be avoided and the ionic Cu impurity should be controlled with optimal concentration during recycling process for spent LIBs.

25 ENERGY STORAGE↗

DOE OSTI2020

Systematic Study of Al Impurity for NCM622 Cathode Materials

Many recycling processes have been developed for spent Li-ion batteries (LIBs), such as pyrometallurgy, hydrometallurgy, and direct recycling. For all the recycling methods, however, impurities are always introduced from the current collectors or casing materials, especially aluminum (Al), which might lead to negative effects on recovered electrode materials. Therefore, it is significant to determine the impacts of Al impurity on recovered materials. Here, the influence of the Al impurity for the synthesized LiNi 0.6 Co 0.2 Mn 0.2 O 2 (NCM622) precursor and cathode is systematically studied. The cell with 0.2 at % Al impurity displays the highest reversible capacities (145.2, 130.5, and 100.3 mAh g -1 from 2, 3, and 5 C, respectively) and striking cycling capability at 2 C after 100 cycles with the highest retention capacity of 138.5 mAh g -1 . Meanwhile, the excess Al ions (5 at %) lead to the Li/Mn superlattice structure and deteriorate electrochemical performance of the synthesized NCM622 cathode.

25 ENERGY STORAGE↗