Engineering topics
Zhou, Weiyue
Publications and source records attributed to Zhou, Weiyue.
Author Correction: Proton irradiation-decelerated intergranular corrosion of Ni-Cr alloys in molten salt
In the original version of this article, numbers for the beam current densities were incorrectly given as 1.5, 2.0, and 2.5 mA cm -2 in various locations, instead of the correct values 0.3, 0.4, and 0.5 mA cm -2 . This was owing to a measurement error coming from the indirect correspondence between the Faraday cup and the beam profile monitor (BPM) on the accelerator as the proton beam traveling along the beamline resulted in mismatching between calculated values and real beam currents, which were obtained by ex-situ calibration. The following changes have been made in the correct version. The eighth sentence of the Results, and the figure legend of Fig. 2j state '0.3, 0.4, 0.5 mA cm -2 ' in place of '1.5, 2.0, 2.5 mA cm -2 '. The figure legend of Fig. 1j–l states '0.5, 0.4, 0.3 mA cm -2 ' in place of '2.5, 2.0, 1.5 mA cm -2 '. Figure 1e states '0.5 mA cm -2 ' in place of '2.5 mA cm -2 ', Fig. 1h states '0.4 mA cm -2 ' in place of '2.0 mA cm -2 ', and Fig. 1k states ‘0.3 mA cm -2 ' in place of ‘1.5 mA cm -2 '. Figure 2c states '0.5 mA cm -2 ' in place of '2.5 mA cm -2 ', Fig. 2d states '0.4 mA cm -2 ' in place of '2.0 mA cm -2 ', and Fig. 2e states '0.3 mA cm -2 ' in place of '1.5 mA cm -2 '. Figure 2j and k states ‘0.3 mA cm -2 ', '0.4 mA cm -2 ', '0.5 mA cm -2 ' in place of '1.5 mA cm -2 ', '2.0 mA cm -2 ', and '2.5 mA cm -2 ', respectively. The figure legend of Fig. 3b states '0.4 mA cm -2 ' in place of '2.0 mA cm -2 '. The figure legend of Supplementary Fig. 1 states '0.5 mA cm -2 ' in place of '2.5 mA cm -2 '. This has been corrected in the PDF and HTML versions of the Article.
One dimensional wormhole corrosion in metals
Corrosion is a ubiquitous failure mode of materials. Often, the progression of localized corrosion is accompanied by the evolution of porosity in materials previously reported to be either three-dimensional or two-dimensional. However, using new tools and analysis techniques, we have realized that a more localized form of corrosion, which we call 1D wormhole corrosion, has previously been miscategorized in some situations. Using electron tomography, we show multiple examples of this 1D and percolating morphology. To understand the origin of this mechanism in a Ni-Cr alloy corroded by molten salt, we combined energy-filtered four-dimensional scanning transmission electron microscopy and ab initio density functional theory calculations to develop a vacancy mapping method with nanometer-resolution, identifying a remarkably high vacancy concentration in the diffusion-induced grain boundary migration zone, up to 100 times the equilibrium value at the melting point. Deciphering the origins of 1D corrosion is an important step towards designing structural materials with enhanced corrosion resistance.
Proton irradiation-decelerated intergranular corrosion of Ni-Cr alloys in molten salt
The effects of ionizing radiation on materials often reduce to "bad news". Radiation damage usually leads to detrimental effects such as embrittlement, accelerated creep, phase instability, and radiation-altered corrosion. Here we report that proton irradiation decelerates intergranular corrosion of Ni-Cr alloys in molten fluoride salt at 650 °C. We demonstrate this by showing that the depth of intergranular voids resulting from Cr leaching into the salt is reduced by proton irradiation alone. Interstitial defects generated from irradiation enhance diffusion, more rapidly replenishing corrosion-injected vacancies with alloy constituents, thus playing the crucial role in decelerating corrosion. Our results show that irradiation can have a positive impact on materials performance, challenging our view that radiation damage usually results in negative effects.