Strategies to Counter Cr poisoning on air electrodes of solid oxide cells
Not Available
Kalu, Awa (ORCID:0009000786347732)↗
Engineering topics
Zhou, Lingfeng
Publications and source records attributed to Zhou, Lingfeng.
Unraveling the conundrum of electronic leakage in protonic ceramic cells: Operation-specific insights and rational design strategies
Electronic conduction through proton-conducting electrolytes significantly impairs the efficiency of protonic ceramic cells (PCCs). Here, in this study, we explore the electron and ion mixed transport properties of four common protonic ceramics, BaZr 0.8 Y 0.2 O 3-δ (BZY82), BaZr 0.7 Ce 0.2 Y 0.1 O 3-δ (BZCY721), BaZr 04 Ce 0.4 Y 0.1 Yb 0.1 O 3-δ (BZCYYb4411), and BaZr 0.1 Ce 0.7 Y 0.1 Yb 0.1 O 3-δ (BZCYYb1711). It marks the first instance of investigating these properties under operation-specific scenarios: fuel side of electrolysis cell, air side of electrolysis cell, fuel side of fuel cell, and air side of the fuel cell. BZCYYb1711 exhibits the highest ionic conductivity, but two to three times higher electronic leakage when exposed to oxygen-containing environments than the others. BZY82 exhibits approximately two times higher electronic leakage in a hydrogen-containing environment. BZCY721 demonstrates excellent ion transport numbers (~0.95) across these four operating conditions. BZCYYb4411 behaves quite similarly to BZCY721. The most challenging operating environment for all candidates is the air side of fuel cell mode. This mode leads to a high initial electronic leakage, followed by a significant increase with polarization. The probable cause for this behavior is a H 2 -free, polarization-induced reduction that leads to the formation of V$^•_O$. The electron small polaron associated with V$^•_O$ is released by the electrical field due to the Poole-Frenkel effect. ZnO and NiO sintering aids are found to be detrimental to the ionic conductivity of the electrolytes. In particular, NiO substantially lowers the ion transport number. The correlation of the operation-specific electronic leakage to full cells is discussed. It is suggested that a rational PCC design should synergistically couple BZCYYb1711 at fuel side with BZCY4411 at air side to deliver a well-balanced performance and faradaic efficiency simultaneously, and the high temperature sintering process with a NiO fuel electrode should be shortened or replaced by ultra-fast sintering techniques or using a fuel electrode scaffold-infiltration fabrication strategy.
42 ENGINEERING↗
Chromium evaporation and oxidation characteristics of alumina-forming austenitic stainless steels for balance of plant applications in solid oxide fuel cells
The chromium (Cr) evaporation behavior of several different types of iron (Fe)-based AFA alloys and benchmark Cr 2 O 3 -forming Fe-based 310 and Ni-based 625 alloys was investigated for 500 h exposures at 800 °C to 900 °C in air with 10% H 2 O. The Cr evaporation rates from alumina-forming austenitic (AFA) alloys were ~5 to 35 times lower than that of the Cr 2 O 3 -forming alloys depending on alloy and temperature. The Cr evaporation behavior was correlated with extensive characterization of the chemistry and microstructure of the oxide scales, which also revealed a degree of quartz tube Si contamination during the test. As a result, long-term oxidation kinetics were also assessed at 800 to 1000 °C for up to 10,000 h in air with 10% H 2 O to provide further guidance for SOFC BOP component alloy selection.
08 HYDROGEN↗
Redox-stable symmetrical solid oxide fuel cells with exceptionally high performance enabled by electrode/electrolyte diffuse interface
Here, in this study, we report a high performance and redox-stable symmetrical solid oxide fuel cell (SOFC) based on (Ba 0.5 Sr 0.5 ) (Mo 0.1 Fe 0.9 )O 3-δ (BSMF) electrode and La 0.8 Sr 0.2 Ga 0.8 Mg 0.2 O 3-δ (LSGM) electrolyte. BSMF is able to operate both as anode and cathode. Excellent electrocatalytic activity has been achieved on BSMF towards hydrogen oxidation and oxygen reduction. Due to its closely matched lattice parameter to LSGM electrolyte, a unique diffuse interface is formed between BSMF and LSGM. Compared to a clean interface, e.g. BSMF/gadolinium doped ceria interface, this diffuse interface promotes the performance of BSMF electrode 1–1.8 times in 600–800 °C. Polarization resistance of the BSMF/LSGM specimen is as low as 0.047 and 0.007 Ωcm 2 in humidified H 2 and in air at 800 °C, respectively. On the BSMF/LSGM/BSMF symmetrical cell, a maximum power density of 2.28 W/cm 2 is achieved at 800 °C, the highest among with redox-stable ceramic electrodes to the best of our knowledge. Redox stability of this cell is confirmed. The role of anode and cathode is reversed back and forth in different operation modes. No apparent degradation is observed through 4 cycles within a 110 h operation period. These findings demonstrate that (Ba 0.5 Sr 0.5 ) (M o0.1 Fe 0.9 )O 3-δ coupled with LSGM electrolyte is an excellent choice to build a high performance, redox-stable SOFC.
25 ENERGY STORAGE↗