Engineering topics
Zheng, Yiwei
Publications and source records attributed to Zheng, Yiwei.
KOH vs Deionized Water Operation in Anion Exchange Membrane Electrolyzers
Anion exchange membrane water electrolyzers (AEMELs) have recently received significant attention due to their potential advantages over proton exchange membrane electrolyzers (PEMELs). However, some AEMELs feed an aqueous salt solution to the cell where PEMELs typically feed deionized (DI) water. DI water is preferred to keep the system and maintenance costs low. Because of this, many AEMEL researchers report performance both in the salt solution (typically KOH) and DI water. However, the methodology for switching between KOH and DI water is often poorly defined, and it is unclear what impact the residual salt has on cell performance after switching from salt to DI water. Having a fully deionized environment is important because the presence of salts in the water feed increase the effective electrochemical surface area of the catalyst in the three-dimensional electrode and residual salt remaining after switching to DI water feed can have a misleading transient effect on cell performance. This paper focuses on understanding the transition from KOH to DI water testing in AEMELs. It is shown that when switching from salt to DI water feed, a large volume of DI water must be fed over several hours to achieve true DI-water performance. It is also shown that starting AEMELs from the beginning with DI water feed (without any KOH ever being fed to the cell) results in better cell durability. Lastly, a cell is demonstrated having operated exclusively on DI water at 1.0 A cm −2 for 500 h at an operating voltage of ca. 2 V and a low degradation rate.
Using operando techniques to understand and design high performance and stable alkaline membrane fuel cells
There is a need to understand the water dynamics of alkaline membrane fuel cells under various operating conditions to create electrodes that enable high performance and stable, long-term operation. Here we show, via operando neutron imaging and operando micro X-ray computed tomography, visualizations of the spatial and temporal distribution of liquid water in operating cells. We provide direct evidence for liquid water accumulation at the anode, which causes severe ionomer swelling and performance loss, as well as cell dryout from undesirably low water content in the cathode. We observe that the operating conditions leading to the highest power density during polarization are not generally the conditions that allow for long-term stable operation. This observation leads to new catalyst layer designs and gas diffusion layers. This study reports alkaline membrane fuel cells that can be operated continuously for over 1000 h at 600 mA cm -2 with voltage decay rate of only 32-μV h -1 – the best-reported durability to date.
Effect of reacting gas flowrates and hydration on the carbonation of anion exchange membrane fuel cells in the presence of CO 2
Anion exchange membrane fuel cells (AEMFCs) have been widely touted as a low-cost alternative to existing proton exchange membrane fuel cells. However, one of the limitations of this technology has been the severe performance penalty related to the introduction of CO 2 to the cell – typically in the air cathode feed. Introduction of CO 2 into AEMFCs results in cell carbonation, which imparts thermodynamic, kinetic and Ohmic overpotentials that can add up to hundreds of millivolts. Therefore, it is important to find strategies and operational protocols for AEMFCs that minimize these overpotentials. In this paper, we reserach the impacts of the anode and cathode flowrate, as well as the cell hydration level, on the extent of cell carbonation and cell polarization. Key findings include: (1) decreasing the cathode flowrate generally decreases the total CO 2 -related voltage loss while changing the anode flowrate has a minimal effect; (2) increasing cell hydration helps to mitigate the performance loss in the presence of CO 2 ; and (3) operational combinations are found that significantly reduce the CO 2 penalty compared to the present literature.